Tuning the high-order harmonic lines of a Nd:Glass laser for soft x-ray laser seeding
2010
Taking advantage of the non-adiabatic blue-shift of high-order harmonics generated by a fixed frequency Nd:Glass laser system, we are able to report more than 50 % coverage of the XUV spectral range between 18 nm and 35 nm. The generated harmonic lines are capable of seeding Ni-like Y, Zr and Mo soft x-ray lasers and others.
Nonlinear Optical Characterization of InP@ZnS Core-Shell Colloidal Quantum Dots Using 532 nm, 10 ns Pulses
2021
InP@ZnS core-shell colloidal quantum dots (CQDs) were synthesized and characterized using the z-scan technique. The nonlinear refraction and nonlinear absorption coefficients (γ = −2 × 10−12 cm2 W−1, β = 4 × 10−8 cm W−1) of these CQDs were determined using 10 ns, 532 nm pulses. The saturable absorption (β = −1.4 × 10−9 cm W−1, Isat = 3.7 × 108 W cm−2) in the 3.5 nm CQDs dominated at small intensities of the probe pulses (I ≤ 7 × 107 W cm−2) followed by reverse saturable absorption at higher laser intensities. We report the optical limiting studies using these CQDs showing the suppression of propagated nanosecond radiation in the intensity range of 8 × 107–2 × 109 W cm−2. The role of nonline…
Nanoparticles Size Distribution Assessment During Early Synthesis Stages
2021
Nanotechnology, an innovative field of material science, designs and produces nanostructures materials with unique properties that make them suited for various bioengineering applications. The shape and the dimension are the main variables depending on the method of synthesis or chemical precursors. Silver nanoparticles obtained through chemical synthesis exhibit as strong antibacterial effect if their size lays in a well-defined range. However, a small size of such particles, in the range of nanometers to several tens of nanometers, requires specific techniques as Dynamic Light Scattering or Transmission Electron Microscopy, both being affected by certain assumptions or by the high cost an…
Raman Spectroscopy and Low-Temperature Transport Measurements of Individual Single-Walled Carbon Nanotubes with Varying Thickness
2009
We have investigated two metallic and one semiconducting individual single-walled carbon nanotubes (SWNT) and one bundle of two semiconducting nanotubes with a diameter range 1.1−2.9 nm with Raman spectroscopy and low-temperature electric transport measurements. With these two methods, we obtain mutually independent measurements on the basic properties of a specific nanotube. In particular, we obtain data on metallic and semiconducting properties. Evidence of a small band gap for one metallic tube was obtained. For the semiconducting SWNTs with diameters of 2.7−2.9 nm, a special resonance condition was observed which causes an anomalous intensity ratio for the two components of the G-band. …
Differential Cross Sections and Product Rovibrational Distributions for (16)O + (32)O2 and (18)O + (36)O2 Collisions.
2015
We report rotationally resolved opacity functions, product rotational distributions, and differential cross sections for the (16)O + (16)O(16)O (v = 0,j = 1) → (16)O(16)O (v' = 0,j') + (16)O and (18)O + (18)O(18)O (v = 0,j = 1) → (18)O(18)O (v' = 0,j') + (18)O collisions calculated by a time-independent quantum mechanical method employing one of the latest potential energy surface of ozone [ Dawes ; et al. J. Chem. Phys. 2013 , 139 , 201103 ]. The results obtained for both collisional systems in the energy range 0.001-0.2 eV are examined, and interesting mass scaling effects have been discovered. The shapes of product angular distributions suggest a transition from an indirect to a direct s…
COST 241 intercomparison of nonlinear refractive index measurements in dispersion shifted optical fibres at =1550 nm
1997
COST 241 measurements of the nonlinear refractive index, n/sub 2/, exhibit a large scatter depending on the specific measurement technique. This is largely due to the electrostrictive contribution to the Kerr nonlinearity, as is revealed by the resonant behaviour of n/sub 2/ (with peak values up to 3.9 10/sup -20/ m/sup 2/ W/sup -1/) observed with signal modulation frequencies in the 0.11 GHz range.
Sub 500 nm refractory carbonaceous particles in the polar stratosphere
2017
Abstract. Eleven particle samples collected in the polar stratosphere during SOLVE (SAGE III Ozone loss and validation experiment) from January until March 2000 were characterized in detail by high-resolution transmission and scanning electron microscopy (TEM/SEM) combined with energy-dispersive X-ray microanalysis. A total number of 4175 particles (TEM = 3845; SEM = 330) was analyzed from these samples which were collected mostly inside the polar vortex in the altitude range between 17.3 and 19.9 km. By particle volume, all samples are dominated by volatile particles (ammonium sulfates/hydrogen sulfates). By number, approximately 28–82 % of the particles are refractory carbonaceous with si…
Differential study of substituted and unsubstituted cobalt phthalocyanines for gas sensor applications
2011
Abstract The conductivity of CoPc (cobalt phthalocyanine) and Co[(SO3Na)2,3Pc] was measured under a flow of two different gases (NH3 and O3), during exposure/recovery cycles. It appears that the relative responses are linearly related to the concentration, in the 20–200 ppb range for O3 and in the 20–200 ppm range for NH3. Observed during time, the sensing parameters allow a qualitative understanding of the kinetics. The comparative study of those products under both different gases gave interesting results for sensor applications. Whereas CoPc is sensitive to both gases, its sulfonated counterpart is only sensitive to NH3.
Heat Capacity and Dielectric Properties of the PNN-PT Ferroelectric Ceramics
2012
A study of dielectric permittivity and heat capacity of the (1-х)PbNi1/3Nb2/3O3 – хPbTiO3 solid solution system (x = 0.3, 0.4, 0.5) within the 290–700 K range is reported. Temperatures of phase transitions Tm determined from maximums of dielectric permittivity ϵ depends on the content of PbTiO3. A broad phase transition is shown to proceed in the 0.7PbNi1/3Nb2/3O3–0.3PbTiO3 composition around 312 K. Specific to phase transitions anomalous heat capacity is observed at Т ≈ 520 K in all compositions studied.
Thermal properties of ferroelectric 0.7PbNi1/3Nb2/3O3–0.3PbTiO3ceramics
2013
A study of heat capacity as function of temperature of the 0.7PbNi1/3Nb2/3O3–0.3PbTiO3 solid solution within the 120–800 K range is reported. Broad anomalies on the curve of heat capacity are revealed in the 250–450 K and 450–650 K intervals peaking at 520 K and a λ-anomaly at T ≈ 225 K. Results are discussed with account for dielectric and structural data.