Pulsed laser growth and characterization of thin films on titanium substrates
2007
Abstract Colored layers were obtained by laser surface treatment of Ti substrates with a pulsed Nd:YAG Q-switched laser. The changes in the morphology, structure and chemical composition of the layers were studied by SEM, EDS, XPS, SIMS and Raman spectroscopy as a function of the laser fluence in the 4–60 J cm −2 . For laser fluences lower than 25 J cm −2 , the layers are colorless or yellow. Their surface is smooth, but they display cracks which increase when the fluence increases. The O/Ti ratio, determined by XPS analysis, varies from 0.7 (colorless layers) to 1.3 (yellow layer). Moreover, XPS spectra evidence non-negligible amounts of nitrogen and carbon in these layers. Raman spectra s…
Highly Active Photocatalytic TiO2 Powders Obtained by Thermohydrolysis of TiCl4 in Water
2009
Highly active photocatalytic TiO2 samples were synthesized by thermohydrolysis of TiCl4 in water at 100 °C. Rutile, binary mixtures of anatase and rutile or anatase and brookite or ternary mixtures of anatase, brookite, and rutile were obtained depending on the TiCl4/H2O ratio. Rietveld refinements were employed to evaluate the crystalline phases and composition of the mixtures. The effect of the aging time on the phase composition was also studied. The band gap values of the samples were obtained by the diffuse reflectance spectra. The position of the flat band potentials of anatase, brookite, and rutile was determined measuring the photovoltage as a function of the suspension pH. From the…
Optical and Acoustic Vibrations Confined in Anatase TiO2 Nanoparticles under High-Pressure
2014
International audience; The effect of an applied high pressure on the optical and acoustic vibrations of small anatase TiO2 nanoparticles is studied using Raman scattering. All the Raman peaks show a significant variation of their frequency with pressure, except for the low-frequency peak which is due to acoustic vibrations confined in the nanoparticles. These variations (or lack thereof) are compared to first-principles calculations of the stiffness tensor and phonons of bulk anatase TiO2 as a function of pressure. In particular, the variation of the shape of the low-frequency peak is explained by the increase of the elastic anisotropy of anatase TiO2 as pressure is increased.
Preparation, Characterization, and Photoactivity of Polycrystalline Nanostructured TiO2 Catalysts.
2004
Various preparations of nanostructured TiO2 starting from Ti(iso-OC3H7)4 or TiCl4 are reported. The samples were characterized by X-ray diffractometry, specific surface area and porosity determinations, scanning and transmission electron microscopy, and diffuse reflectance spectroscopy. 4-Nitrophenol photodegradation in aqueous medium was employed as a probe reaction to test the photoactivity of the catalysts. The photoactivity of some samples derived from Ti(iso-OC3H7)4 was found comparable with that of commercial powders. Calcination after the hydrolysis process was necessary to achieve crystallization of the particles before using them as photocatalysts for the reaction studied. The samp…
Preparation and characterisation of TiO2 (anatase) supported on TiO2 (rutile) catalysts employed for 4-nitrophenol photodegradation in aqueous medium…
1999
Abstract In this paper the preparation of two sets of polycrystalline photocatalysts prepared by supporting TiO2 (anatase) on TiO2 (rutile) or Al2O3 is reported. The powders were prepared by a wet impregnation method using titanium(IV) isopropylate. The impregnation was followed by thermal treatment and this procedure was repeated several times in order to obtain samples with progressively increasing amounts of TiO2 (anatase). The photocatalytic activity of all of the specimens was tested by carrying out the 4-nitrophenol photodegradation, used as a “probe” reaction, in aqueous medium and in different kinds of batch photoreactors. The solids were characterised by X-ray diffraction (XRD), sp…
Mesocrystalline Cr and Sb-codoped anatase visible-light-driven photocatalyst
2018
Abstract We report on the synthesis, characterization and visible-light-driven photocatalytic activity of mesocrystalline Cr- and Sb-codoped anatase nanoparticles. Discrete and morphologically well-defined assemblies of anatase nanoparticles sized below 100 nm × 50 nm were prepared by hydrothermal aging of aqueous solutions containing titanium alkoxide, chromium acetylacetonate, antimony acetate and triethanolamine (TEOA) as stabilizer. The as-prepared and TEOA-free doped nanoparticles showed similar crystallographic parameters and spectroscopic features. The incorporation of Cr and Sb dopant cations into the anatase nanoparticles was evaluated by Rietveld refinement of X-ray diffraction pa…
Nature of Interactions at the Interface of Two Water-Saturated Commercial TiO2 Polymorphs
2013
Two commercial TiO2 samples, a 100% anatase and a 100% rutile, were used for the fast field cycling NMR experiments. The results showed a different behavior between the different samples. In particular, water molecules were unbonded to the solid surface for the rutile sample, whereas they appeared to chemically interact with the surface through H-bond formation with the anatase sample. The above findings accord with the generally lower activity of rutile with respect to anatase reported in literature for photocatalytic oxidation reactions in water. The difficulty of water to interact with rutile surface, indeed, could hinder the formation of OH radicals, which are the most important oxidant…
Combined Adsorption/Photocatalytic dye removal by copper-titania-fly ash composite
2020
Abstract Achieving both photocatalytic efficiency and adsorption capacity is essential to produce a highly efficient photocatalyst. This study fabricated a new photocatalyst by combining copper (Cu) doped titanium dioxide (TiO2) with fly ash (FA). The photocatalysts were synthesized using mild acid (acid-FA/Cu/TiO2), base (base-FA/Cu/TiO2), and deionized water (rFA/Cu/TiO2) activated FA. EDX confirmed the inclusion of Cu in both Cu/TiO2 and FA/Cu/TiO2 composites. XRD analysis indicated the presence of the anatase form of TiO2 after Cu doping and incorporation into modified FA. All three FA/Cu/TiO2 composites demonstrated high absorption (UV and visible region) compared to their TiO2 and Cu/…
Nanostructured Pt–TiO2 composite thin films obtained by direct liquid injection metal organic chemical vapor deposition: Control of chemical state by…
2015
Abstract Nanostructured Pt–TiO 2 composite thin films were synthesized by direct liquid injection metal organic chemical vapor deposition process, using trimethyl(methylcyclopentadienyl)platinum and titanium isopropoxide as precursors. Surface and cross-sectional morphologies obtained by scanning electron microscopy and transmission electron microscopy evidenced the uniform distribution of platinum nanoparticles in the TiO 2 matrix. At higher Pt content, the X-ray diffraction analysis showed that the face-centered cubic phase of platinum appeared together with an anatase TiO 2 structure. In addition, as far as the platinum chemical state is concerned, the co-deposition of TiO 2 and Pt allow…
Influence of Amorphous TiO2-x on Titania Nanoparticle Growth and Anatase-to-Rutile Transformation
2012
Amorphous TiO2-x formed together with precursors and anatase nuclei, during TiCl4 hydrolysis at soft conditions, influences both crystal growth and phase stability. The highly defective nanoparticles of anatase grow by reaction of their basic hydroxyls with acidic ones of TiO2 precursor species. The growth of anatase crystals, however, is affected by their interactions with simultaneously formed amorphous TiO2-x which increasingly covers the particles hindering the anatase-precursor contact. The interactions among anatase and amorphous and precursor components have been studied by H-1-MAS (magic angle spinning) NMR spectroscopy. The interaction between acid and basic hydroxyls favors the fo…