Estimation of interfacial fracture toughness based on progressive edge delamination of a thin transparent coating on a polymer substrate
2010
Evaluation of interfacial toughness of sub-micron-thickness layers deposited on a ductile substrate is a challenging task which has motivated different experimental approaches Fragmentation testing was used in the present study as a means of interface characterization of a silicon-nitride-coated polyimide substrate. During the test, after an initial rapid segmentation-cracking phase, the coating fragments developed edge delaminations which propagated in a stable manner with further increase in the applied strain The debonding process was modelled by the finite element method Incorporating a cohesive zone at the front of the interfacial crack The edge cracks were found to be dominated by mod…
Effects of fiber orientation of adjacent plies on the mode I crack propagation in a carbon-epoxy laminates
2011
Abstract The influence of ply orientation on the resistance to mode I delamination of multidirectional composite laminates can be assessed by Double Cantilever Beam (DCB) tests. However, one of the difficulties associated with such a study is the change in overall elastic parameters occurring when modifying local ply orientations. The present work uses laminates with special stacking sequences allowing for isolating the orientation parameter. Multidirectional DCB specimens were designed so as to obtain an uncoupled quasi isotropic and quasi-homogeneous elastic behavior, with the same properties for the entire laminate and the two sub laminates separated by the pre crack at mid-plane. The re…
Environmental and depositional controls on laminated freshwater carbonates: An example from the Roman aqueduct of Patara, Turkey
2013
Carbonate deposits in aqueducts are a new high-resolution data source for environmental changes during the time of the Roman Empire, notably in the fields of palaeoclimate and spring hydrology. In order to distinguish environmental effects from those related to depositional setting, laminated carbonate deposits were compared along the entire length of an ancient aqueduct channel at Patara, Turkey. The carbonate deposits, up to 80mm in thickness, are composed of lamina couplets up to 1mm thick of alternating porous microspar and dense, columnar sparite. The former formed in the dry, warm season and the latter in the wet, cool season. The presence of biofilms seems to play a role in the devel…
Micromechanisms of load transfer in a unidirectional carbon fibre-reinforced epoxy composite due to fibre failures: Part 3. Multiscale reconstruction…
2008
International audience; This third article describes a multiscale process which takes into account the most important microscopic phenomena associated with composite degradation, including fibre fractures and interfacial debonding, overloading of fibres neighbouring a fibre break as well as viscoelastic behaviour of the matrix. The results have been used to accurately predict the macroscopic failure of unidirectional carbon fibre-reinforced epoxy and quantify damage accumulation in pressure vessels made of the same material. The approach described has allowed the acoustic emission activity resulting from fibres breaks to be evaluated and shown how the residual lifetimes of such vessels, whe…
A comparative evaluation of shear bond strength between feldspathic porcelain and lithium di silicate ceramic layered to a zirconia core? An in vitro…
2020
Background The bond strength between the zirconia core and ceramic veneer is the weakest component in the layered structure. Delamination of veneering ceramic is reported as one of the most frequent problems associated with Veneered Zirconia restorations. The aim of this study is to compare the shear bond strength of lithium di silicate porcelain to that of feldspathic porcelain on a zirconia Substrate. Material and Methods Two groups (group A and B) of zirconia blocks with each group having 20 samples were fabricated according to Schmitz Schulmeyer method. Group A (n =20 ) samples were veneered with feldspathic veneering porcelain and Group B (n=20) samples were veneered with heat pressed …
R-Curve Modelling of Mode I Delamination in Multidirectional Carbon/Epoxy Composite Laminates
2014
In the present work, the mode I delamination behaviour of a quasi-isotropic quasi-homogeneous carbon/epoxy composite laminate with adjacent plies of 0o//45o is studied numerically. To describe the R-curve behaviour observed during crack propagation, a linear-exponential traction-separation law is proposed, where the fracture toughness and the increment in the fracture energy could be considered separately in the model. This model is then implemented in the finite element simulation of the delamination process in the composite laminate. Numerical results indicate that with the incorporation of the fibre bridging effect leads to a well-predicted force-displacement response of the composite la…
Application of cohesive-zone models to delamination behaviour of composite material
2012
International audience; The parameters of cohesive elements have to be chosen correctly in the simulation of composite delamination by finite element method: such as interface strength, interface stiffness and shape of cohesive law. The purpose of this work is to investigate their influence on the accuracy of the results obtained. A three-dimensional cohesive-zone model has been established using Ls-dyna to simulate Double-Cantilever-Beam mode I (DCB) and Edge-Notched-Flexure mode II (ENF) tests. The influence of these parameters of cohesive element on the maximum load and the slope of load-displacement curve have been discussed by comparing experimental and numerical results. Four traction…
A thermodynamically consistent cohesive-frictional interface model for mixed mode delamination
2016
Abstract A new interface constitutive model based on damage mechanics and frictional plasticity is presented. The model is thermodynamically consistent, it is able to accurately reproduce arbitrary mixed mode debonding conditions and it is proved that the separation work is always bounded between the fracture energy in mode I and the fracture energy in mode II. Analytical results are given for proportional loading paths and for two non-proportional loading paths, confirming the correct behavior of the model for complex loading histories. Numerical and analytical solutions are compared for three classical delamination tests and frictional effects on 4ENF are also considered.
Flying Laser Spot Thermography technique for the NDE of Fibre Metal Laminates disbonds
2017
Abstract The present work investigates the features of an active Infrared-NDT Thermography technique derived from a Flying Laser Spot set-up for the analysis of interlaminar disbonds in layered structures in general and Fibre Metal Laminates in particular. The presented technique uses a laser-spot heat source, which moves at a constant speed, raster scanning the object surface. Interlaminar defects parallel to the surfaces act as barriers towards through-the-thickness heat diffusion. This produces some modifications over the surface thermal field which are well identified in the Standard Deviation calculated over a Reference Area following the heat source. The mechanisms leading to such def…
Laminations and tilings of the Hyperbolic upper half plane
2005
This thesis is devoted to the study of dynamical systems associated with tilings of theEuclidean plane or of the Hyperbolic half-plane. A such tiling codes an action of a group ofisometries (namely the group of translations of the plane or the group of affine maps) on a compactmetric space $\Omega$ such that the properties of this action are related with the combinatoricproperties of the tiling. The behaviors of the actions obtained by this way are really various. Insome cases, like for example for the Penrose's tiling, this action is free and minimal. This givesto the set $\Omega$ a structure of a specific lamination called {\it solenoid}. This space islocally the product of a Cantor set w…