Corrosion resistance of the FeAlC permanent magnet alloy

1998

Abstract The correlation between corrosion behaviour rate of hard magnetic FeAlC alloys and their microstructure and phase composition is presented. Potentiokinetic polarization curves of the tested material in acid (pH = 1 and 2) and neutral (pH = 7) sulphate solutions have been measured. For open-circuit condition, kinetic curves of etching of the samples in 0.5 M H2SO4 have been determined. The resistance of the tested magnets against atmospheric corrosion has been evaluated using a salt-spray test. The atmospheric corrosion rate is 1.5–2 times slower than that found for Nd-Fe-B type magnets. The FeAlC alloys show good corrosion resistance in neutral environments and corrode at rates…