Evaluation of crack-closure by second harmonic thermoelastic stress analysis
2022
The work illustrates a new experimental approach to evaluate crack-closure in samples undergoing Fatigue Crack-Growing. Crack-closure leaves a peculiar signature on both amplitude and phase of the harmonic of the temperature signal at twice the loading frequency (Second Harmonic), due to the periodic nature of the internal elastic compression stresses. Thermoelastic Stress Analysis (TSA) is successfully applied to reveal such signatures on Single-Edge-Notched steel samples. A methodology is also proposed to evaluate the Crack-Opening-Load from temperature data. The work finally explores the influence of crack-closure on crack-tip identification and on the evaluation of the Stress Intensity …
Binder and Mixture Fatigue Performance of Plant-Produced Road Surface Course Asphalt Mixtures with High Contents of Reclaimed Asphalt
2019
The aged properties of Reclaimed Asphalt (RA) binders are one of the main factors working against their utilisation in high-RA content (>
Cracking behavior of zeolites with connected 12- and 10-member ring channels: The influence of pore structure on product distribution
1997
n-Heptane has been cracked on a CIT-1 zeolite which has connected 12- and 10-member ring (MR) channels, and its behavior was compared with that of MCM-22 with nonconnected 12- and 10-MR channels, and SSZ-24 and BETA with unidirectional and tridirectional 12-MR channels, respectively. The kinetic rate constant is highest for CIT-1, and the decay constant is lowest. From the selectivity point of view, its behavior can be better represented by a system with large cavities (the intersections between the 12- and 10-MR) connected by windows. This gives a behavior typical of that of large pore zeolites. CIT-1 produces a remarkably high selectivity toi-C4, and specially to isobutane. This zeolite s…
Steam catalytic cracking of naphtha over ZSM-5 zeolite for production of propene and ethene: Micro and macroscopic implications of the presence of st…
2012
One option to produce more ethene and propene can be to crack naphtha type fractions in dedicated smaller FCC units. We present here the results obtained for high temperature steam catalytic cracking (SCC) of a representative naphtha product (n-heptane) with ZSM-5. It has been found that under those conditions the presence of steam produces an irreversible dealumination of the zeolite as well as a reversible deactivation due to the interaction of water with active sites with a negative effect on protolytic cracking. A kinetic decay model that takes into account the two phenomena has been developed. The apparent activation energy is lower in the presence of steam. It appears that whilst the …
Mechanism of brittle fracture in a ductile 316 alloy during stress corrosion
1990
Abstract The ductile f.c.c. 316 alloy is shown to exhibit brittle transgranular (and intergranular) stress corrosion cracking in a 153°C MgCl2 solution at free corrosion potential. Tests on smooth and pre-cracked specimens are performed to identify the mechanisms of fracture. Transgranular cracking is related to both a discontinuous microcleavage mainly on {100} planes and a microshearing on {111} planes. A new physical modelization is proposed to explain the brittle transgranular cracking. It is based on the influence of the localized anodic dissolution on the enhancement of the plasticity at the crack tip. The formation of dislocation pile-ups and the conditions of restricted slip induce …
LONG-TERM STRUCTURAL DEFICIENCIES IN A MAT FOUNDATION ON CLAY SOIL
2013
A 3-story building with a mat foundation consisting of a slab on a grid of grade beams performed poorly on clay soil. Cracking of the slab became rogressively worse as a result of the incorrect esign and fluctuations in the groundwater pressure under the foundation. The cyclic presence and absence of water rusted the steel reinforcement, and the sulfates in the clay soil caused formation of ettringite in the concrete. Plastic hinges formed in the slab and settlements occurred, causing damage to the beams. The situation is still in progress and may lead to the collapse of the structure under normal service conditions. The geotechnical and structural investigations performed to survey and ass…
Fatigue crack propagation from a cold-worked hole
2007
Abstract The cold expansion process is widely used to enhance the fatigue life of structures with fastener holes. Various studies assert that the cold expansion improves the fatigue strength of fastener holes; however, the improvement of fatigue life is difficult to quantify. Therefore, the influence on fatigue life of cold-worked process was studied by numerical and experimental tests. Then, a parametric study on material hardening behavior and Bauschinger’s parameter was performed for several loading conditions in order to determine their effect on crack growth propagation. The results of the numerical tests have exhibited a good prediction of the fatigue life of the component.
Effect of steel collars on the seismic behaviour of axially-cracked historical stone columns
2014
Granite and heavy stone circular columns could often be found in the cultural heritage among ancient churches and historical buildings in all the Mediterranean area. Their good strength properties allow them to carry big load values, while their bright colours and aesthetical characteristics were used by a lot of architects in the past to achieve structural solutions with great visual impact.Though such materials have great compressive strength values, environmental effects, especially long term effects, can damage the structural members, by cracking them. In this way the slenderness of the column increases, and the presence of an imposed ground motion can be very dangerous, since the colum…
Hot cracking in Al–Mg–Si alloy laser welding – operating parameters and their effects
2005
Abstract Hot cracking is a phenomenon that frequently occurs in the laser welding of some “special” alloys, such as the aluminium–magnesium–silicon type. Each occurrence of this phenomenon needs to be studied in itself, taking into account not only the individual, but also the interactive, influences of the various parameters. The advantage of using laser beams in welding processes lies in the speeds that can be reached. The disadvantage, however, is that, owing to the high cooling rates characteristic of the interaction between the laser beam and the material, the welding speed itself becomes a cause of hot cracking. The aim of this paper is to see how this disadvantage may be eliminated. …
The role of pore topology on the behaviour of FCC zeolite additives
1999
Abstract A large variety of zeolite topologies including: large pore tridirectional (Beta), large pore unidirectional (Mordenite, SSZ-24), bidirectional 10 member ring pores (MRP) (ZSM-5), bidirectional 10 × 8 MRP (Ferrierite), tridirectional with connected 12 and 10 MRP (CIT-1), bidirectional with 12 MRP connected by 10 MRP (NU-87), tridirectional with 10 × 11 × 12 MRP (NU-86), and finally 10 MRP, and independent 12 MR cavities connected by 10 MR windows (MCM-22), have been studied as catalysts for the cracking of a gasoline range model molecule ( n -heptane). Kinetic and decay constants as well as selectivity parameters such as paraffin/olefin, i -C 4 / n -C 4 , i -C 5 / n -C 5 , C 3 /C 4…