The structural and dielectric properties of the Na0.96Li0.04NbO3ceramics
2007
Ceramic samples Na0.96Li0.04NbO3 were obtained using ceramic technology. The phase and structural analysis, the microstructure, EDS and EPMA, dielectric and hysteresis loops measurements have been performed. The dielectric and hysteresis loops measurements of Na0.96Li0.04NbO3 have been carried out. The dielectric measurements were performed both without and under axial pressure up to 120 MPa. It was shown that Na0.96Li0.04NbO3 ceramics have orthorhombic symmetry at room temperature and undergo a first order phase transition at a temperature of about 570 K. The axial pressure shifts the phase transition temperature and decreases the hysteresis in field-polarisation and field-strain dependenc…
The Effect of Bias Field on Dielectric Response in Lead Ferrotantalate Ceramics
2011
Studies of dielectric properties of PbFe1/2Ta1/2O3 ceramics at low- and infra-low-frequencies under bias field over a wide range of temperatures are reported. Applied bias field is found to broaden the ϵ′(Т) maxima shifting positions Тm of the maximums to higher temperatures. Additional anomalies in the dielectric response are revealed at T<Тm. The anomalies in the vicinity of Тm are related to structural change at phase transition, while those observed at TТm – to magneto-electric interactions in PbFe1/2Ta1/2O3.
PHASE TRANSITIONS IN Na1/2Bi1/2TiO3-SrTiO3-PbTiO3 SOLID SOLUTIONS
2009
ABSTRACT Studies of nature of polarization in ternary solid solutions of Na1/2Bi1/2TiO3-SrTiO3-PbTiO3 were done, using measurements of dielectric properties and polarization hysteresis loops. Various stages of relaxor behavior depending on concentration of PbTiO3 were established and compared with other known ferroelectric relaxors.
Dielectric Properties and Conductivity of Ferroelectric LixNa1-xTa 0.1Nb0.9O3 Solid Solutions
2011
Results of a study of dielectric properties and conductivity of ferroelectric perovskite solid solutions of the LixNa1-xTa0.1Nb0.9O3 (х = 0.03–0.135) series with the 290–700 K thermal range and frequencies from 25 to 106 Hz are reported. The charge in this kind of materials is shown to be transferred by Li+ ions the contribution from bulk transport of ions dominating. A first order phase transition close to the second order transitions proceeds in LixNa1-xTa0.1Nb0.9O3 solid solutions within the thermal range examined. The increase of Li concentration enhances the features of the second order transition.
Computer simulation of models for orientational glasses
1991
Abstract Monte Carlo studies of two- and three-dimensional lattice models where quadrupoles interact with a nearest-neighbor Gaussian coupling are reviewed. None of these models has a thermodynamic glass phase transition at non-zero temperature like the Ising spin glass: rather, phase transitions at zero temperature occur that exhibit a dynamical freeze-in spread out over a wide temperature range and are characterized by a strongly non-exponential relaxation. The time-dependent glass order parameter, q(t), decays with time, t, compatible with a stretched exponential decay q(t) ∼ exp [− (t/τ)y] with a strongly temperature-dependent exponent. While the static glass ‘susceptibility’ for isotro…
PHASE TRANSITIONS IN THE PLZT x/85/15 SOLID SOLUTIONS
2008
ABSTRACT Role of a La on the nature of phase transition in the PLZT x/85/15 is compared with the PLZT compositions of lower Zr/Ti ratio. Thermal dependence of the dielectric permittivity, thermal expansion and elastic modulus reveal sequential transfer from macroscopic ferroelectric to antiferroelectric and nonpolar state, if La concentration is increased. Diffused, from frequency independent thermal dependence of dielectric permittivity for compositions in certain La concentration range above 4 at% coexist with the well expressed phase transition between paraelectric and antiferroelectric phases.
Broadband dielectric spectroscopy of PbMg1/3Nb2/3O3–PbSc1/2Nb1/2O3 ceramics
2010
Abstract Broadband dielectric spectroscopy results of various ordered and disordered (1 − x)Pb(Mg1/3Nb2/3)O3–(x)Pb(Sc1/2Nb1/2)O3 (PMN–PSN) ceramics are investigated in the temperature range from 80 K to 300 K and frequency range from 20 Hz to 2 THz. Dielectric dispersion is very broad and in the ferroelectrics case (x = 1, 0.95) consists of two parts: low-frequency part caused by ferroelectric domains and higher frequency part caused by soft mode. The relaxational soft mode exhibits pronounced softening close to phase transition temperature, as it is typical for order–disorder phase transitions. By substituting Sc3+ by Mg2+ in PMN–PSN ceramics relaxation slows down, and for relaxors (x = 0.…
DIELECTRIC AGEING IN LAYERED FERROELECTRICS
2008
ABSTRACT Studies of the effects of sample history on long-term relaxation of polarization in the Na0.5Bi8.5Ti2Nb4O27 and Na0.5Bi8.5Ti2Ta4O27 ferroelectrics of layered structures are reported. The type of functional relationship of e′(t) at measuring procedures including heating or cooling to the temperature being examined Ta is found to change from exponential (Kohlrausch function) to logarithmic. Results are discussed within the assumption of presence of defect complexes in disordered ferroelectrics.
Size effects of static and dynamic polarization in ferroelectric thin film multilayers
2001
Abstract A thermodynamic theory for the calculation of static and dynamic polarization profiles of ferroelectric thin film multilayers is developed. The free energy functional is written down using a multilayer model in which c-domain layers of the ferroelectric material alternate with a-domain layers of a second ferroelectric materials. We assume that the interfaces are perfectly sharp and that the polarization at these boundaries is zero. The equilibrium polarization profile, its temperature and thickness dependencies were determined from the solutions of the Euler-Lagrange equations. A thickness induced ferroelectric phase transition is shown to exist and its transition temperature and c…
Dielectric Properties of Na0.5K0.5(Nb1-xSbx)O3+MnO2 Ceramics (x = 0.04, 0.05 and 0.06)
2011
Lead-free ceramics Na0.5K0.5(Nb1-xSbx)O3+0.5mol%MnO2 (x = 0.04, 0.05 and 0.06) were prepared by conventional sintering and hot pressing process; their microstructure and dielectric properties have been studied. It is found that increase of sintering temperature promotes the obtaining highly dense microstructure and increase in grain size while doping with Sb contributes to more dense and homogeneous microstructure and smaller grain size. Low frequency (100 Hz-200 kHz) investigations revealed the diffuse phase transitions. It can be concluded from experimental results that Sb doping improves dielectric properties. The obtained materials are expected to be promising candidates for lead-free e…