Improvement of the mechanical properties of photo-oxidized films after recycling
2002
Mechanical recycling of post-consumer plastics gives rise, in most cases, to secondary materials with mechanical properties worse than those of the reclaimed polymer. This is mostly due to the thermomechanical treatment undergone during the melt reprocessing operations. In this work, low density polyethylene films have been photo-oxidized in artificial accelerated ageing conditions and then the brittle films have been melt reprocessed. It is shown that the secondary material, after reprocessing, shows mechanical properties, in particular elongation at break, better than those of the photo-oxidized films. This behaviour has been attributed to the fact that the melt reprocessing has the effec…
Analysis of the intensities of the longitudinal acoustic vibrations inn-alkanes and polyethylene
1980
Simple theoretical considerations indicate, that the integral intensity of the „longitudinal acoustic modes” (LAM) in the Raman spectrum ofn-alkanes should be independent of the chain length. The experiment in fact confirms this expectation. Using this property it becomes possible for polyethylene samples, to derive from the measured LAM-intensity the mass fraction of all-turns sequences contributing to this band. For solution crystallized samples this fraction coincides with the crystallinity, whereas in melt crystallized samples it generally turns out as smaller. The observed difference is likely to be due to the occurrence of local conformational defects (kinks, chain torsions) which int…
Durability of a strach-based biodegradable polymer
2007
Abstract The photo-oxidation and the photo-stabilization of a commercial biodegradable polymer have been investigated in order to establish the possibility of using this polymer as raw material for films for agriculture. The degradation has been followed by measuring the mechanical properties as a function of photo-oxidation time and in particular by following the elongation at break. The virgin polymer, made from maize starch and a synthetic biodegradable polyester, shows poor resistance to the UV irradiation as observed by the fast decay of the elongation at break, but the presence of small amounts of conventional UV stabilizers strongly improves the durability of this polymer. The UV sta…
Isobornyl Methacrylate as a Reactive Solvent of Polyethylene
2004
Solutions containing 15 wt, -% of a low-molar-mass polyethylene (PE) in isobornyl methacrylate (IBoMA), containing 0, 5 or 10 wt.-% of 1,4 butanediol dimethacrylate (BDDMA) as crosslinker, were polymerized using either benzoyl peroxide (BPO), at 80°C, or dicumyl peroxide (DCPO), with a thermal cycle attaining 150°C, as initiators. Phase separation of an amorphous PE-rich phase took place when carrying out the reaction at temperatures higher than the PE melting temperature. Partial crystallization of PE was observed when cooling to room temperature. Depending on the initial amount of BDDMA, the fraction of PE that was phase separated varied between 57 and 66% of the initial amount, with crys…
Prediction of the flow curves of thermoplastic polymer/clay systems from torque data
2014
Abstract The aim of this work was to determine some relevant rheological parameters of polymer/clay systems using mixing torque and mixing speed data obtained during processing in an internal mixer. The method used was originally proposed by Marquez et al. for monophase polymers, and is here applied to polymer/clay systems for the first time. Several clay-containing composites based on different polymer matrices (i.e., LDPE, HDPE, PA6, EVA) were used to verify the effectiveness of the method for measuring the flow curves of these polymer/clay systems. The results indicated that, for all the systems at low clay level, the rheological curves calculated with the Marquez method fit quite well t…
Polymer mechanical recycling: downcycling or upcycling?
2004
Recycled plastics are considered as materials with physical, mechanical and aesthetic properties worse than the virgin ones. In fact, this is true because degradation during lifetime and during the recycling operations changes the structure and the morphology of the polymers and then the final properties of the secondary material. Several “strategies” are under investigation, and in some cases also applied, in order to avoid further degradation during recycling and, if possible, to repair the macromolecules broken during lifetime and then to restore or to improve the initial properties. In this paper the more important techniques, already used in industry or under investigation, according …
Mechanical properties of recycled polyethylene ecocomposites filled with natural organic fillers
2006
The use of natural organic fillers in addition to postconsumer recycled polymers is getting a growing interest during the last years; this is due to many advantages they can provide in terms of cost, aesthetic properties, environmental impact. In this work, several types of wood flour (differing each other with regard to production source and particle size) were added to a recycled polyethylene coming from films for greenhouses and the effects of filler type, content, and size were investigated. Investigation was then focused on the improvement of mechanical properties, through the addition of polar copolymers (ethylene-co-acrylic acid, ethylene-vinyl acetate) and a maleic anhydride-grafted…
Relationship between structure of drawn polymers and molecular motion
1971
In order to study the relationship between structure and molecular motion, drawn polymers are more suitable than isotropic samples since their morphology can be characterized more easily by quantitative methods such as small angle X-ray scattering (SAXS) and electron microscopy (EM). The effects of changes in morphological structure on molecular motion are demonstrated by comparing the results of the SAXS and EM measurements with the dynamic mechanical behavior of drawn polyethylene. In addition the NMR broad line spectra of these samples were analyzed and the influence of annealing conditions and external stress was investigated.
Stimuli-Responsive Y-Shaped Polymer Brushes Based on Junction-Point-Reactive Block Copolymers
2012
Reversibly responsive, thin or ultrathin polymer fi lms, often referred to as “smart surfaces”, can alter their properties upon application of external stimuli. [ 1 , 2 ] One particular application fi eld represents the engineering of nanostructured fi lms mimicking cell membranes. [ 3 , 4 ] Such materials offer application potential for sensors, textiles, construction materials, and smart coatings due to a rapid change in surface energy and morphology. [ 5–7 ] The surface response can be triggered by various external stimuli such as light, temperature, electrical potential, mechanical force, magnetic fi eld, pH change, or selective solvent treatment. [ 1 , 8–12 ] A variety of different thi…
The influence of mechanical damaging on the lifetime of positrons In ultrahigh-molecular polyethylene
2013
We study the influence of damaging of ultrahigh-molecular polyethylene [(PE-UHMW) Chirulen®1120] applied, among other materials, in the production of hip endoprostheses on the spectra of positrons lifetime in this material. Polyethylene samples were damaged by the impacts, rolling friction, and collisions with metal balls in a planetary mill. The changes in the parameters of the spectra of positrons lifetime related to the annihilation of orthopositronium (o-Ps) were analyzed depending on the mechanical energy transferred to the sample. On the basis of the Eldrup–Tao model, the changes in the radii of voids in which positroniums are formed and annihilated and the changes in the degree of fi…