Metodi elettrochimici per la preparazione di nanostrutture in membrane di allumina anodica
2008
Influence of electrodeposition techniques on Ni nanostructures
2008
Abstract Different Ni nanostructure arrays were fabricated by pulsed electrodeposition from a Watts bath inside the pores of anodic alumina membrane (AAM) templates. Under a trapezoidal waveform of potential, consisting of fast linear sweeps between 0 and −3 V (SCE) interleaved by delay times at 0 (10 s) and −3 V (0.1 s), Ni nanowires were grown. The rate of nanowires growth was constant up to 60 min of deposition. For longer times, the growth of nanowires was not uniform, and after about 180 min some nanowires reached the template surface exposed to the electrolyte. Under square potential pulses between the same potentials (pulse length 1 s), nanotubes of Ni are obtained. Morphological ana…
Anodic alumina membranes: from electrochemical growth to use as template for nanostructure fabrication
2009
Electrochemical synthesis and characterization of self-standing metal oxide nanostructures
2009
Nanostructures Fabrication by Template Deposition in Anodic Alumina Membranes
2009
Raman spectroscopy of lead dioxide nanowires
2009
Visible Photoluminescence of Variable-Length Zinc Oxide Nanorods Embedded in Porous Anodic Alumina Template for Biosensor Applications
2021
Zinc oxide (ZnO) and porous anodic aluminum oxide (PAAO) are technologically important materials, rich with features that are of interest in optical applications, for example, in light-emitting and sensing devices. Here, we present synthesis method of aligned ZnO nanorods (NR) with 40 nm diameter and variable length in 150 to 500 nm range obtained by atomic layer deposition (ALD) of ZnO in pores of continuously variable thickness PAAO. The relative intensity of yellow (1.99 eV), green (2.35 eV), and blue (2.82 eV) photoluminescence (PL) components originating from the different types of defects, varied with non-monotonic dependency on the composite film thickness with a Fabry–Pérot like mod…
Porous Anodic Alumina as template for the cathodic electrodeposition of oxide and hydroxide nanostructures
2009
Advances in Anodic Alumina Membranes-based fuel cell: CsH2PO4 pore-filler as proton conductor at room temperature
2009
Abstract Anodic alumina membranes (AAM) filled with cesium hydrogen phosphate proton conductor have been tested as inorganic composite electrolyte for hydrogen–oxygen thin film (≤50 μm) fuel cell (TFFC) working at low temperatures (25 °C), low humidity ( T gas = 25 °C) and low Pt loading (1 mg cm −2 ). Single module TFFC delivering a peak power of around 15–27 mW cm −2 , with open circuit voltage (OCV) of about 0.9 V and short circuit current density in the range 80–160 mA cm −2 have been fabricated. At variance with pure solid acid electrolytes showing reproducibility problems due to the scarce mechanical resistance, the presence of porous alumina support allowed to replicate similar fuel…