New low-temperature phosphate glasses as a host for Europium Ions
2021
Abstract Artificial lightining, especially that of light emitting diodes, and telecommunications are penetrating every part of human lives daily. Different compositions phosphate glasses were suggested as a suitable host material for Eu3+ ions. Here rare earth metal ions act as luminescent centers also perturbing the bond order of phosphate glass network comprised of (PO4)3−, [−(O)PO3]2−, [−(O)2PO2]−, [−(O)3PO] structural units, which is indicated by Raman spectroscopy, confirming successful integration of aforementioned ions into the glass material. Glasses doped with Eu3+ ions show their typical photoluminescence spectra in low symmetry environment, consisting of the highest intensity 5D0…
Thermal expansion and polarization of (1-x)PNN-xPT solid solutions
2019
The paper presents the results of detailed studies of the thermal expansion of (1-x)PbNi1/3Nb2/3O3-xPbTiO3 solid solutions with x = 0-0.8. The anomalous and lattice contributions to deformation and...
Anomalies of dielectric properties and conductivity in single domain LiNbO3:Zn crystals
2016
ABSTRACTA study of the temperature dependence of dielectric constant, conductivity, and piezoelectric modulus in the single-domain state of LiNbO3 crystals modified by Zn admixture at threshold concentration is reported. Unipolarity of the LiNbO3:Zn crystals is observed to increase after treatment of brand-new samples by high-temperature electro-diffusion annealing and by subsequent high-temperature annealing of short-circuited samples. The observed effects are explained as a result of meta-stable residual domains collapsing at high temperature the collapse being assisted by disintegration of charged clusters stabilizing domain walls. The rise of unipolarity is accompanied by anomalies on t…
The effects of the additive of Eu ions on elastic and electric properties of BaTiO3ceramics
2016
ABSTRACTThe BaTiO3 and BaTiO3+X%wt.Eu2O3 (X = 1, 2, 3) ceramics were prepared by a solid phase reaction. The structural and morphology studies were carried out by means of an X-ray diffraction technique and scanning electron microscopy, respectively. Elastic moduli were determined with the use of an ultrasonic method. The dielectric permittivity (ϵ′) and tanδ as a function of composition and temperature were investigated. The increasing concentration of Eu ions leads to a slight shift of the Curie temperature and changes the characteristics of ϵ′ and tanδ. The structural, mechanical and dielectric properties of the BTEX ceramics were discussed in terms of microstructure and dopants contents.
SrTiO3-doping effect on dielectric and ferroelectric behavior of Na0.5Bi0.5 TiO3 ceramics
2018
Lead-free (Na0.5Bi0.5)1-xSrxTiO3 ceramics (x = 0–0.04) were synthesized by a conventional mixed-oxide technique. The microstructure study showed a dense structure, in good agreement with that of ab...
Preparation and dielectric properties of (Na 0.5 K 0.5 )NbO 3 ceramics with ZnO and CdO addition
2019
The sintering conditions, phase structure, and electrical properties of the ZnO and CdO doped (Na0.5K0.5)NbO3 (NKN) ceramics were investigated and discussed. All the samples were prepared by a solid state reaction method. The addition of 1 wt% CdO and ZnO as a sintering aid increases the density and lowering the sintering temperature. XRD analysis indicated perovskite structure with monoclinic symmetry. The investigated samples are good quality, the grains are well shaped without a glassy phase. The results of dielectric measurements revealed, that the dielectric properties of NKN based ceramics are stable in the wide temperature range.
EPR in glass ceramics
2019
Abstract The development of novel materials requires a profound understanding of the relationship between a material's performance and its structural properties. Electron paramagnetic resonance (EPR) is a well-established technique for a direct detection and identification of paramagnetic defects in solids. This chapter provides an overview of the applicability of continuous wave EPR spectroscopy in the studies of glass ceramics focusing on transition metal (Mn2 +, Cu2 +, Cr3 +) and rare earth (Gd3 +, Eu2 +, Er3 +, Yb3 +) ion local structure analysis. EPR spectra features of the above-mentioned paramagnetic probes in glasses and glass ceramics are compared and discussed in detail. The chapt…
Comparative Study on Micromechanical Properties of ZnO:Ga and ZnO:In Luminiscent Ceramics
2021
The research has been supported by the Project ERANET RUS_ST#2017-051(Latvia) and #18-52-76002 (Russia). The Institute of Solid State Physics, University of Latvia as the Centre of Excellence has received funding from the European Union’s Horizon 2020 Framework, Program H2020-WIDESPREAD-01-2016-2017-Teaming Phase 2 under grant agreement No. 739508, project CAMART2.
Structural, microstructural and dielectric studies in multiferroic LaSrNiO4-δ prepared by mechanical milling method
2016
Abstract The solid solution LaSrNiO 4-δ has been successfully prepared by a rapid method combining mechanical milling and heat treatment. The structure and microstructure transformations were characterized by X-ray powder diffraction, scanning and transmission electron microscopy. The dielectric property was also investigated. After 10 h of milling and 8 h of heat treatment at 1300 °C, X-ray diffraction analysis revealed LaSrNiO 4-δ single phase, exhibiting tetragonal structure with space group of I4/mmm. This result was confirmed by using the ED pattern for sample using the [001] orientation. The corresponding lattice images show the compound to be well ordered, indicating the absence of s…
Improve the dielectric properties of PrSrNi0.8Mn0.2O4 compounds by longer mechanical milling
2018
Abstract Structural and dielectric properties of PrSrNi 0.8 Mn 0.2 O 4 ceramics elaborated by a rapid method combining mechanical milling and heat treatment were studied for the first time. The raw materials are milled at different times ( t mil = 0, 5, 10, 20 and 30 h) and annealed at 1300 °C for 8 h to produce a revealed PrSrNi 0.8 Mn 0.2 O 4 single phase, exhibiting tetragonal structure with space group I 4/ mmm . This result was confirmed by using the TEM/ED pattern for sample milled at 30 h using the [001] orientation. The corresponding lattice images show a well-ordered compound, indicating the absence of stacking faults and the growth of the crystallites. Giant dielectric response …