Crystallized nano-sized alpha-tricalcium phosphate from amorphous calcium phosphate: microstructure, cementation and cell response
2015
New insight on the conversion of amorphous calcium phosphate (ACP) to nano-sized alpha tricalcium phosphate (α-TCP) provides a faster pathway to calcium phosphate bone cements. In this work, synthesized ACP powders were treated with either water or ethanol, dried, crystallized between 700 and 800 °C, and then cooled at different cooling rates. Particle size was measured in a scanning electron microscope, but crystallite size calculated by Rietveld analysis. Phase composition and bonding in the crystallized powder was assessed by x-ray diffraction and Fourier-transform infrared spectroscopy. Results showed that 50 nm sized α-TCP formed after crystallization of lyophilized powders. Water trea…
Amorphous polyphosphate/amorphous calcium carbonate implant material with enhanced bone healing efficacy in a critical-size defect in rats
2016
In this study the effect of amorphous calcium carbonate (ACC) microparticles and amorphous calcium polyphosphate (polyP) microparticles (termed aCa-polyP-MP) on bone mineral forming cells/tissue was investigated in vitro and in vivo. The ACC particles (termed ACC-P10-MP) were prepared in the presence of Na-polyP. Only the combinations of polyP and ACC microparticles enhanced the proliferation rate of human mesenchymal stem cells (MSCs). Gene expression studies revealed that ACC causes an upregulation of the expression of the cell membrane-associated carbonic anhydrase IX (CA IX; formation of ACC), while the transcript level of the alkaline phosphatase (ALP; liberation of orthophosphate from…
Biocompatibility studies of endothelial cells on a novel calcium phosphate/SiO 2 -xerogel composite for bone tissue engineering
2008
The bone biomaterial BONITmatrix®, a nanoporous, granular scaffold composed of hydroxylapatite, calcium phosphate and SiO2, linked by a dense collagen mesh, was tested for its biocompatibility using endothelial cells (EC) in the form of macrovascular HUVEC, microvascular HDMEC and the endothelial cell line ISOHAS-1. Cells were examined for their adherence and growth on the biomaterial and this was followed by confocal laser scanning microscopy after vital staining or immunocytochemical reactions, as well as by scanning electron microscopy. Macro- and microvascular ECs predominantly spread on BONITmatrix®-collagen mesh-covered surfaces and fibres and maintained their typical morphology. As E…
In vitro evaluation of biomimetic chitosan-calcium phosphate scaffolds with potential application in bone tissue engineering.
2013
This work reports on the physicochemical properties and in vitro cytotoxicity assessment of chitosan–calcium phosphate (Cs–CP) scaffolds for bone tissue engineering, which were synthesized by a novel biomimetic co-precipitation method. X-ray diffraction (XRD) along with scanning electron microscopy (SEM) analysis confirmed the porous morphology of the scaffolds and the amorphous nature of the inorganic phase with different crystallite sizes and the formation of various forms of calcium phosphate. Compressive mechanical testing revealed that the Young’s modulus of the biomaterials is in the range of human trabecular bone. In vitro tests were performed on the biomaterials for up to 14 days to…
Galvanic deposition and characterization of brushite/hydroxyapatite coatings on 316L stainless steel
2016
In this work, brushite and brushite/hydroxyapatite (BS, CaHPO4·H2O; HA, Ca10(PO4)6(OH)2) coatings were deposited on 316L stainless steel (316LSS) from a solution containing Ca(NO3)2·4H2O and NH4H2PO4 by a displacement reaction based on a galvanic contact, where zinc acts as sacrificial anode. Driving force for the cementation reaction arises from the difference in the electrochemical standard potentials of two different metallic materials (316LSS and Zn) immersed in an electrolyte, so forming a galvanic contact leading to the deposition of BS/HA on nobler metal. We found that temperature and deposition time affect coating features (morphology, structure, and composition). Deposits were char…
Bioresorbable β-TCP-FeAg nanocomposites for load bearing bone implants: High pressure processing, properties and cell compatibility.
2017
In this paper, the processing and properties of iron-toughened bioresorbable β-tricalcium phosphate (β-TCP) nanocomposites are reported. β-TCP is chemically similar to bone mineral and thus a good candidate material for bioresorbable bone healing devices; however intrinsic brittleness and low bending strength make it unsuitable for use in load-bearing sites. Near fully dense β-TCP-matrix nanocomposites containing 30vol% Fe, with and without addition of silver, were produced employing high energy attrition milling of powders followed by high pressure consolidation/cold sintering at 2.5GPa. In order to increase pure iron's corrosion rate, 10 to 30vol% silver were added to the metal phase. The…
Composite Hydrogels of Alkyl Functionalized Gellan Gum Derivative and Hydroxyapatite/Tricalcium Phosphate Nanoparticles as Injectable Scaffolds for b…
2021
An alkyl functionalized gellan gum derivative was here used to produce hydrogels containing hydroxyapatite and tricalcium phosphate nanoparticles as injectable nanostructured scaffolds for bone regeneration. The amphiphilic nature of the polysaccharide derivative along with its thermotropic behavior and ionotropic crosslinking features made possible to produce injectable bone mimetic scaffolds that can be used to release viable cells and osteoinductive biomolecules. The influence of different nanoparticles concentration on the rheological and physicochemical properties of the injectable systems was studied. We found that the presence of inorganic nanoparticles reinforces the three-dimension…
Collagen-embedded hydroxylapatite–beta-tricalcium phosphate–silicon dioxide bone substitute granules assist rapid vascularization and promote cell gr…
2010
In the present study we assessed the biocompatibility in vitro and in vivo of a low-temperature sol-gel-manufactured SiO(2)-based bone graft substitute. Human primary osteoblasts and the osteoblastic cell line, MG63, cultured on the SiO(2) biomatrix in monoculture retained their osteoblastic morphology and cellular functionality in vitro. The effect of the biomaterial in vivo and its vascularization potential was tested subcutaneously in Wistar rats and demonstrated both rapid vascularization and good integration within the peri-implant tissue. Scaffold degradation was progressive during the first month after implantation, with tartrate-resistant acid phosphatase-positive macrophages being …
Induction of carbonic anhydrase in SaOS-2 cells, exposed to bicarbonate and consequences for calcium phosphate crystal formation.
2013
Ca-phosphate/hydroxyapatite crystals constitute the mineralic matrix of vertebrate bones, while Ca-carbonate dominates the inorganic matrix of otoliths. In addition, Ca-carbonate has been identified in lower percentage in apatite crystals. By using the human osteogenic SaOS-2 cells it could be shown that after exposure of the cells to Ca-bicarbonate in vitro, at concentrations between 1 and 10 mm, a significant increase of Ca-deposit formation results. The crystallite nodules formed on the surfaces of SaOS-2 cells become denser and larger in the presence of bicarbonate if simultaneously added together with the mineralization activation cocktail (β-glycerophosphate/ascorbic acid/dexamethason…
Cream fermentation by a mixed culture of lactococci entrapped in two-layer calcium alginate gel beads
1992
This investigation was directed towards the development of a process which produces a fermented cream of greatly reduced cell number.Lactococcus lactis subsp.Lactis andLactococcus lactis subsp.lactis biovardiacetylactis were entrapped separately in normal or two-layer Ca-alginate gel beads. Pasteurized cream (31% fat content) was inoculated with free-cells and with normal or two-layer beads. When 8% of the total volume was occupied by the gel, there was 300–800 times more inoculum in this system and the fermentation time was considerably reduced (5h against 18h). When pH 5.0 was reached, the residual free-cell count was 150 and 1800 times less than for a classical inoculation method with fr…