Lead Nanowires for Microaccumulators Obtained Through Indirect Electrochemical Template Deposition
2010
Metallic lead nanowires were deposited within pores of commercial anodic alumina membranes having an average pore diameter of 210 nm. "Direct" electrodeposition was attempted from 0.1 M Pb(NO 3 ) 2 aqueous solution with a variable concentration of H 3 BO 3 as a chelating agent, but it gave unsatisfactory results. An "indirect" two-step deposition procedure was then adopted, consisting of the anodic electrodeposition of α-PbO 2 nanowires, followed by their in situ reduction to metallic lead. Both these processes occurred at a high rate so that the indirect method led to a complete template pore filling with pure polycrystalline Pb in short times and with a high current efficiency.
Template electrosynthesis of La(OH)3 and Nd(OH)3 nanowires using porous anodic alumina membranes
2007
High quality arrays of Ln(OH)3 (Ln = La, Nd) nanowires have been successfully fabricated for the first time by an electrochemical process using anodic alumina membrane templates. A physico-chemical characterisation of electrodeposited hydroxides has been carried out by different techniques (XRD, SEM and EDX). The results show that the synthesized nanostructures are crystalline, dense, continuous, well aligned, and with high aspect ratio, suggesting further development of possible applications in the lanthanide family species. Keywords: Nanowires, Anodic alumina membranes, Hydroxide electrodeposition, Template, Lanthanide compounds
Comments on 'formation and characterization of nanotubes of La(OH) 3 obtained using porous alumina membranes'
2010
New experimental evidence concerning the formation of La(OH)3 nanowires on anodic alumina membranes by cathodic polarization in 0.05 M lanthanum nitrate solution is provided to further support the conclusions previously reached in our work (Bocchetta et al 2007 Electrochem. Commun. 9 683-8) and recently criticized by González-Rovira et al (Nanotechnology 2008 19 495305). Some unconvincing aspects of the paper of González-Rovira et al, according to which the same electrochemical process should lead to the formation of hydroxycarbonate nanotubes, are also discussed.
A new route to grow oxide nanostructures based on metal displacement deposition. Lanthanides oxy/hydroxides growth
2012
Abstract A metal displacement reaction has been used in order to cause precipitation of oxide nanostructures within pores of anodic alumina membrane (AAM) templates. Here, we focus on the displacement deposition of LnO/OH (Ln = La, Ce, Sm, Er) nanostructures using Zn as sacrificial anode, employing a specific cell arrangement where a galvanic couple was formed between zinc anode and the Au thin layer covering template pore bottom. Progress of displacement deposition reaction into template channels was monitored measuring the open circuit potential as well as pH changes of the electrolyte. A progressive de-activation of the anode surface was observed for long deposition times, caused by depo…
Anodic alumina membranes as template for the synthesis of 1-D metal oxide and hydroxide nanostructures
2008
Anodic alumina membranes with highly ordered cylindrical pores and tuneable geometry have been prepared (pore diameters=20−200 nm; pore density 1012-1014 pores/m2; thickness: 20-100 mm) by controlling the anodizing process of aluminum in phosphoric, oxalic and sulphuric acid. The influence of different parameters (initial treatment of aluminium surface, composition of electrolyte, temperature and applied potential) on the final characteristics of the membranes have been investigated. The use anodic alumina membranes as template for the electrosynthesis of some metal hydroxides and oxides 1-D nanostructures (nanowires and nanotubes) will be also proved.
One-step electrochemical synthesis and physico-chemical characterization of CdSe nanotubes
2013
Abstract Stoichiometric CdSe nanotubes (NTs) with a length of ∼700 nm have been successfully grown by one-step electrochemical technique into anodic alumina membranes. Cyclovoltammetric method has been performed using porous anodic alumina as template electrode and an electrochemical bath containing Cd 2+ ions and SeO 2 . The as-prepared NTs have been identified as face-centred-cubic CdSe by XRD, while micro-Raman analysis reveals the typical peaks of nanostructured CdSe. The stoichiometric deposition of CdSe NTs formation is suggested by EDX analysis, with an average atomic percentage of Cd:Se of ∼0.93. Photoelectrochemical measurements reveal that CdSe NTs are photoactive materials with d…
Nanoscale membrane electrode assemblies based on porous anodic alumina for hydrogen–oxygen fuel cell
2007
In this paper, we demonstrate that nanoscale membrane electrode assemblies, functioning in a H 2/O 2 fuel cell, can be fabricated by impregnation of anodic alumina porous membranes with Nafion® and phosphotungstic acid. Porous anodic alumina is potentially a promising material for thin-film micro power sources because of its ability to be manipulated in micro-machining operations. Alumina membranes (Whatman, 50 μm thick, and pore diameters of 200 nm) impregnated with the proton conductor were characterized by means of scanning electron microscopy, X-ray diffraction, and thermal analysis. The electrochemical characterization of the membrane electrode assemblies was carried out by recording t…
Growth and Characterization of Ordered PbO[sub 2] Nanowire Arrays
2008
Large arrays of PbO 2 nanowires having high aspect ratios (length-to-width ratio) were grown by potentiostatic electrodeposition into anodic alumina templates under anodic polarization. Different electrolytic solutions were used in order to obtain nanowires of pure α-PbO 2 , pure β-PbO 2 , and a a + β mixture, We have found that, in a lead nitrate bath, a crystallographic structure of nanowires depends on pH; this latter was varied adding diluted nitric acid to the electrolyte. Nanowires of pure β-PbO 2 were obtained at pH 0.6, while mixed α-PbO 2 + β-PbΟ 2 nanowires were grown at pH 2. Pure α-phase was obtained in a bath containing lead acetate at pH 6.6. In all deposition conditions, nano…
Electrodeposition of supported gadolinium-doped ceria solid solution nanowires
2012
Gadolinium-ceria solid solution nanowires with tunable composition have been prepared through template cathodic electrodeposition from solutions containing Ce 3+Gd 3+ in a variable ratio. The employed template is Porous Anodic Alumina because it can function as thermal resistant separator supporting the nanowires if used as ionic conductor in Solid Oxide Fuel Cell (SOFC). Scanning Electron Microscopy of the deposited nanostructures revealed that the use of ethanol as solvent and metal chloride as electrolyte allowed to prepare continuous, compact and well defined nanowires with morphological features stable even after thermal treatment. EDX compositional analysis confirms the presence of bo…
Characterization of Sn-Co nanowires grown into alumina template
2009
Nanowires of Sn-Co alloys were grown inside the channels of anodic alumina membrane by potentiostatic deposition. The scanning electron microscope images showed the formation of cylindrical nanowires whose height was increasing with deposition time. The X-ray patterns did not show significant diffraction peaks, suggesting the formation of amorphous phases. The higher content of Co in the nanowires, in comparison to the initial composition of the electrolytic bath, was attributed to a higher rate of Co electrodeposition. These nanowires seem to possess specific features suitable for innovative application in the field of Li-ion batteries due to their dimensional stability and high specific s…