Electrokinetic Properties which Control the Coagulation of Silicate Cement Suspensions during Early Age Hydration
1998
The coagulation of cement particles during early age hydration has been previously identified as the first step of the setting and hardening of cement pastes. By hydrating Ca3SiO5and a silicate-rich clinker under controlled conditions, a correlation between the coagulation of the suspensions and the electrokinetic properties of particles is established. The zeta potential, and hence the surface charge, of particles in suspension depends on the calcium content of the medium. At low concentrations of Ca2+, the zeta potential of Ca3SiO5particles, calcium silicate hydrate (C–S–H), and clinker is negative (<−30 mV) and the suspensions are well dispersed. A strong coagulation occurs at intermedia…
The Micro-Shear bond strength of different cements to commercially pure titanium
2019
Background The most appropriate luting agent for attaching the prefabricated Ti-based insert of hybrid abutments to its ceramic component has not yet been determined. This study was done aimed at examining the micro-shear bond strength (μSBS) of different cements to commercially pure titanium (Cp Ti). Material and Methods A total of 100 milled cubes of Cp Ti was airborne-particle abraded using 250 μm aluminum oxide particles. Specimens were then divided into 5 groups (n=20) according to the type of resin cement used: (1) Panavia F.2, (2) Rely X U200, (3) Panavia SA LUTING Plus, (4) GC Fuji I, and (5) GC FujiCEM 2. After 24h storage, half of the samples were subjected to 5000 cycles of therm…
Prediction of Long-Term Chemical Evolution of a Low-pH Cement Designed for Underground Radioactive Waste Repositories
2012
Low-pH cements, also referred as low-alkalinity cements, are binders with a pore solution pH ≤ 11. They can be designed by replacing significant amounts of Portland cement (OPC) (≥40 %) by silica fume, which can be associated in some cases to low-CaO fly ash and/or ground granulated blast furnace slag to decrease the heat output during hydration by dilution of OPC and improve the mechanical strength of the final material. With the prospect of using these materials in a geological repository, it is of main importance to estimate their long-term properties and the influence of external and internal factors (chemical composition of the binder, storage temperature) on their characteristics. For…
Evaluation of the effect of home bleaching agents on surface microhardness of different glass-ionomer cements containing hydroxyapatite
2017
Background Home bleaching agents may exert some negative effects on surface hardness of restorative materials such as glass-ionomer cements (GICs). Since some studies have shown that some components such as hydroxyapatite (HA), as a bioactive glass, can improve the mechanical properties of dental materials, the effect of bleaching agents on surface hardness of GICs containing hydroxyapatite is questionable. This study was designed to evaluate the effect of home bleaching agents on the surface hardness of two different commercially available GICs containing hydroxyapatite. Material and methods 80 disk-shaped specimens were made from two different GICs, including resin modified glass-ionomer …
Hydration of alite containing aluminium
2011
Abstract The most important phase in Portland cement is tricalcium silicate, which leads during its hydration to the nucleation and growth of calcium silicate hydrate [referred to as C–S–H, (CaO)x–SiO2–(H2O)y]. The development of this hydrate around the cement grains is responsible for the setting and hardening of cement pastes. The general term for designating the tricalcium silicate in cements is alite. This name relates to all polymorphs containing various foreign ions inserted in their structure. These ions may influence the intrinsic reactivity, and once released during the dissolution, they may interact also with C–S–H. One of the most likely species to be inserted in the alite struct…
On the physico-chemical evolution of low-pH and CEM I cement pastes interacting with Callovo-Oxfordian pore water under its in situ CO2 partial press…
2014
International audience; Abstract Within the framework of geological repositories for radioactive waste, structural concretes must be adapted to the underground chemical conditions. CEM I cement-based materials are characterised by high pH that may produce an alkaline plume in the near-field of the repository. In order to avoid this problem, low-pH cements have been designed. This study compares the physico-chemical behaviour of a low-pH material with a CEM I cement paste, both being subjected to leaching by an aqueous solution. An original experimental setup was designed to reproduce the underground conditions using a specific CO2 regulation device. Under these conditions, the low-pH materi…
Formation of the C−S−H Layer during Early Hydration of Tricalcium Silicate Grains with Different Sizes
2005
Portland cement is a mixture of solid phases which all react with water. Tricalcium silicate (Ca3SiO5) is its main component and is often used in model systems to study cement hydration. It is generally recognized that setting and hardening of cement are due to the formation, by a dissolution-precipitation process, of a calcium silicate hydrate (C-S-H) on anhydrous grains during Ca3SiO5 hydration. The purpose of this paper is to study the effect of Ca3SiO5 particle size on the nucleation-growth process of C-S-H. An experimental study of the rate of hydration by using different grain sizes under controlled conditions has been performed. The experimental data have been compared with results o…
Influence of thickness and translucency of lithium disilicate ceramic on degree of conversion of resinous materials
2020
Background In this study was assessed the degree of conversion (DC) of amine-free resin cements light cured through lithium disilicate-reinforced ceramics at different thicknesses and translucency. Material and Methods Specimens were divided into 21 groups (n = 5) according to luting agent used: Variolink Esthetic LC (Light shade), RelyX Ultimate (A1 shade), and Filtek Z350 XT Flow (A1 shade); the ceramic translucency: low (LT) and high (HT); and the ceramic thickness: no ceramic (control), 0.5 mm, 1 mm, and 2 mm. A Teflon mold with (5 x 5 x 0.5 mm) was used to standardize the cement and over it the ceramic block from each group was placed. Set was cured using a polywave LED light (1200 mW/…
Does phosphorus affect the industrial Portland cement reactivity?
2018
Abstract The effect of phosphorous on the mineralogy and reactivity of Portland cement has been investigated through an industrial clinkers series. The samples were collected from the same Tunisian cement plant and classified according to the content of P2O5 from 0.5% to 1.1%. All samples were manufactured at the same thermal and cooling conditions as well as possible. The specimens were characterized by X-ray fluorescence spectrometry and optical microscopy techniques and their mineralogy was determined by X-ray powder diffraction coupled to the Rietveld analysis. The cements reactivity prepared from the clinkers was followed by means of isothermalcalorimetry. The compressive strength of t…
Recent Development on Self-Cleaning Cementitious Coatings
2013
The recent improvements in nano-technologies applied to building coatings are reported, starting from the historical origins of the research on photocatalysis. The description of the main air pollutants and the chemical mechanism of photocatalysis introduce to self-cleaning surfaces and the super-hydrophilic and hydrophobic attitude. Self-cleaning cementitious surfaces, due to nano-structured photocatalysts, mainly titanium dioxide, show environmental benefit in reduction of air pollutants and many experimental evidences are reported together with several applications on building construction. International standards and main spectroscopic techniques aim to evaluate the benefit in terms of …