Preparation and characterization of polyamide 6/polyethylene blend-clay nanocomposites in the presence of compatibilisers and stabilizing system
2010
Abstract Several compatibilising systems were added to high-density polyethylene (HDPE) and polyamide 6 (PA6) blends in the presence of an organically modified montmorillonite (OMM). All the blends were prepared by using a co-rotating twin-screw extruder and characterized by SEM, TEM and XRD analyses. In addition, the rheological behaviour and the mechanical properties – tensile and impact – were evaluated. The presence of OMM affects the dimensions of the polymeric phases in the blend but not their mutual adhesion, granted only by the compatibilisers. TEM, SEM and XRD analyses indicated that there is a strict correlation between the compatibilisation level and the final interlayer distance…
Effect of adding new phosphazene compounds to poly(butylene terephthalate)/polyamide blends. I: Preliminary study in a batch mixer
2005
Abstract Poly(butylene terephthalate) (PBT) and a sample of polyamide have been melt processed in the presence of two new phosphazene compounds, namely 2,2-dichloro-4,4,6,6-bis[spiro(2′,2″dioxy-1′,1″biphenyl)]cyclotriphosphazene (2Cl-CP) and 2,2-bis-(2-methoxy-4-methyleneoxy-phenoxy)-4,4,6,6,-bis[spiro(2′,2″dioxy-1′,1″biphenyl)]cyclophosphazene (CP-2EPOX). The blends were prepared by using polyamide 6 (PA6) at 25/75 w/w and 75/25 w/w composition. In order to perform a preliminary analysis on the behaviour of the blends, the materials were prepared in a batch mixer. The materials have been completely characterized from a rheological, morphological, mechanical point of view. The results indic…
Properties and morphology of PMMA/ABN blends obtained via MMA in situ polymerisation through γ-rays
2001
Abstract Methylmethacrylate polymerisation in the presence of 4 wt% butadiene-acrylonitrile rubber was carried out at fixed dose-rate and temperature. The effect of irradiation was investigated with respect to the mechanical and dynamic-mechanical properties in the solid state. A general increase of the “compatibilisation” on irradiation is obtained. In fact both rubber and polymethylmethacrylate glass transition temperatures, determined through dynamic-mechanical analysis, reveal the presence of strong interactions between the components. Furthermore an improvement of the mechanical tensile properties of the blends is observed when irradiation is continued after polymerisation, at least un…