Phase formation in mixed TiO2-ZrO2 oxides prepared by sol-gel method
2011
Pure titania, zirconia, and mixed oxides (3—37 mol.% of ZrO2) are prepared using the sol-gel method and calcined at different temperatures. The calcined samples are characterized by Raman spectroscopy, X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption porosimetry. Measurements reveal a thermal stability of the titania anatase phase that slightly increases in the presence of 3—13 mol.% of zirconia. Practically, the titania anatase-rutile phase transformation is hindered during the temperature increase above 700 C. The mixed oxide with 37 mol.% of ZrO2 treated at 550 C shows a new single amorphous phase with a surface area of the…
High photodegradation and antibacterial activity of BN–Ag/TiO 2 composite nanofibers under visible light
2018
To develop material with good photocatalytic properties for organic compound degradation and bacterial removal, we produced Ag/TiO2 and BN–Ag/TiO2 composite nanofibers that included controlled amounts of boron nitride (BN) nanosheets and silver (Ag). After annealing at 500 °C under air, we used scanning electron microscopy, transmission electron microscopy, Brunauer–Emmet–Teller analysis, X-ray diffraction, energy-dispersive X-ray spectroscopy, Raman spectroscopy, UV-visible reflectance spectroscopy and room temperature photoluminescence to investigate the morphological, structural and optical properties of all samples. The photocatalytic tests using methylene blue under visible light, in r…
Risk estimation for air travel-induced malaria transmission in central Europe – A mathematical modelling study
2019
Abstract Background Aim of our study was to identify conditions under which malaria transmission caused by imported infectious mosquitoes or travellers could occur at large central European airports, and if such transmission could be sustained by indigenous mosquitoes. Methods We developed a deterministic and a stochastic compartmental Susceptible-Exposed-Infectious-Recovered-Susceptible (humans)/Susceptible-Exposed-Infectious (mosquitoes) model with two mosquito (imported Anopheles gambiae, indigenous A. plumbeus) and three human (travellers, airport personnel exposed/not exposed to imported A. gambiae) populations. We assessed various scenarios to identify combinations of model parameters…
Transmissibility ofBroad bean wilt virus 1by aphids: influence of virus accumulation in plants, virus genotype and aphid species
2012
Broad bean wilt virus 1 (BBWV-1) is transmitted by several aphid species in a non-persistent manner. Transmission efficiency by vectors is a key factor for understanding virus epidemiology and applying disease control measures based on limiting virus spread. We evaluated the transmission rates of two genetically divergent BBWV-1 isolates (PV-132 from USA and Ben from Spain) infecting broad bean (Vicia faba L.) by isofemale lines of nine aphid species from eight different genera collected in Spain. Our analyses showed that: (a) the virus concentration in the source plant was a key factor in BBWV-1 transmissibility; (b) The Spanish isolate Ben was transmitted more efficiently than the America…
Symbiosis between photoactive nanoparticles and their organic ligands.
2013
Photoactive spherical metal and semiconductor nanoparticles (NPs) are smart systems that exhibit unique properties, such as a high surface-to-volume ratio, a broad absorption spectrum and size-dependent properties. They are capped with a considerable number of ligands required to give rise to stable organic and aqueous NP colloidal solutions. In addition, the ligands can also be used to introduce functionality at the NP periphery. In this case, the NP could act as a 3D-scaffold, which would make a high local concentration of a functional moiety at the NP periphery possible, moreover, the photophysical properties of the NP could be tuned. The combined action of the organic capping and the in…
Influence of temperature on the synthesis of thiol-stabilized CdTe nanoparticles in aqueous solutions
2010
We have investigated the evolution of thiol-capped cadmium telluride nanocrystals prepared in aqueous solutions at low and room temperature followed by heating at 50–100 °C. The UV–visible absorption spectra, as well as transmission electron microscopy, atomic force microscopy, and dynamic light scattering observations made it possible to reveal differences in size and structure originating from different heating temperatures. It was shown that minimization of the nucleation process temperature provided formation of larger nanoparticles than at higher temperatures.
Facile synthesis and characterization of functionalized, monocrystalline rutile TiO2 nanorods.
2006
Functionalized, monocrystalline rutile TiO2 nanorods were prepared from TiCl4 in aqueous solution under acidic conditions in the presence of dopamine, followed by aging and hydrothermal treatment at 150 degrees C. The surface-bound organic ligand controls the morphology as well as the crystallinity and the phase selection of TiO2. The presence of monocrystalline rutile TiO2 was confirmed by X-ray powder diffraction and HRTEM investigations. The as-prepared nanorods are soluble in water at pH3. The surface functionalization was analyzed by IR and 1H NMR, confirming the presence of dopamine on the surface. The surface amine groups can be tailored further with functional molecules such as dyes…
Characterization of Zirconium Phosphate/Polycation Thin Films Grown by Sequential Adsorption Reactions
1997
Monolayer and multilayer thin films consisting of anionic α-zirconium phosphate (α-ZrP) sheets and polycations (poly(allylamine hydrochloride) (PAH), cytochrome c) were characterized by transmission electron microscopy (TEM), ellipsometry, UV−visible absorbance spectroscopy, reflectance FT-IR, XPS, and X-ray diffraction. Titration and powder X-ray diffraction experiments confirm that exfoliation of α-ZrP begins to occur when enough tetra(n-butylammonium) hydroxide (TBA+OH-) has been added to exceed single-layer packing of TBA+ ions (x ≈ 0.50) in the intercalation compound Zr(HPO4)2-x(TBA+PO4-)x·nH2O. The identical contrast of many sheets in TEM micrographs suggests that the suspension is un…
Double-Shell Vesicles, Strings of Vesicles and Filaments Found in Crosslinked Micellar Solutions of Poly(1,2-butadiene)-block-poly(ethylene oxide) Di…
2001
Micellar structures of amphiphilic poly(1,2-butadiene)-block-poly(ethylene oxide) diblock copolymers have been crosslinked in aqueous solution by γ-irradiation. By transmission electron microscopy (TEM) of neganively stained specimen it is shown that the precominant structures present are sopolymer sesicles (which appear to be double latered. These fived vesules are stable with respect to their share and can be transferred from water into a good solvent for blue filbeks, such as tetrahydrofuran, this demonstrating the effectiveness of the crosslinking. In addition to the resicles a small number of flexible cylindrichl/filimented structures sequentially fused vesicles/strings of vesicles and…
Structural Characterization of Zirconia Nanoparticles Prepared by Microwave-Hydrothermal Synthesis
2009
Nanocrystalline zirconia powders have been prepared by microwave-hydrothermal synthesis starting from aqueous solution of ZrOCl2·8H2O. Results of investigations on the aqueous suspension stability of the washed zirconia nanopowders by dynamic light scattering showed that the suspension, constituted by superaggregates of nanoparticles (131 ± 10 nm), was stable up to 15 days. Nanopowders were investigated by means of transmission electron microscopy and small angle x-ray scattering measurements which proved that the zirconia nanopowder is constituted by small primary nanoparticles of ca. 8 nm that agglomerate forming bigger aggregates of 50 ± 1 nm.