The evaluation of surface sealants effect on the color stability of Nano-hybrid composite after polishing with One-Step system (in-vitro)
2018
Background The clinical use of composite resins has increased substantially over the past few years due to increased esthetic demands by patients, improvements in formulation, and simplification of bonding procedures. An alternative for preventing or reducing composite discoloration is using of composite surface sealant. The purpose of this study was to determine the effect of surface sealant on color-stability of Nano-hybrid composites after polishing with one-step system. Material and Methods 56 disk-shaped specimens (10*2 mm) of a Nano-hybrid composite resin (VOCO,Cuxhaven,Germany) were prepared. The specimens were randomly divided in to 2 groups of 28 specimens each. The surfaces of spe…
One-step electrodeposition of superhydrophobic coating on 316L stainless steel
2021
Superhydrophobic coatings were fabricated through a one-step electrochemical process onto the surface of 316L stainless steel samples. The presence of hierarchical structures at micro/nanoscale and manganese stearate into the coatings gave superhydrophobicity to the coating, with contact angle of ~160°, and self-cleaning ability. Corrosion resistance of 316L samples was also assessed also after the electrodeposition process through Electrochemical Impedance Spectra recorded in an aqueous solution mimicking seawater condition.
Boosting the Performance of One-Step Solution-Processed Perovskite Solar Cells Using a Natural Monoterpene Alcohol as a Green Solvent Additive
2021
The perovskite film is the core of a perovskite solar cell (PSC), and its quality is crucial for the performance of such devices. The morphology, crystallinity, and surface coverage of the perovskite layer greatly affect the power conversion efficiency (PCE), hysteresis, and long-term stability of PSCs. The incorporation of appropriate solvent additives in the perovskite precursor solution is an effective strategy to control the film morphology and reduce the defects and grain boundaries. However, the commonly used solvent additives are environmentally harmful and highly toxic. In this work, α-terpineol (a nontoxic, eco-friendly, and low-cost monoterpene alcohol) is employed for the first t…
One-step electrochemical synthesis and physico-chemical characterization of CdSe nanotubes
2013
Abstract Stoichiometric CdSe nanotubes (NTs) with a length of ∼700 nm have been successfully grown by one-step electrochemical technique into anodic alumina membranes. Cyclovoltammetric method has been performed using porous anodic alumina as template electrode and an electrochemical bath containing Cd 2+ ions and SeO 2 . The as-prepared NTs have been identified as face-centred-cubic CdSe by XRD, while micro-Raman analysis reveals the typical peaks of nanostructured CdSe. The stoichiometric deposition of CdSe NTs formation is suggested by EDX analysis, with an average atomic percentage of Cd:Se of ∼0.93. Photoelectrochemical measurements reveal that CdSe NTs are photoactive materials with d…
One-Step Electrodeposition of CZTS for Solar Cell Absorber Layer
2015
CZTS thin films were obtained by one-step electrochemical deposition from aqueoussolution at room temperature. Films were deposited on two different substrates, ITOon PET, and electropolished Mo. Differently from previous studies focusing exclu‐sively on the formation of kesterite (Cu4ZnSnS4), here, the synthesis of a phase withthis exact composition was not considered as the unique objective. Really, startingfrom different baths, amorphous semiconducting layers containing copper–zinc–tin–sulphur with atomic fraction Cu0.592Zn0.124Sn0.063S0.221 and Cu0.415Zn0.061Sn0.349S0.175, werepotentiostatically deposited. Due to the amorphous nature, it was not possible to de‐tect if one or more phases…
Organic-inorganic materials through first simultaneous frontal polymerization and frontal geopolymerization
2021
Abstract The first frontal geopolymerization (FGP) took place in the same reaction medium in which the frontal polymerization (FP) of 1,6-hexanediol diacrylate (HDDA) was occurring, thus giving rise to an organic-inorganic hybrid in one step in just a few minutes. Because of their exothermicity, the two reactions support each other and sustain propagating fronts. By contrast, using the classical techniques (prolonged heating) instead of FP, due to large gas formation, the reaction is explosive or, if carried out at room temperature, phase separation occurred.
Rapid One-Step Fabrication of Graphene Oxide-Decorated Polycaprolactone Three-Dimensional Templates for Water Treatment
2020
Coating of flexible substrates is crucial to prepare versatile, multifunctional materials. However, exploration of effective fabrication approaches is still a challenging issue, because the pathways generally proposed require time-consuming, multistep protocols. Here, we developed a one-pot process for decorating either pearl necklace-like or fibrous fluffy-like structures of polycaprolactone (PCL) with graphene oxide (GO) skin. PCL solutions were dry jet-wet electrosprayed or electrospun into a stirred liquid collector constituted by ethanol-containing GO nanoparticles. The stirred liquid collector enables the formation of 3D-structures, whose microarchitecture can be designed by controlli…
Solution precursor plasma spray process as an alternative rapid one-step route for the development of hierarchical ZnO films for improved photocataly…
2018
Abstract The development of efficient photocatalytic hierarchical coral-like ZnO films via a relatively simple, efficient, rapid and single-step process is essential for industrial development. Herein, we report a novel method for directly synthesizing well-shaped ZnO nanorods (NRs) by Solution Precursor Plasma Spray (SPPS) process rather than conventional spherical/ellipsoidal particles. In the prepared ZnO-NRs films, the ZnO NRs display an average diameter of 190 nm, and exhibit a preferential orientation growth along (002) plane compared to a reference ZnO films (called ZnO-P) containing spherical/ellipsoidal particles. ZnO-NRs films exhibit relative narrower bandgap (3.02 eV) probably d…
One-Step Synthesis and Consolidation of Nanophase Iron Aluminide
2001
The simultaneous synthesis and densification of nanophase iron aluminide is investigated. Elemental nanophase reactants produced by mechanical activation were reacted by field activation with the simultaneous application of uniaxial pressure. The process was demonstrated in this work by the synthesis of dense nanometric FeAl. Iron and aluminum powders were co-milled in a specially designed planetary mill to obtain nanometric reactants and to avoid formation of any product phases. These powders were then subjected to high AC currents (1250–1500 A) and pressures in the range of 70–106 MPa. Under these conditions, a reaction was initiated and completed within a short period of time (2.5–3.5 mi…
Characteristics of LiFePO4 obtained through a one step continuous hydrothermal synthesis process working in supercritical water
2009
International audience; The olivine-like material LiFePO4 was prepared via a continuous hydrothermal synthesis process working from subcritical to supercritical water conditions. The influence of some processing parameters–temperature and reaction time–was investigated in terms of material purity, grain size and morphology. Supercritical conditions were found to be attractive to synthesize in one step a well-crystallized material without impurities. The primary particles size was in the nanometric range. They showed a natural tendency to form micron size agglomerates, which were supposed to be the cause of the limited capacity, as demonstrated through a cross study using laser particle size…