Negative thermal expansion in cuprite-type compounds: A combined synchrotron XRPD, EXAFS, and computational study of Cu2O and Ag2O
2006
Cuprite-type oxides (Cu2O and Ag2O) are framework structures composed by two interpenetrated networks of metal-sharing M4O tetrahedra (M = Cu, Ag). Both compounds exhibit a peculiar negative thermal expansion (NTE) behaviour over an extended temperature range (9 240 K for Cu2O, 30-470 K for Ag2O). High-accuracy synchrotron powder diffraction and EXAFS measurements were performed from 10 K up to the decomposition temperature to understand the nature of the NTE effects. The critical comparison of the diffraction and absorption results concerning the temperature dependence of the interatomic distances and of the atomic vibrational parameters proves to be fundamental in defining the local dynam…
Multiple-scan voltammetry and OCP: Archaeometric tools for dating archaeological bronzes
2021
[EN] The application of a multiple-scan strategy to nanosamples taken from 18 cross-sections of Bronze Age arms and armour, as well as two Roman coins using two solid-state electrochemical techniques, the voltammetry of immobilized microparticles (VIMP) and open circuit potential measurements (OCP) is described. The voltammetric responses in contact with aqueous acetate buffer can be attributed to the reduction of cuprite with variable degree of compaction and crystallinity revealing significant differences in the gradient of such properties with depth. Such differences are also revealed by "dry" OCP measurements connecting points in the cross section near and separated from the corrosion l…
Sintering of copper nanopowders under hydrogen: an in situ X-ray diffraction analysis.
2003
Abstract The reduction by hydrogen gas of the cuprite layer on copper nanocrystals and the subsequent sintering of the nano-particles were studied using in-situ X-ray diffraction and dilatometry. Spherical nanocrystals produced by evaporation and condensation have an average size of 35 nm, exhibiting a large surface curvature. Each nanoparticle is coated with a 3.5 nm layer of Cu 2 O, which is rough and disordered, as revealed by high-resolution electron microscopy. Reduction by hydrogen of this curved cuprite layer occurs at 363 K, which is ≈65 K lower than is observed on a layer supported by micrometer-sized or bulk copper with a flat surface. The reduction process and its effect on the s…
Synchrotron Radiation-Based Micro-XANES and Micro-XRF Study of Unsuccessfully Produced Egyptian Blue from the Late Hellenistic Production Site of Kos…
2021
International audience; This paper examines the production technology of Egyptian blue, an ancient artificial pigment, through the investigation of an unsuccessfully produced pellet derived from the Hellenistic production site of Kos (Dodecanese, Greece). This heterogeneous material was investigated by a combination of laboratory and synchrotron radiation-based (SR) techniques: scanning electron microscopy coupled with energy-dispersive Xray spectrometry, micro-Raman spectroscopy, high-resolution SR micro-X-ray fluorescence spectroscopy, and SR micro-X-ray absorption near-edge structure spectroscopy (XANES), at the ID21 beamline of the European Synchrotron Radiation Facility. Principal comp…
Reaction between Cu-bearing minerals and hydrothermal fluids at 800 °C and 200 MPa: Constraints from synthetic fluid inclusions
2020
Abstract Transport and deposition of copper in the Earth's crust are mainly controlled by the solubility of Cu-bearing phases and the speciation of Cu in magmatic-hydrothermal fluids. To improve our understanding of copper mobilization by hydrothermal fluids, we conducted an experimental study on the interaction between Cu-bearing phases (metallic copper, Cu2O, CuCl) and aqueous chloride solutions (H2O ± NaCl ± HCl; with Cl concentrations of 0 to 4.3 mol kg-1). The experiments were run in rapid heat/rapid quench cold-seal pressure vessels at 800 °C, 200 MPa, and logfO2 ~ NNO+2.3. Either Cu or Au capsules were used as containers. The reaction products were sampled in situ by the entrapment o…
Electrochemical Characterization of Coinage Techniques the 17(th) Century: The maravedis Case
2017
[EN] The voltammetry of immobilized particles (VIMP) methodology was applied to the discrimination of Spanish maravedis produced in 10 different mints between 1661 and 1664 using characteristic signatures for the reduction of cuprite and tenorite in the patina of the coins and catalytic effects on the hydrogen evolution reaction (HER). The variation of the apparent tenorite/cuprite ratio with depth was fitted to potential laws differing from one mint to another for A Coruna, Burgos, Cordoba, Cuenca, Granada, Madrid, Trujillo, Segovia, Sevilla and Valladolid coins. Electrochemical data permitted to detect the changes in the composition (with lowering of the silver content) and manufacturing …
Microchemical surface analysis of historic copper-based coins by the combined use of FIB-FESEM-EDX, OM, FTIR spectroscopy and solid-state electrochem…
2019
[EN] A multi-technique strategy, including microscopy, spectroscopic and electrochemical techniques, is proposed to study thin corrosion layers that form on the surface of historic copper-based coins. An accurate characterisation of this external corrosion layer is important for selecting a suitable conservation and/or restoration treatment. For this purpose, a series of copper-based coins from different historical periods and provenances, which mainly exhibited atmospheric corrosion, was analysed. The morphology of the corrosion layer and the upper core of coins was studied in trenches done on coin surfaces with a focused ion beam gun, coupled to a field emission scanning electron microsco…
Raman spectroscopy characterization of 10-cash productions from the late Chinese emperors to the Republic
2017
[EN] The use of Raman spectroscopy for discriminating monetary emissions, a recurrent problem in much archaeological studies, is described. The method involves the record of Raman signatures of tenorite and crystalline and defective cuprite in the patina based on the idea that subtle, mint-characteristic variations in the composition and metallography of the base metal during the manufacturing process are reflected in the variation in depth of the composition and crystallinity of the corrosion patina. The technique was applied to a series of 10-cash copper coins produced around the transition between the Kuang Hsu and Hsuan Tung last Chinese emperors and the first Republic whose averaged co…
Archaeometric analysis of Roman bronze coins from the Magna Mater temple using solid-state voltammetry and electrochemical impedance spectroscopy
2017
Voltammetry of microparticles (VMP) and electrochemical impedance spectroscopy (EIS) techniques, complemented by SEM-EDX and Raman spectroscopy, were applied to a set of 15 Roman bronze coins and one Tessera from the temple of Magna Mater (Rome, Italy). The archaeological site, dated back between the second half and the end of the 4th century A.D., presented a complicated stratigraphic context. Characteristic voltammetric patterns for cuprite and tenorite for sub-microsamples of the corrosion layers of the coins deposited onto graphite electrodes in contact with 0.10 M HClO4 aqueous solution yielded a grouping of the coins into three main groups. This grouping was confirmed and refined usin…
Electrochemical discrimination of mints: The last Chinese emperors Kuang Hsü and Hsüan T'ung monetary unification.
2017
[EN] An electrochemical methodology for discriminating monetary emissions, a recurrent problem in much archaeological studies, is introduced. The method is based on the record of voltammetric signatures of cuprite and tenorite corrosion products in the patina using a minimally invasive nanosampling following the voltammetry of immobilized particles methodology. A model for the depth variation of voltammetric electrochemical parameters characterizing the composition of the corrosion patinas is presented. This model permits to rationalize electrochemical data and discriminate different monetary emissions. The application of this technique, corroborated by electrochemical impedance spectroscop…