Vacuum-ultraviolet absorption of amorphous SiO2: intrinsic disorder and role of silanol groups
Eleonora VellaRoberto BoscainoGiovanna Navarrasubject
Settore FIS/01 - Fisica SperimentaleVacuum UV absorption amorphous silicon dioxide absorption edge silanol groupsdescription
We present a study on the vacuum-ultraviolet VUV absorption properties of amorphous SiO2 a-SiO2 with high concentrations of silanol groups Si-OH . We found that the absorption spectra are made up of a couple of exponential profiles. The first, in the range from 7.5 to 8.1 eV, was attributed to Si-OH group absorption, while the second, in the range from 8.1 to 8.25 eV, was ascribed to the intrinsic absorption. The VUV absorption cross section of Si-OH groups in a-SiO2 was determined as well. The intrinsic absorption was found to be affected by the Si-OH concentration: high silanol group contents allow lower values of the Urbach energy. This result is interpreted in terms of a reduction in the degree of disorder in wet materials.
| year | journal | country | edition | language |
|---|---|---|---|---|
| 2008-01-01 |