Layer formation on silicon steel by processing in H2/H2O at elevated temperatures
1992
Silicon steel (Fe-3wt%Si), as used for transformers and generators, has been annealed in wet hydrogen at elevated temperatures. The composition, sequence, and thicknesses of the layers found by conversion electron Mossbauer spectroscopy (CEMS) and Auger electron spectroscopy (AES) depth profiling for a 10 minutes anneal in different atmospheres are reported. In the range from 500°C to 720°C we observed carbide formation, indicating that the decarburization is hindered. Above 800°C, the layers consist of fayalite or of fayalite and iron oxides, depending on the oxygen potentialaO. At 843°C, the onset of iron oxide formation was found ataO=0.33.
AES and CEMS analysis of the formation of layers on Si steel under thermal treatment in a flux of H2/water vapour
1991
The near surface diffusion and reaction processes in iron-silicon steel (3.1 wt.%Si) during 10 min decarburization in water vapour/hydrogen have been studied. The decarburization temperature has been varied between 506 and 714°C for the fixed partial pressure ratio pH2O/pH2=0.017. An outer layer of SiO2 forms on the surface with its thickness increasing with temperature. From 600°C upwards, the decarburization process is hindered and a cementite layer is formed below the SiO2 layer. The formation of fayalite at the surface has been studied at a fixed decarburization temperature with pH2O/pH2 ranging from 0.017 to 0.49. The scale thickness reduces abruptly just before the ratio pH2O/pH2 nece…