Luting of ceramic crowns with a self-adhesive cement: Effect of contamination on marginal adaptation and fracture strength
2012
Objectives: This study evaluated the percentages of continuous margins (%CM) and fracture strength (FS) of crowns made out from blocs of leucite-reinforced ceramic (IPS Empress CAD) and luted with a representative self-adhesive cement (RelyX Unicem) under four contaminating agents: saliva, water, blood, a haemostatic solution containing aluminium chloride (pH= 0.8) and a control group with no contamination. Study Design: %CM at both tooth-cement (TC) and cement-crown (CC) interfaces were determined before and after a fatigue test consisting of 600’000 chewing loads and 1’500 temperature cycles changing from 5º C to 50º C. Load to fracture was recorded on fatigued specimens. Kruskal-Wallis t…
Fracture resistance after implantoplasty in three implant-abutment connection designs
2020
Background To assess the effect of implantoplasty and implant-abutment design on the fracture resistance and macroscopic morphology of narrow-diameter (3.5 mm) dental implants. Material and Methods Screw-shaped titanium dental implants (n = 48) were studied in vitro. Three groups (n = 16) were established, based on implant-abutment connection type: external hexagon, internal hexagon and conical. Eight implants from each group were subjected to an implantoplasty procedure; the remaining 8 implants served as controls. Implant wall thickness was recorded. All samples were subjected to a static strength test. Results The mean wall thickness reductions varied between 106.46 and 153.75 µm. The me…
Load-deflection characteristics of superelastic and thermal nickel-titanium wires
2011
SUMMARY The aim of this study was to investigate the mechanical properties of superelastic and thermal nickel–titanium (NiTi) archwires for correct selection of orthodontic wires. Seven different NiTi wires of two different sizes (0.014 and 0.016 inches), commonly used during the alignment phase, were tested. A three-point bending test was carried out to evaluate the load–deflection characteristics. The archwires were subjected to bending at a constant temperature of 37°C and deflections of 2 and 4 mm. Analysis of variance showed that thermal NiTi wires exerted significantly lower working forces than superelastic wires of the same size in all experimental tests (P < 0.05). Wire size had a s…
The influence of platform switching on the biomechanical aspects of the implant-abutment system. A three dimensional finite element study
2011
Objective: To evaluate the biomechanical scenario of platform switching geometric implant-abutment configuration relative to standard configurations by means of finite element analysis.Study Design: A 3D Finite Element Analysis (FEA) was performed on 3 different implant-abutment configurations: a 3.8 mm implant with a matching diameter abutment (Standard Control Design, SCD), a 5.5 mm implant with matching diameter abutment (Wider Control Design, WCD), and a 5.5mm implant with a 3.8 mm abutment (Experimental Design, ED). All the different experimental groups were discretized to over 60000 elements and 100000 nodes, and 130N vertical (axial) and 90N horizontal loads were applied on the coron…
Measurement of gap between abutment and fixture in dental conical connection implants. A focused ion beam SEM observation
2020
Background The aim of the authors was to examine the abutment-fixture interface in Morse-type conical implants in order to verify gaps at this level using a new microscopical approach. Material and Methods In this in vitro study, 20 abutment-fixture complexes were prepared by sectioning (longitudinal and cross-sectional to the long axis) with a microtome and then with a focused ion beam (FIB). This is a micrometric machine tool that uses gallium ions to abrade circumscribed areas to dig deeper into the cuts obtained with the microtome in order to eliminate cut-induced artifacts. This is because the FIB abrasion is practically free from artifacts, which are normally generated by the action o…
Influence of material and diameter of pre-fabricated posts on maxillary central incisors restored with crown.
2009
Summary Numerous research works have studied the effect of post-design parameters on the mechanical behaviour of restored teeth without reaching any clear conclusions. Previous works by the authors ascertained the effect of material and post-dimensions for non-crowned restored teeth. The aim of this work was to study the effect of post-material and diameter for crowned teeth. First, an experimental fracture strength test was performed on eighteen extracted human maxillary central incisors. Teeth were decoronated, treated endodontically and restored (nine with glass fibre posts and nine with stainless steel posts). Several post-diameters were used. The final crown restoration was carried ou…
Design characteristics, primary stability and risk of fracture of orthodontic mini-implants: Pilot scan electron microscope and mechanical studies
2013
Objectives: Orthodontic mini-implants (OMIs) are increasingly used in orthodontics but can fail for various reasons. This study investigates the effects of OMI design characteristics on the mechanical properties in artificial bone. Material and Methods: Twelve self-drilling OMIs (2 small, 6 medium, 4 large) from 8 manufacturers were tested for their primary stability in simulated medium-high cancellous bone and the risk to fracture in high-density methacrylate blocks. For the assessments of the maximum insertion torque (IT) and torsional fracture (TF) 5 of each OMI were used and for the pull-out strength (POS) 10. The OMIs were inserted with a torque screwdriver (12 sec/360°) until the bott…
Primary Stability of a Hybrid Self-Tapping Implant Compared to a Cylindrical Non-Self-Tapping Implant with Respect to Drilling Protocols in an Ex Viv…
2011
Background: Modifications of implant design have been intending to improve primary stability. However, little is known about investigation of a hybrid self-tapping implant on primary stability. Purposes: The aims of this study were to evaluate the primary stability of two hybrid self-tapping implants compared to one cylindrical non-self-tapping implant, and to elucidate the relevance of drilling protocols on primary stability in an ex vivo model. Materials and Methods: Two types of hybrid self-tapping implants (Straumann® Bone Level implant [BL], Straumann® Tapered Effect implant [TE]) and one type of cylindrical non-self-tapping implant (Straumann® Standard Plus implant [SP]) were investig…
Molar distalization with pendulum appliances in the mixed dentition: effects on the position of unerupted canines and premolars.
2004
Introduction: The pendulum appliance allows for rapid molar distalization without the need for patient compliance. Its efficiency has been confirmed in a number of clinical studies. However, the potential interactions and positional changes between the deciduous molars used for dental anchorage and the erupted and unerupted permanent teeth have yet to be clarified when this appliance is used for molar distalization in the mixed dentition. Methods: Twenty-nine patients in the mixed dentition each received a modified pendulum appliance with a distal screw and a preactivated pendulum spring for bilateral distalization of the maxillary molars. The patients were divided into 4 groups based on de…