Physico-chemical evolution of low-pH cements : influence of the temperature and the retention mechanisme of alkalins

subject

description

Because of their high alkalinity, Portland cement (OPC)-based materials may have deleterious effects in an underground waste repository. A solution would be to use low-alkalinity cements (also referred as low-pH cements) generating interstitial solutions with a reduced pH (11 instead of 13.5 for OPC), and thus showing an improved chemical compatibility with the repository environment. In this work, the investigated formulations were based on binary (OPC / silica fume) or ternary (OPC / silica fume / slag or fly ash) blends, with high substitution levels of CEM I (from 30% to 80%). This research project met two main objectives: (i) study the chemical evolution of low-pH cements at 50°C or 80°C, since such temperatures could be encoutered in certain zones of the waste repositories, and (ii) determine the mechanisms of alkali retention by hydrated low-pH cements. (i) Investigation of low-pH cement pastes with ongoing hydration over one year showed that increasing the temperature from 20°C to 80°C accelerated cement hydration and favoured the depletion of portlandite. A lengthening of the C-A-S-H silicate chains was also detected by 27Al and 29Si NMR analyses. Besides, ettringite precipitated at 20°C, but was destabilised at higher temperature. The released sulphates were partly adsorbed on the C-A-S-H and dissolved in the interstitial solution. The pH of this solution was reduced from 1.7 to 2.2 units depending on the formulations. The soluble fractions of alkalis did not significantly change with temperature. Among the five investigated blends, ternary binder T1 (37.5% CEM I, 32.5% silica fume, 30% fly ash) was the only one giving a pore solution pH lower than 11 at 20, 50 and 80°C (curing time of 6 months and 1 year). Its long-term evolution was simulated by model systems reproducing its chemical composition with reactive oxides. At equilibrium, the hydrate assemblage comprised C-A-S-H (Ca/Si and Al/Si ratios of 0.75 and 0.15 respectively), amorphous silica and aluminium hydroxide. It led to a pH of 10.3 at 20°C. (ii) C-A-S-H hydrates played a major role in the retention of alkalis. Sorption of potassium was higher than that of sodium and mainly resulted from electrostatic interactions with C-A-S-H. Monte Carlo modelling of these interactions showed that the difference of solvated radii between these ions could not explain by itself the sorption selectivity experimentally observed.