Improvement of boehmite nanoparticles' aqueous dispersability by controlling their size, shape and crystallinity
2014
In this work, results on the control of size, shape, crystallinity and aqueous dispersability of boehmite prepared by a hydrothermal process are reported. The two step synthetic procedure entailed the precipitation of a xerogel by adding NaOH until pH 10 to a solution of aluminum nitrate at 100 °C without or with additives such as tartaric acid and maltitol, and a subsequent hydrothermal treatment at 150 and 200 °C for different periods of time. The final materials were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD) and elemental analysis. The stability and other characteristics of the boehmite nanoparticle aqueous dispersions were determined by measuring t…
One-pot preparation of surface modified boehmite nanoparticles with rare-earth cyclen complexes.
2007
We report on the one-pot synthetic procedure of cyclen derivatives bearing three acetate groups attached on boehmite nanoparticles, the complexing capabilities of these inorganic–organic hybrid materials with rare earth cations, and the behaviour as contrast agents or fluorescence probes. Delgado Pinar, Estefania, Estefania.Delgado@uv.es ; Frias Martinez, Juan Carlos, Juan.Frias@uv.es ; Albelda Gimeno, Maria Teresa, Teresa.Albelda@uv.es ; Alarcon Navarro, Javier, Javier.Alarcon@uv.es ; Garcia-España Monsonis, Enrique, Enrique.Garcia-Es@uv.es
Naphthalene-containing polyamines supported in nanosized boehmite particles
2007
Boehmite nanoparticles with covalently linked polyamine chains functionalized with naphthalene fluorophores have been prepared and characterized. The characterization of the materials by elemental microanalysis, X-ray powder diffraction, MAS 29Si NMR and electron microscopy unambiguously prove that the covalent anchorage had occurred. Steady-state fluorescence emission studies show that the luminescent properties of the modified nanoparticles are sensitive to changes in concentration of hydrogen ions, metal ions and anionic nucleotides such as ATP. The behaviour of the attached materials in aqueous solution is parallel to the behaviour of the single fluorophoric polyamines. Comparisons are …
Grafted squaramide monoamine nanoparticles as simple systems for sulfate recognition in pure water.
2012
New simple systems formed by a chain containing a squaramide function and a quaternised amine group attached to boehmite or silica-coated boehmite nanoparticles are able to discriminate anions in pure water.
Lanthanide complexes as imaging agents anchored on nano-sized particles of boehmite
2011
International audience; The synthesis of boehmite nanoparticles modified with lanthanides (Eu, Tb and Gd) is described. Their synthesis, characterization and in vitro assays with HeLa cells were performed. The nuclear magnetic relaxation dispersion (NMRD) profiles of the two chelating moieties were studied. Imaging data from laser scanning confocal fluorescence microscopy and flow cytometry revealed that the nanoscaffolds were taken up by the cells, distributed throughout the cytoplasm and showed no toxicity. This platform could represent an alternative to silica-based inert matrices as imaging vehicles.
The influence of the nature of the surface oxide on the adhesive fracture energy of aluminium-bonded joints as measured by T-peel tests
2008
Abstract Modification of aluminium alloy substrates microstructure and morphology by depositing new oxide layers on top of the metal surface has been investigated, with the aim of improving adhesion. The effect of treating the metal with boiling water or immersing it in a cerate bath has been studied by means of electron microscopy, contact angle measurements and peeling tests. The formation of pseudoboehmite layers or cerium conversion coatings both led to an increase in joint's adhesive fracture energy and more durable adhesive bonds with respect to joints obtained with “mechanically grinded only” substrates. Differences in the performance of the bonded joints has been discussed in terms …
The Relevance of Kneading and Extrusion Parameters in the Manufacture of Active Porous Aluminas from Pseudoboehmites
1987
In order to study the effect-on crushing strength, attrition resistance, specific pore volume, and pore volume distribution of extrudates-of kneading and extrusion parameters in the manufacture of active porous aluminas, a commercial pseudoboehmite (Pural SB from Condea Chemie, Brunsbuttel, FRG) was employed. A minimum kneading torque was required to prepare an extrudable paste, predetermined by extrusion conditions. The torque had an upper limit with respect to certain extrudate properties. The amount of water and the concentration of nitric acid as binder solutions were found to have a decisive bearing on the mechanical properties and the distribution of the pore volume. Crushing strength…
Boehmite Supported Pyrene Polyamine Systems as Probes for Iodide Recognition
2013
New organic–inorganic fluorescent probes made by attaching the tripodal polyamine (tris(2-aminoethyl))amine (tren), propylamine, or diethylenetriamine functionalized with pyrene as a fluorophore to an γ-aluminum oxohydroxide matrix have been prepared and studied both in solution and supported on the surface of boehmite nanoparticles. Both kinds of systems have been revealed as sensitive and selective fluorescence turn-off chemosensors for iodide in aqueous solution with an estimated detection limit that reaches 36 ppb. The recognition characteristics and photophysical properties of these molecules are essentially preserved when they are grafted to the surface of the particles. Since the nan…
Tuning the size and shape of nano-boehmites by a free-additive hydrothermal method
2015
A synthetic procedure allowing the control of boehmite micro and nanoparticles is presented. The proposed hydrothermal synthetic procedure is based on the control of three reaction parameters, the pH and temperature of precipitation of xerogels and the water/xerogel ratio for the hydrothermal process, carried out at 200 °C for 48 h. Results obtained by measurements on transmission electron microscopy (TEM) images indicate that at pH 5 micro or nanorods of controlled length between ca. 300 and 50 nm were obtained depending on the temperature of precipitation of the xerogel (25 or 100 °C) and the water/xerogel ratio used (1/1, 6/1, 15/1). On the contrary, at pH 10, nanoplatelets with major ba…
New sensing devices part 1: indole-containing polyamines supported in nanosized boehmite particles
2005
The synthesis, characterisation and optical properties of new sensing systems made by attaching different polyamine chains functionalised with an indole fluorophore to a boehmite matrix is reported for the first time. Firstly, a family of tri(alkoxy)alkylpolyaminosilanes have been reacted with indole-3-carboxaldehyde to form the corresponding Schiff bases which were reduced with sodium borohydride. The anchoring to the surface of the boehmite nanoparticles was carried out by reacting the precursors with the hydroxyl groups available in the surface of the support. The characterisation of the materials by elemental microanalysis, X-ray powder diffraction, CP-MAS 29Si NMR and electron microsco…