X-ray and dielectric characterization of Co doped tetragonal BaTiO3 ceramics
2016
ABSTRACTThe crystal structure modifications of BaTiO3 induced by cobalt doping were studied. The polycrystalline (1 − x)BaTiO3 + xCo2O3 samples, with x ≤ 10 wt.%, were prepared by high temperature sintering conventional method. According to X-ray phase and structural characterization, performed by full-profile Rietveld refinement technique, all synthesized samples showed tetragonal symmetry perovskite structure with minor amount of parasitic phases. Pure single-phase composition has been detected only in the low level of doping BaTiO3. It was indicated that substitution of Co for the Ti sites in the (1 − x)BaTiO3 + xCo2O3 series led to decrease of tetragonality (c/a) of the BaTiO3 perovskit…
Enhancement of the dielectric response through Al-substitution in La1.6Sr0.4NiO4 nickelates
2016
The structures and dielectric properties of La1.6Sr0.4Ni1−xAlxO4 (x = 0, 0.2 and 0.4) ceramics elaborated using the Pechini method were studied for the first time. The same unique tetragonal phase was found in all compounds. The lattice parameters were found using Rietveld refinement. The surface morphology characterization and elemental analysis of these samples were respectively carried out using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). A giant dielectric response was observed in these ceramics, and one dielectric relaxation was found. The substitution of nickel with aluminum results in a colossal dielectric constant value (>106). The dielectric l…
Spin crossover (SCO) iron(II) coordination polymer chain: Synthesis, structural and magnetic characterizations of [Fe(abpt)2(μ-M(CN)4)] (M=PtII and N…
2013
Abstract New iron(II) coordination polymeric neutral chain of formula [Fe(abpt) 2 (μ-M(CN) 4 )], with M = Pt II ( 1 ), Ni II ( 2 ) and abpt = 4-amino-3,5-bis(pyridin-2-yl)-1,2,4-triazole, have been synthesized and characterized by infrared spectroscopy, X-ray diffraction and magnetic measurements. The two compounds are isostructural as deduced from a Rietveld analysis of X-ray powder diffraction data of 2 simulated from the single crystal structure of 1 . The crystal packing of 1 is formed by regular chains running along the crystallographic [−1 0 1] direction where the planar [Pt(CN) 4 ] 2− anion acts as a μ 2 -bridging ligand via two nitrogen atoms of two different trans cyano groups, whi…
Mechanism of crystallization of fast fired mullite-based glass–ceramic glazes for floor-tiles
2006
Abstract The mechanism of crystallization from a B 2 O 3 -containing glass, with composition based in the CaO–MgO–Al 2 O 3 –SiO 2 system, to a glass–ceramic glaze was studied by different techniques. Glass powder pellets were fast heated, simulating current industrial tile processing methods, at several temperatures from 700 to 1200 °C with a 5 min hold. Microstructural study by field emission scanning electron microscopy revealed that a phase separation phenomenon occurred in the glass, which promoted the onset of mullite crystallization at 900 °C. The amount of mullite in the glass heated between 1100 and 1200 °C was around 20 wt%, as determined by Rietveld refinement. The microstructure …
Effect of boron oxide on the microstructure of mullite-based glass-ceramic glazes for floor-tiles in the CaO–MgO–Al2O3–SiO2 system
2006
Abstract The effect of increasing replacement of Al2O3 by B2O3 in a parent glass on the sintering and further crystallization of mullite was investigated. The composition of the parent glass was chosen in the mullite primary phase field of the CaO–MgO–Al2O3–SiO2 quaternary system. Glass powder pellets were heated under standard (10 °C/min and 2 h of hold time) and fast heatings (25 °C/min and 5 min of hold time) at different temperatures from 700 to 1190 °C. Sintering of B2O3-containing glasses took place in the range between 850 and 1050 °C. X-ray diffraction results showed that mullite formed as unique crystalline phase for glasses containing amounts of B2O3 larger than 6 wt%. For lower a…
BN/GdxTi(1-x)O(4-x)/2 nanofibers for enhanced photocatalytic hydrogen production under visible light
2019
Abstract BN/GdxTi(1-x)O(4-x)/2 nanofibers were elaborated via electrospinning technique. The properties of the prepared nanofibers were controlled using different ratios of gadolinium. All the prepared nanofibers exhibit the tetragonal structure of anatase TiO2 phase. An increase in the unit cell volume and a decrease in the crystallite size were observed with increasing the doping amount of Gd3+ as revealed by Rietveld refinement analysis. The defect in TiO2 lattice was observed by Raman. The Gd3+ incorporation inside TiO2 lattice, which is accompanied by the creation of Ti-O-Gd bond, was characterized by the X-ray photoelectron spectra. Scanning electron microscopy demonstrates that the a…
Photocatalytic activity of anatase-nickel ferrite heterostructures
2015
The simple co-precipitation route was used to couple commercial TiO2 anatase nanopowder with nickel ferrite (NiFe2O4). The morphology and the crystalline structure of composite nanoparticles were characterised by TEM, N2 adsorption-desorption, XRD and Rietveld refinement, XPS and XAS. The optical and magnetic properties were investigated. After co-precipitation NiFe2O4 nanoparticles, composed of spinel ferrite crystal phase, were formed on the surface of TiO2 anatase nanopowder. The TiO2/NiFe2O4 composite oxide demonstrated large specific surface area, high visible light absorption efficiency and efficient charge carrier separation, compared to pristine anatase TiO2 or pristine NiFe2O4, rep…
Phase formation in mixed TiO2-ZrO2 oxides prepared by sol-gel method
2011
Pure titania, zirconia, and mixed oxides (3—37 mol.% of ZrO2) are prepared using the sol-gel method and calcined at different temperatures. The calcined samples are characterized by Raman spectroscopy, X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption porosimetry. Measurements reveal a thermal stability of the titania anatase phase that slightly increases in the presence of 3—13 mol.% of zirconia. Practically, the titania anatase-rutile phase transformation is hindered during the temperature increase above 700 C. The mixed oxide with 37 mol.% of ZrO2 treated at 550 C shows a new single amorphous phase with a surface area of the…
MZ-35, a new layered pentasil borosilicate synthesized in the presence of large alkali cations
2013
Abstract A new layered borosilicate has been synthesized in the presence of cesium and sodium cations and its structure has been solved by a combination of automated diffraction tomography (ADT) and X-ray powder diffraction (XRPD). MZ-35 has a composition NaCs 2 [BSi 7 O 16 (OH) 2 ](OH) 2 ·4H 2 O and features space group P-4m2. The unusually small unit cell ( a 7.3081 A, c 10.7520 A) is shared by two random-stacked configurations of the structure: a network of connected pentasil units related to the layer of RUB-18 and a bidimensional checkerboard of intersecting ladders of 4-membered rings. The two configurations are related by the simple face-sharing inversion of a hydroxyl-bearing tetrah…
Smaller calcite lattice deformation caused by occluded organic material in coccoliths than in mollusk shell.
2015
7 pages; International audience; The growth and nucleation of biominerals are directed and affected by associated biological molecules. In this paper, we investigate the influence of occluded biomolecules on biogenic calcite from the coccolithophorid Pleurochrysis carterae and from chalk, a rock composed predominantly of fossil coccoliths. We compare the results with data on chalk from the extensively studied mussel Pinna nobilis that served as a control. Using high resolution synchrotron powder X-ray diffraction combined with in situ heating, the influence of organic compounds on the structure of the inorganic phase was probed. Two heating cycles allow us to differentiate the effects of th…