The time-resolved luminescence characteristics of Ce and Ce/Pr doped YAG ceramics obtained by high pressure technique
2012
Abstract Transparent Ce and Ce/Pr doped YAG ceramics were prepared under high pressures (up to 8 GPa) and relative low temperature (450 °C). Grain size of the ceramics is less than 50 nm. However unknown defects or disorders strains on grain boundaries caused the additional absorption in these ceramics. The luminescence intensity, spectra and the decay time dependence on pressure applied during ceramic preparation were studied. Concentration of some intrinsic point defect was reduced under the high pressure applied for sintering process. It is shown that formation time of the excited state of Ce luminescence depends on the pressure applied during ceramic sintering.
Structure, nanohardness and photoluminescence of ZnO ceramics based on nanopowders
2015
ZnO ceramics obtained from grained powders with different grain size by hot pressing and ceramics from tetrapods nanopowders obtained by press-less sintering have been investigated under identical conditions. Ceramics obtained by hot pressing were optically transparent but were composed of large inhomogeneous grains (d = 8–35 μm) exhibiting a substructure. Decreased values of elastic modulus within a grain and a wide defect-associated ('green') photoluminescence (PL) band at 2.2–2.8 eV in conjunction with a weak excitonic band indicate a high concentration of residual point defects in hot pressed ZnO ceramics. Utilization of more small-grained powders contributes to the formation of more un…
Photoluminescence and photocatalytic activity of zinc tungstate powders
2011
Abstract ZnWO4 powders with grain size in range 20 nm–10 µm have been synthesized by a simple combustion method and subsequent calcinations. The photocatalytic activities of powders were tested by degradation of methylene blue solution under UV light. The luminescence spectra and luminescence decay kinetics were studied and luminescence decay time dependence on average powder-grain size was obtained. The correlation between self-trapped exciton luminescence decay time and photocatalytic activity of ZnWO4 powders was shown. A model explaining the excitonic luminescence decay time correlation with photocatalytic activity was proposed.
Universal Dynamic Fragmentation inDDimensions
2004
A generic model is introduced for brittle fragmentation in $D$ dimensions, and this model is shown to lead to a fragment-size distribution with two distinct components. In the small fragment-size limit a scale-invariant size distribution results from a crack branching-merging process. At larger sizes the distribution becomes exponential as a result of a Poisson process, which introduces a large-scale cutoff. Numerical simulations are used to demonstrate the validity of the distribution for $D=2$. Data from laboratory-scale experiments and large-scale quarry blastings of granitic gneiss confirm its validity for $D=3$. In the experiments the nonzero grain size of rock causes deviation from th…
The impact of grain size on the efficiency of embedded SIMD image processing architectures
2004
Pixel-per-processing element (PPE) ratio-the amount of image data directly mapped to each processing element-has a significant impact on the area and energy efficiency of embedded SIMD architectures for image processing applications. This paper quantitatively evaluates the impact of PPE ratio on system performance and efficiency for focal-plane SIMD image processing architectures by comparing throughput, area efficiency, and energy efficiency for a range of common application kernels using architectural and workload simulation. While the impact of grain size is affected by the mix of executed instructions within an application program, the most efficient PPE ratio often does not occur at PE…
Stabilization of polar solid oxide surfaces: competition between adsorption and reconstruction
2002
Multi-cationic spinel compounds are solids that exhibit polar faces. X-ray Photoelectron spectroscopy revealed the main phenomena allowing the stabilization of these faces, carried out as a function of the material treatment, particularly the cooling rate after thermal treatment at a high temperature (1200°C). This study showed that, whatever the cooling rate, each sample is subject to a significant hydroxylation that reduces the polarity. Nevertheless, it appears that the hydroxyl group content at the surface is a strong function of the cooling rate. Indeed, whereas quenched materials are subject to high levels of hydroxylation, slowly cooled samples are sparingly hydroxylated. This phenom…
The Impact of Grain Size Composition and Organic Matter Content on Magnetic Susceptibility of Anthropogenically Transformed Bottom Sediments, as Exem…
2017
The article presents the results of an analysis of the surface layer of bottom sediments in the naval harbour in Hel. During field work conducted in June 2013, 54 sediment samples were collected. The aim of the study was to examine magnetic susceptibility of harbour sediment as a parameter determining the degree of anthropopressure. As part of laboratory tests, grain size analysis was performed in order to determine organic matter content and magnetic susceptibility of the sediment. The study also measured the impact of environmental factors on fluctuations in the other studied parameters. The results demonstrate increased dynamics of sedimentary environment in the open part of the naval ha…
Influence of thermal tempering processes on color characteristics of different monolithic computer-assisted design and computer-assisted manufacturin…
2019
Background The optical properties of dental restoration were influenced by the sintering parameters. This study investigated the effects of different tempering processes on optical properties of three monolithic Cad-Cam ceramics. Material and Methods 135 monolithic material bars (4 mm width, 14 mm length, 1.2 mm thickness) were prepared from yttria-stabilized tetragonal zirconia polycrystalline (inCoris TZI, I), zirconia-reinforced lithium silicate (Vita Suprinity, V), and lithium disilicate glass (e.max CAD, E) ceramics, with different tempering processes through slow (S), normal (N), and fast (F) cooling (n=15). The color appearance (∆EW), translucency parameter (TP), contrast ratio (CR),…
Role of sintered temperature and sintering time on spectral translucence of nano-crystal monolithic zirconia
2018
Background Sintering process is accountable for aesthetic appearance of zirconia restoration. This study appraised the effect of different sintering procedure via sintered temperatures and sintering times on spectral translucence of monolithic zirconia. Material and Methods One hundred and thirty five monolithic zirconia specimens (width, length, thickness = 10, 20, 1.5 mm) were prepared from yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP, Ceramill®) and unintentionally divided into nine groups to be sintered at different temperatures [decreasing- (SD, 1350°C), regular- (SR, 1450°C), and increasing- (SI, 1550°C) sintering temperature] and different sintering times [shortening…
Luminescence properties of Tb3+:Y3Al5O12 nanocrystallites prepared by the sol–gel method
2004
Tb 3+ :YAG nanocrystalline powders have been prepared by the sol-gel route. Structure and morphology of the obtained materials have been studied. The average grain sizes have been determined by X-ray powder diffraction measurements. Photo- and cathodoluminescence spectra of the Tb 3+ :Y 3 Al 5 O 12 powders have been measured. It has been found that the samples at low concentration demonstrate emission ascribable to the 5 D 3 →F J and 5 D 4 → 7 F J transitions. In particular, the concentration dependence of the luminescence spectra and lifetimes have been investigated as a function of the YAG grains sizes. It has been shown that the cross-relaxation responsible for the quenching of the 5 D 3…