Effect of water contamination on the shear bond strength of five orthodontic adhesives
2010
Objectives: To evaluate the shear bond strength and site of failure of brackets bonded to dry and wet enamel. Study design: 50 teeth were divided into ten groups of 5 teeth each (10 surfaces). In half the groups enamel was kept dry before bonding, and in the other half distilled water was applied to wet the surface after etching. The following groups were established: 1)Acid/Transbond-XT (dry/wet) XT; 2) Transbond Plus Self Etching Primer (TSEP)/Transbond-XT paste (dry/wet); 3) Concise (dry), Transbond MIP/Concise (wet), 4) FujiOrtho-LC (dry/ wet); 5) SmartBond (dry/wet). Brackets were bonded to both buccal and lingual surfaces. Specimens were stored in distilled water (24 hours at 37ºC) an…
The effect of different force magnitudes for placement of orthodontic brackets on shear bond strength, in three adhesive systems.
2018
Background: Amount of pressure exerting on orthodontic brackets during bonding can create different thickness of adhesive and affect shear bonding strength(SBS) in different adhesive systems. The purpose of this study was to evaluate the effect of different force magnitudes for placement of brackets on SBS. Material and Methods: In an in vitro study, 420 brackets were placed on the bovine teeth, using three types of adhesives, Concise (chemically cured two-paste mix), Unite (chemically cured no mix), and Transbond XT( light cured), with the application of seven force magnitudes of 50, 100, 200, 300, 400, 600 and 1000 grams in twenty-one groups of twenty samples each. SBS means (using two-wa…
Lessons Learned on the Tensile and Bond Behavior of Fabric Reinforced Cementitious Matrix (FRCM) Composites
2020
Fabric Reinforced Cementitious Matrix (FRCM) composites represent an effective, compatible and cost-efficient solution for strengthening and retrofitting existing structures. A strong research effort was done to investigate the tensile and bond properties of these materials, as well as the overall behaviour of strengthened members. A Round Robin Test was organized by Rilem TC 250-CSM on 28 FRCM composites comprising basalt, carbon, glass, PBO, aramid and steel textiles, embedded in either cement, lime or geopolymer mortars, to collect an experimental dataset and define test protocols. This paper collects the outcomes of this study to highlight fundamental properties of FRCM and to investiga…
Effect of glycine pretreatment on the shear bond strength of a CAD/CAM resin nano ceramic material to dentin
2016
Background: The purpose of this study was to evaluate the effect of glycine pretreatment on the shear bond strength between dentin and a CAD/CAM resin nano ceramic material (LavaTM Ultimate Restorative), bonded together with adhesive cements using three different luting protocols (total-etch; self-etch; self-adhesive). Material and Methods: Thirty cylinders were milled from resin nano ceramic blocks with CAD/CAM technology. The cylinders were subsequently cemented to the exposed dentin of 30 bovine permanent mandibular incisors. The specimens were assigned into six groups of five teeth each according to luting procedure and dentin pretreatment. In the first two groups (A1, A2) 10 cylinders …
Evaluation of the effect of three innovative recyling methods on the shear bond strength of stainless steel brackets-an in vitro study
2016
Background Orthodontists are commonly faced with the decision of what to do with debonded or inaccurately positioned brackets. An economical option to this dilemma is to recycle the brackets. Many recycling methods have been proposed, but the optimal bond strength of these recycled brackets needs further evaluation. Objectives: To evaluate and compare the effect of three recycling methods: (i) Sandblasting (ii) Sandblasting / direct flaming (iii) Sandblasting /direct flaming /acid bath solution on shear bond strength (SBS) of stainless steel brackets. Material and Methods Eighty human premolars were bonded with premolar stainless steel brackets as per manufacturer’s instructions. The teeth …
Comparative evaluation of orthodontic bracket base shapes on shear bond strength and adhesive remnant index : an in vitro study
2017
BACKGROUND The objective of this study was to evaluate the effect of orthodontic bracket base shape on shear bond strength and adhesive remnant index. MATERIAL AND METHODS In this in vitro study using 140 bovine incisors, shear bond strength (SBS) of brackets with different base shapes (rectangle, flower, round, heart, diamond, star, and football) were measured with an Instron testing machine and tested until bond failure. Adhesive Remnant Index (ARI) scoring was evaluated after debonding to evaluate the location of bond failure. Descriptive and one-way ANOVA post-hoc Tukey statistical analyses were performed with a statistical significance set at p≤0.05. RESULTS Statistically significant d…
The impact of different surface treatments on the shear bond strength of orthodontic metal brackets applied to different CAD/CAM composites
2020
Background To investigate the shear bond strength (SBS) of orthodontic metal brackets applied to different CAD/CAM composites treated with different surface treatments. Material and Methods Specimens of two CAD/CAM composites were obtained of Lava Ultimate (LU; n=60) and Brilliant Crios (BC; n=60) which were randomly separated into six subgroups (n=10) according to the surface treatment: control (CTL); sandblasting (SB); sandblasting and silane (SBSL); hydrofluoric acid (HF); hydrofluoric acid and silane (HFSL); and Monobond Etch&Prime (MEP). The mandibular central incisor metal brackets were bonded with a light-cure adhesive. The SBS data were analyzed using the two-way analysis of varianc…
Effects of recycling and bonding agent application on bond strength of stainless steel orthodontic brackets
2014
Objectives: 1) to assess different methods of recycling orthodontic brackets, 2) to evaluate Shear Bond Strength (SBS) of (a) new, (b) recycled and (c) repeated recycled stainless steel brackets (i) with and (ii) without bracket base primer. Study Design: A total of 180 extracted human premolar teeth and 180 premolar stainless steel brackets were used. One hundred teeth and 100 brackets were divided into five groups of 20-teeth each. Four methods of recycling orthodontic brackets were used in each of the first four groups while the last one (group V) was used as the control. Groups (I-V) were subjected to shear force within half an hour until the brackets debond. SBS was measured and the me…
Shear bond strengths of composite resin and giomer to mineral trioxide aggregate at different time intervals
2017
Background The efficacy of the bond between the restorative materials and the pulp capping materials has an important role in the success of vital pulp therapy. Therefore, the aim of this study was to evaluate the shear bond strength of composite resin and giomer to MTA at different time intervals after mixing of MTA. Material and methods Ninety cylindrical MTA samples were prepared and assigned to two groups (n=45) based on the restorative materials used (composite resin or giomer). Each group was subdivided into 3 subgroups (n=15) based on the evaluation intervals (immediately, 2.45 hours and 3 days after mixing MTA). After the bonding procedures, the shear bond strengths of the samples w…
Comparative evaluation of shear bond strength of three flowable compomers on enamel of primary teeth: An in-vitro study
2015
Background: The aim of the present study was to determine Shear bond strength (SBS) of different flowable compomers on the enamel surface of primary teeth. The null hypothesis to be tested was that none of the flowable compomer would differ significantly from the other two with respect to SBS. As a result, the tested materials that have the easiest application on child patient is preferred. Material and Methods: Sixty newly extracted non carious primary molars were selected. The buccal surface was cleaned and polished to obtain a flat enamel surface. The specimens were randomly divided into three groups of 20 teeth each, based on the flowable compomers applied, as follows: group I: Dyract F…