The formation and behaviour of radiation-induced free radicals in statistical copolymers of ethoxyvinylthiomethane (1a) with N-vinylpyrrolidone (2) (1:2,5) and of ethylthiovinylthiomethane (1b) with 2 (1:3,5) has been studied using electron spin resonance spectroscopy. After a γ-irradiation of the copolymers at 77K Cα-radicals in the vinylpyrrolidone moieties could be detected. Investigations on the behaviour of these radicals with an annealing procedure revealed that only in the copolymer (3b) with the dithioacetal group a transfer reaction of hydrogen atoms to the Cα-radicals in the vinylpyrrolidone moieties occurs. This process may be regarded as a repair mechanism. Es wurde die Bildung und das Verhalten von freien Radikalen in statistischen Copolymerisaten aus Athoxyvinylthiomethan (1a) und N-Vinylpyrrolidon (2) (1:2,5) sowie aus Athylthiovinylthiomethan (1b) und 2 (1:3,5) mit Hilfe der ESR-Spektroskopie untersucht. Nach einer γ-Bestrahlung bei 77 K konnten in den Copolymerisaten Cα-Radikale in den Vinylpyrrolidon-Einheiten nachgewiesen werden. Untersuchungen uber das Temperaturverhalten dieser freien Radikale zeigten, das nur im Copolymerisat (3b) mit der Dithioacetal-Gruppe ein Transfer von Wasserstoffatomen (Kettenubertragung) zu den Cα-Radikalen in den Vinylpyrrolidon-Einheiten stattfindet. Dieser Vorgang kann als „Repair” - Mechanismus aufgefast werden.