Determination of mass attenuation coefficient by numerical absorption calibration with Monte-Carlo simulations at 59.54 keV
2016
Abstract This study presents a numerical method in order to determine the mass attenuation coefficient of a sample with an unknown chemical composition at low energy. It is compared with two experimental methods: a graphic method and a transmission method. The method proposes to realise a numerical absorption calibration curve to process experimental results. Demineralised water with known mass attenuation coefficient ( 0.2066 cm 2 g − 1 at 59.54 keV) is chosen to confirm the method. 0.1964 ± 0.0350 cm 2 g − 1 is the average value determined by the numerical method, that is to say less than 5% relative deviation compared to more than 47% for the experimental methods.
F centre production in CsI and CsI–Tl crystals under Kr ion irradiation at 15 K
2000
Abstract We present results of simultaneous in situ luminescence and optical absorption studies in scintillator CsI and CsI–Tl crystals, exposed to very dense electronic excitations induced by 86Kr ions (8.63 MeV/amu). Irradiation at 15 K leads to the formation of the prominent F absorption band. In addition, several other features of the broad absorption between exciton and F bands were ascribed to an anion vacancy, α centre (240 nm), self-trapped hole, Vk centre (410 nm) and interstitials, H centres (560 nm). We have found that low doping of thallium (∼1017 cm−3) causes the F centre formation to proceed more rapidly than in pure crystal. On the other hand, we were not able to create any a…
Theoretical simulations of the radiation-induced defect processes in insulating materials
1994
Abstract The results of two basic kinds of computer simulations of radiation-induced processes in insulating materials, one based on quantum-mechanical and pair-potential (atomistic) approaches, and the other a phenomenological theory of diffusion-controlled reactions, are presented. It is shown that, by combining different techniques (atom-atom potentials and semi-empirical quantum chemical methods) the optimized geometry and the electronic structure of a family of hole centres in crystalline corundum (α-Al2O3) could be found. Their energetics are analyzed; V2−, V−V−Mg hole centres all have a common basic element, namely the diatomic molecule O23−, which is responsible for their similar ab…
The model of recombination process in TlBr
2002
The time-resolved luminescence was used as a tool in the study of recombination process in several undoped TlBr crystals. The spectra and decay kinetics observed under electron beam excitation were investigated. Observation of several luminescence bands with different decay rates shows that more than one recombination center is involved and the recombination process is quite complicated. The band at ∼2.5 eV is dominant under 10 ns excitation pulse (electron beam or nitrogen laser pulses). The results of short-lived absorption and luminescence are used for analysis of possible mechanisms of recombination processes in TlBr.
Measurement of the neutrino-oxygen neutral-current interaction cross section by observing nuclear deexcitation gamma rays
2014
We report the first measurement of the neutrino-oxygen neutral-current quasielastic (NCQE) cross section. It is obtained by observing nuclear deexcitation $\gamma$-rays which follow neutrino-oxygen interactions at the Super-Kamiokande water Cherenkov detector. We use T2K data corresponding to $3.01 \times 10^{20}$ protons on target. By selecting only events during the T2K beam window and with well-reconstructed vertices in the fiducial volume, the large background rate from natural radioactivity is dramatically reduced. We observe 43 events in the $4-30$ MeV reconstructed energy window, compared with an expectation of 51.0, which includes an estimated 16.2 background events. The background …
LiF crystals irradiated with 150MeV Kr ions: Peculiarities of color center creation and thermal annealing
2013
Abstract Color centers in LiF crystals are studied under irradiation at room temperature with 150 MeV Kr ions in the fluence (Φ) range of 1010–1014 ions/cm2 with a beam current density of 10, 50, and 100 nA/cm2, corresponding to flux of 4.46 × 109, 2.23 × 1010 and 4.46 × 1010 ions/(cm2 × s), respectively. At Φ ⩾ 3 × 1012 ions/cm2 besides F and Fn centers also charged F 3 + centers are created. Thermal annealing of irradiated LiF crystals with Φ ⩾ 1013 ions/cm2 at 400 K leads to a decrease of F centers (due to annihilation with H centers) and an enhancement of complex Fn color centers (neutral and charged) due to interaction with thermally activated anion vacancies. Annealing LiF crystals at…
Radiation displacement defect formation in some complex oxide crystals
2000
The work is devoted to an analysis of the formation processes of radiation displacement defects (RDDs) and color centers (CCs) under irradiation of complex oxide crystals. The results of the displacement process simulation as well as the analysis of the RDDs and CCs accumulation kinetics in some complex oxide crystals are presented. New experimental results on additional absorption spectra induced by neutron irradiation of LiNbO3 (LNO) crystals doped with Fe and Cr and YAlO3 (YAP) crystals doped with Nd and Er as well are presented. Dose dependencies are compared and their peculiarities are discussed. ” 2000 Elsevier Science B.V. All rights reserved.
Exciton-created defects and their participation in energy transfer from excitons to Tl ions in KI–Tl crystal
2000
Abstract Luminescence properties (spectra, yields, kinetics) of Tl ions induced by energy transfer from different types of anion excitons were studied and compared with those observed under direct Tl ion excitation by light quanta from A and C absorption bands in KI–Tl crystal at low temperature. The mechanism of energy transfer from excitons to the impurity ions was proposed based on the exciton-created defects participating in the impurity ion excitation.
Color centers and nanodefects in LiF crystals irradiated with 150MeV Kr ions
2012
Abstract The modifications of structure, optical and nano-mechanical properties of LiF crystals after irradiation with 150-MeV Kr +14 ions at a fluence of 6 × 10 12 ions cm −2 have been studied using optical absorption spectroscopy, scanning electron and atomic force microscopy, and nanoindentation. Optical spectroscopy shows the saturation of F centers and a comparatively high number of F n centers. AFM and SEM imaging reveals a nanostructured region with columnar nanocrystallites (size 30–90 nm). Nanostructuring occurs in depths up to 10 μm, where the ion energy loss surpasses a critical threshold of about 10 keV/nm. At a lower energy loss a zone enriched with dislocations is observed. S…
Thermal annealing and transformation of dimer F centers in neutron-irradiated Al2O3 single crystals
2020
This work has been carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom research and training programme 2014-2018 and 2019-2020 under grant agreement No 633053. The views and opinions expressed herein do not necessarily reflect those of the European Commission. In addition, the research leading to these results has received funding from the Estonian Research Council grant (PUT PRG619).