The role of radiolysis products in in situ luminescence of Li2O
1998
Abstract A new phenomenon of an “excess luminescence” (EL) in Li 2 O observed at 4.5–2.5 eV under light ion (H + , He + ) irradiation during the rise of temperature (>573 K ) was studied. The essence of the EL is in the rapid pulse increase of the luminescence intensity. It is proposed that this phenomenon is based on the thermo-dissociation of colloidal Li into Li lattice ions, F + and F 0 centers, and oxygen vacancies. Formed oxygen vacancies capture electrons during the irradiation and form excited F-centers, whose relaxation gives the EL. This phenomenon was reproduced using X-ray irradiation and a sample containing colloidal Li introduced by irradiation with electron accelerator to an …
Tritium localisation and release from the ceramic pebbles of breeder
2004
Magnetic field (MF) effects on the radiolysis and tritium release from Li4SiO4 (FZK) and Li2TiO3 (CEA) ceramic pebbles were investigated. The tritium chemical forms in Li4SiO4 were estimated by means of lyomethods. In the case of the neutron fluence Fn 6 10 18 nm � 2 , the tritium is mostly in the T þ form, but in the case of Fn � 10 25 nm � 2 , the T þ form accounts for 86–95% of the tritium. A high subsurface concentration of tritium is characteristic of a separate pebble and correlates with the distribution of radiation-induced defects. The MF increases the radiolysis of Li4SiO4 by 20–25%. Irradiation with electrons to 1000 MGy at 1200 K increases the grain size by 5–10%, decreasing the …
LiF crystals irradiated with 150MeV Kr ions: Peculiarities of color center creation and thermal annealing
2013
Abstract Color centers in LiF crystals are studied under irradiation at room temperature with 150 MeV Kr ions in the fluence (Φ) range of 1010–1014 ions/cm2 with a beam current density of 10, 50, and 100 nA/cm2, corresponding to flux of 4.46 × 109, 2.23 × 1010 and 4.46 × 1010 ions/(cm2 × s), respectively. At Φ ⩾ 3 × 1012 ions/cm2 besides F and Fn centers also charged F 3 + centers are created. Thermal annealing of irradiated LiF crystals with Φ ⩾ 1013 ions/cm2 at 400 K leads to a decrease of F centers (due to annihilation with H centers) and an enhancement of complex Fn color centers (neutral and charged) due to interaction with thermally activated anion vacancies. Annealing LiF crystals at…
Radiation displacement defect formation in some complex oxide crystals
2000
The work is devoted to an analysis of the formation processes of radiation displacement defects (RDDs) and color centers (CCs) under irradiation of complex oxide crystals. The results of the displacement process simulation as well as the analysis of the RDDs and CCs accumulation kinetics in some complex oxide crystals are presented. New experimental results on additional absorption spectra induced by neutron irradiation of LiNbO3 (LNO) crystals doped with Fe and Cr and YAlO3 (YAP) crystals doped with Nd and Er as well are presented. Dose dependencies are compared and their peculiarities are discussed. ” 2000 Elsevier Science B.V. All rights reserved.
Color centers and nanodefects in LiF crystals irradiated with 150MeV Kr ions
2012
Abstract The modifications of structure, optical and nano-mechanical properties of LiF crystals after irradiation with 150-MeV Kr +14 ions at a fluence of 6 × 10 12 ions cm −2 have been studied using optical absorption spectroscopy, scanning electron and atomic force microscopy, and nanoindentation. Optical spectroscopy shows the saturation of F centers and a comparatively high number of F n centers. AFM and SEM imaging reveals a nanostructured region with columnar nanocrystallites (size 30–90 nm). Nanostructuring occurs in depths up to 10 μm, where the ion energy loss surpasses a critical threshold of about 10 keV/nm. At a lower energy loss a zone enriched with dislocations is observed. S…
Investigation of heavy ion tracks in LiF crystals by dislocation mobility method
2008
Abstract The track damage created in LiF by swift heavy ions was studied using methods of dislocation mobility and track etching. The crystals were irradiated with Bi and Pb ions of a specific energy of 11 MeV/u at fluences between 10 7 and 10 10 cm −2 . The measurements on cross-sections cleaved parallel to the irradiated surface showed continuity of the track etching for the depth up to 70% of the ion range. In deeper layers, numerous etch pits had a flat-bottomed shape indicating the discontinuities of the track structure. At this stage, a decrease of the ion-induced effect in dislocation mobility was observed. The observed reduction of the efficiency of ion tracks as obstacles for disl…
Nanostructuring and strengthening of LiF crystals by swift heavy ions: AFM, XRD and nanoindentation study
2012
Abstract Modifications of the structure and micromechanical properties of LiF crystals under high-fluence irradiation (10 11 –10 13 ions cm −2 ) with swift C, Ti, Au and U ions of the specific energy of 11.1 MeV/u have been studied. In the case of heavy ions (U, Au), the AFM and SEM results reveal the bulk nanostructure consisting of columnar grains with nano-scale dimensions (50–100 nm). For lighter C ions the structure enriched with prismatic dislocation loops has been observed. High-resolution XRD reciprocal space maps for nano-structured LiF expose a mosaic-type structure with low-angle boundaries between grains.
Void superlattice formation in electron irradiated CaF2: Theoretical analysis
2010
Abstract CaF2 is widely adopted as deep-UV window material and thin film optical coating. The void superlattice was observed experimentally under electron irradiation at room temperature. We performed kinetic Monte Carlo (kMC) simulations of the initial stages of the process when short- and intermediate-range order of defects in small Ca colloids and larger interstitial aggregates (F2 gas voids) is created. The kMC model includes fluorine interstitial–vacancy pair creation, defect diffusion, similar defect attraction and dissimilar defect recombination. Special attention is paid to the statistical analysis of the defect aggregate distribution functions under different conditions (dose rate,…
Thermal annealing and transformation of dimer F centers in neutron-irradiated Al2O3 single crystals
2020
This work has been carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom research and training programme 2014-2018 and 2019-2020 under grant agreement No 633053. The views and opinions expressed herein do not necessarily reflect those of the European Commission. In addition, the research leading to these results has received funding from the Estonian Research Council grant (PUT PRG619).
EPR/alanine dosimetry for two therapeutic proton beams
2016
Abstract In this work the analysis of the electron paramagnetic resonance (EPR) response of alanine pellets exposed to two different clinical proton beams employed for radiotherapy is performed. One beam is characterized by a passive delivery technique and is dedicated to the eyes treatment (OPTIS2 beam line). Alanine pellets were irradiated with a 70 MeV proton beam corresponding to 35 mm range in eye tissue. We investigated how collimators with different sizes and shape used to conform the dose to the planned target volume influence the delivered dose. For this purpose we performed measurements with varying the collimator size (Output Factor) and the results were compared with those obtai…