Development of Eco-Friendly and Self-Cleaning Lime-Pozzolan Plasters for Bio-Construction and Cultural Heritage
2020
Summarization: Nowadays, the design and use of multi-functional mortars has increased significantly, with interesting applications in the green building and cultural heritage conservation sectors. A key point for a correct adoption of these innovative materials is their behavior along time and their resistance to the weathering. The objective of this project was to define the performance and durability of innovative mortars, in order to use them correctly and to avoid irreparable damage over time. For the development of this project, lime–metakaolin and hydraulic lime–metakaolin based mortars (hereinafter called A, B), as well as A and B with the addition of nano-TiO2 and perlite (hereinaft…
Effect of superplasticizers on the rheological properties of fly ash suspensions containing activators of the pozzolanic reaction
2000
Rheological studies have been carried out on the effect of a superplasticizer from the sulphonated melamine formaldehyde (SMF) group upon the properties of fly ash suspensions containing a small quantity of mineral admixtures such as cement, lime and gypsum. The superplasticizers' efficiency has appeared to depend greatly on the admixture used. The highest liquefaction degree was found in fly ash suspensions containing both cement and gypsum together and the next it was, when only cement was added. These suspensions exhibit features of a newtonian fluid of low plastic viscosity, when the water to solid ratio (w/s) is 0.3 and a superplasticizer has been used. However, fly ash suspensions wit…
Characterization of hydraulic mortars by means of simultaneous thermal analysis
2008
The properties of hydraulic mortars were studied by means of simultaneous thermal analysis (STA), according to a procedure proposed in the literature. Hydraulic limes, cement and/or slaked lime were mixed using different proportions of both inert and reactive aggregates, in order to test the effectiveness of such procedure in distinguishing the different degree of hydraulicity of such samples. The use of the normalized coordinates suggested in the literature results in overlapping of the clusters of different kinds of mortars. Modified coordinates are proposed, which give promising results in view of outlining a 'master curve' of hydraulicity.
Pumice powder as filler of self-compacting concrete
2015
Abstract An experimental study on the rheological and mechanical properties of self-compacting concrete with pumice powder used as filler additive is presented. Self-compacting concrete (SCC) shows its peculiar characteristics in the fresh state and many researches have been developed with reference to its rheological characteristics paying attention to the techniques of self-compacting properties assessment. One of the most important aspect in concrete mix-design is the type and the amount of fillers with respect to water and cement: this amount has great influence not only on self-compacting properties (fluidity, segregation, etc.), but also on the mechanical properties of the mixture. Vo…
Retention of alkali ions by hydrated low-pH cements: Mechanism and Na+/K+ selectivity
2013
Low-pH cements, also referred to as low-alkalinity cements, can be designed by replacing significant amounts of Portland cement by pozzolanic materials. Their pore solution is characterized by a pH near 11, and an alkali concentration much lower than that of Portland cement. This work investigates the retention of sodium and potassium by a hydrated low-pH cement comprising 60% Portland cement and 40% silica fume. It is shown that sorption of potassium is higher than that of sodium and mainly results from counterion charge balancing of the C-S-H negative surface charge. To explain the greater retention of potassium compared to sodium, it is postulated that potassium, unlike sodium, may enter…
Analysis of the chemical and microstructural modifications effects on the hydro-mechanical behaviour of a lime-treated clay
2019
The paper presents the results of a characterization of kinetic characteristics of pozzolanic reaction with the aim to investigate the time-dependent modification of clay properties as a consequence of mixing with lime. Results of chemical analyses are in agreement with the increase of mechanical properties and with the observed microstructure modifications up to one year of curing time. The rate of development of pozzolanic reactions seems to be almost constant while the time required for their completion is dependent on the lime content. Pozzolanic products are responsible for the time reduction of swelling strain upon saturation as well as for the increases of yielding stress, stiffness …
Physical and mechanical properties of sustainable hydraulic mortar based on marble slurry with waste glass
2021
This paper aims to propose and characterize a sustainable hydraulic mortar entirely obtained by the reuse of waste materials, with marble slurry coming from quarries in the north-western Sicily and glass powder coming from a waste collection plant in Marsala (Province of Trapani). The first was used as raw material to produce the mortar binder by a kilning and slaking process, while the second was used as a pozzolanic additive. The chemical and morphological characterization of the marble slurry was done by XRD, FTIR, STA and SEM analyses. Glass powder was analyzed through particle size distribution measurements, XRD and standard pozzolanic tests. Hydraulic mortars constituted by slaked lim…
On the hydro-mechanical behaviour of a lime-treated embankment during wetting and drying cycles
2018
Abstract The paper presents some experimental results obtained on samples extracted from a full-scale embankment obtained by compacting a lime-treated clayey soil. A comprehensive test programme was carried out in order to highlight the improvement of mechanical behaviour induced by lime treatment as well as to assess the durability of the improved material, which may be affected by severe seasonal wetting and drying cycles. Direct shear tests, triaxial compression tests, swelling potential measurement and oedometric tests were performed on samples cured in controlled environmental conditions for at least 18 months. Wetting and drying cycles were applied in a very wide range of suction valu…
Morteros hidràulicos para enlucidos: caracterizaciòn mecànica y fìsica de remedios tradicionales y productos industriales
2009
Effect of some additives on the reactions in fly ASH-Ca(OH)2system
2004
Differential thermal analysis and thermogravimetry were used to evaluate the effect of some additives, such as CaSO4, CaCl2 and silica fume amorphous silica from ferrosilicon synthesis on the mechanism and kinetics of reactions occurring in fly ash-Ca(OH)2 system. The accelerating role of these additives was demonstrated from the data relating to Ca(OH)2 consumption in hydrated pastes, determined by TG measurements.