Polyethylene wastes (low-density polyethylene, high-density polyethylene and their binary blends) were subjected to high-energy radiation, using a 60Co gamma radiation source. The crosslinked materials thus obtained were processed to heatshrinkable films. Tensile strength could be sharply improved by increasing the dose up to 20 Mrad, simultaneously increasing the elongation at break of the most degraded PE waste. An increase of the degree of compatibility of LDPE and HDPE waste was also observed. All samples examined exhibit a “memory effect” after drawing at 130°C and cooling under tension followed by further heating under relaxed conditions. The value of shrinkage depended on the degree of degradation of the PE waste and on the irradiation dose. Polyethylen-Abfalle (LDPE, HDPE sowie Blends aus beiden) wurden energiereicher Gammastrahlung aus einer 60Co-Quelle ausgesetzt. Durch die so induzierte Vernetzung des Polyethylens konnte das Material zu Schrumpffolien verarbeitet werden. Die Zugfestigkeit der Proben konnte durch Erhohung der Strahlendosis bis auf 20 Mrad entscheidend verbessert werden, wobei gleichzeitig auch die Bruchdehnung des meist zersetzten PE-Abfalls erhoht wurde. Auserdem wurde die Kompatibilitat zwischen LDPE- und HDPE-Abfall verbessert. Alle untersuchten PE-Proben zeigten einen Memoryeffekt, nachdem das Material bei 130°C zu Folien gezogen, unter Spannung gekuhlt und anschliesend spannungslos erwarmt wurde. Das Ausmas der Schrumpfung war abhangig vom Abbaugrad des eingesetzten PE-Abfalls und von der Strahlendosis.