Evolution Characteristics of Delamination Damage in CFRP Composites Under Transverse Loading

2012

The initiation and subsequent progression of delamination in CFRP composite laminates is examined using finite element method. A 12-ply CFRP composite, with a total thickness of 2.4 mm and anti-symmetric ply sequence is simulated under three-point bend test setup. Each unidirectional composite lamina is treated as an equivalent elastic and orthotropic panel. Interface behavior is defined using cohesive damage model. Complementary three-point bend test on the specimen is performed at crosshead speed of 2 mm/min. The measured load–deflection response at mid-span location compares well with predicted values. Interface delamination accounts for up to 46.7% reduction in flexural stiffness from t…