Polyethylene glycol/clay nanotubes composites
2012
Nanocomposites of poly(ethylene) glycol (PEG) 20000 filled with clay nanotubes (HNTs) were prepared. The thermal properties obtained from thermogravimetry and differential scanning calorimetry were correlated to the morphology imaged by scanning electron microscopy. Low amounts of HNTs generate compact structure while large amounts of HNTs create craters and voids. The decrease of polymer degradation temperature in the presence of large amount of nanoclay (ca. 80 wt%) is a consequence of the morphology at the mesoscale range. The thermal opposite effect observed in the HNTs low regime (up to ca. 20 wt%) is due to the gas entrapment into the nanoparticles lumen. The quantitative analysis of …
Time-resolved rheology as a tool to monitor the progress of polymer degradation in the melt state - Part I: Thermal and thermo-oxidative degradation …
2015
Abstract Thermal and thermo-oxidative degradation of polyamide 11 (PA11) in the melt state (T = 215 °C) are studied by resorting to time-resolved mechanical spectroscopy. Such an approach allows to elude the changes in the rheological properties occurring while testing, thus enabling the rigorous study of polymer degradation in the melt state. Different concurrent degradation reactions in oxidative (air) and non-oxidative (N2) environment are promptly guessed by studying the time evolutions of rheological functions. In particular, changes in the zero-frequency complex viscosity reflects changes in the average molecular weight, while the appearance of a yield stress in the complex viscosity …
On new chemical reactions of polymers
1968
Three major areas of work present themselves to a chemist who is concerned with polymer materials namely: synthesis and degradation of polymers; structure analysis of natural and synthetic polymers; and chemical transformations of polymers. Although these three fields are very closely related, I wish to concern myself only with the last of them.
1987
Comparative Investigation on the Soil Burial Degradation Behaviour of Polymer Films for Agriculture before and after Photo-Oxidation
2020
Polymer films based on biodegradable polymers, polyethylene (PE) and modified PE with oxo-degradable additive were prepared by film blowing. Carbon black (1%) was added to all the films. Commercial biodegradable Ecovio®
Influence of Calcium Carbonate Nanoparticles on the Soil Burial Degradation of Polybutyleneadipate-Co-Butylenetherephthalate Films.
2022
A polybutyleneadipate-co-butylenetherephthalate (PBAT) sample, commercially known as Ecoflex®, was processed via melt extrusion with CaCO3 nanoparticles coated with a hydrophobic coating. Blown films of PBAT and two composites with nanofiller (2% and 5%wt) were prepared and degradation tests in soil at 30 °C up to 180 days were carried out with weight loss measurements. Furthermore, biodegradation test according to ISO 14851 was carried out at 30 °C. The effect of CaCO3 on soil burial degradation was assessed by surface wettability and SEM. ATR-FTIR and XPS analyses highlighted chemical modifications induced by soil degradation. CaCO3 nanoparticles decreased surface wettability …