Search results for "Tensile testing"
showing 10 items of 35 documents
Generation and characterization of T40/A5754 interfaces with lasers
2014
Laser-induced reactive wetting and brazing of T40 titanium with A5754 aluminum alloy with 1.5 mm thickness was carried out in lap-joint configuration, with or without the use of Al5Si filler wire. A 2.4 mm diameter laser spot was positioned on the aluminum side to provoke spreading and wetting of the lower titanium sheet, with relatively low scanning speeds (0.1 to 0.6 m/min). Process conditions did not play a very significant role on mechanical strengths, which were shown to reach 250-300 N/mm on a large range of laser power and scanning speeds. In all cases considered, the fracture during tensile testing occurred next to the TiAl3 interface, but in the aluminum fusion zone. In a second st…
The system of carbon fibre-reinforced plastics micro-tubes for self-healing of glass fibre-reinforced plastics laminates
2016
A system of pultruded carbon fibre-reinforced plastics micro-tubes is used for self-healing simulation in laminated polymer composite. The system consists of a package of micro-tubes, placed in the symmetry plane of the GFR/epoxy laminate stack. Healing agent is a mixture of the epoxy resin and hardener. The healing agent releases and penetrates into the cracks after the composite is damaged by the quasi-static indentation. The specimens are healed at 30℃ for 24 h. Rectangular specimens notched under ASTM D2733 have been subjected to tensile test to determine interlaminar shear strength. Shear strength of specimens has been compared in three states (virgin, damaged and healed) for various …
Inverse growth transport in thermal chromia scales on Fe–15Cr steels in oxygen and in water vapour and its effect on scale adhesion
2007
Chromia scales of near equivalent thickness were thermally grown on Fe–15Cr steels in 16O2 followed by 18O2 and in H216O followed by H218O. SIMS oxygen isotope profiles showed that oxidation in oxygen proceeded by outward chromium transport, whereas oxidation in H2O involved inward transport of hydroxide species. Adhesion measurements using room temperature tensile testing could quantify adhesion energy: 20 J m−2 for O2-grown scales and 80 J m−2 for scales formed in H2O, a result of this mass transport inversion.
Beta-forging of Ti6Al4V titanium alloy powders consolidated by HIP: Plastic flow and strain-rate relation
2014
Ti6Al4V is probably the best known and studied titanium alloy, not only for aerospace applications. Nevertheless the deformation behavior still represents a challenge if any modification in the deformation process is required or introduced. This work deals with deformation behavior description of Ti6Al4V HIPped powders during high temperature deformation tests carried on in the Beta-region. Laboratory compression and tensile tests have been coupled with relaxation tests in order to achieve robust data about strain rate sensibility m-coefficient and activation energy Q. These results have been fitted for the assessment of a more general exponential deformation law. The final result is a “Dor…
Solid state bonding mechanics in extrusion and FSW: Experimental tests and numerical analyses
2007
In the paper the authors compare the different solid state bonding mechanics for both the processes of hollow profiles extrusion and Friction Stir Welding (FSW), through the results obtained from a wide experimental campaign on AA6082-T6 aluminum alloys. Microstructure evaluation, tensile tests and micro-hardness measurements realized on specimens extracted by samples of the two processes are discussed also by means of the results obtained from coupled FEM simulation of the processes. ©2007 American Institute of Physics
Powder metallurgy processing and deformation characteristics of bulk multimodal nickel
2014
cited By 7; International audience; Spark plasma sintering was used to process bulk nickel samples from a blend of three powder types. The resulting multimodal microstructure was made of coarse (average size ∼ 135 μm) spherical microcrystalline entities (the core) surrounded by a fine-grained matrix (average grain size ∼ 1.5 μm) or a thick rim (the shell) distinguishable from the matrix. Tensile tests revealed yield strength of ∼ 470 MPa that was accompanied by limited ductility (∼ 2.8% plastic strain). Microstructure observation after testing showed debonding at interfaces between the matrix and the coarse entities, but in many instances, shallow dimples within the rim were observed indica…
Scale effect of the tensile strength of flax-fabric-reinforced polymer composites
2011
The development of UD natural fiber composites, considered for application as structural materials, necessitates evaluation of the scale effect of their strength. Alignment of the fibers in flax bast fiber composites can be achieved by employing textile reinforcement, such as yarns and fabrics. Cutting specimens for mechanical tests out of such textile-reinforced composite plates results in a complex non-uniform reinforcement structure at their edges, which may affect the strength of specimens. Scale effect of the tensile strength in the fiber direction of flax-fabric-reinforced composites is studied in the current work. A model accounting for both volume and edge effect of the specimens o…
Amorphous and crystalline polyetheretherketone: Mechanical properties and tissue reactions during a 3-year follow-up.
2007
The study was aimed to test the mechanical strength, structural stability, and tissue reactions of optically amorphous and crystalline polyetheretherketone (PEEK) plates during a 3-year follow-up in vivo and in vitro. The injection-moulded PEEK plates were implanted to the dorsal subcutis of 12 sheep, which were sacrificed at 6-156 weeks. Thereafter, the plates were subjected to tensile tests, and levels of crystallinity were assessed by differential scanning calorimetry (DSC). Histological evaluation was carried out using the paraffin technique. In vitro properties were examined with the tensile test and DSC at 0-156 weeks. Tissue reactions were mild and fairly similar for the amorphous an…
Investigation and modeling of the anomalous yield point phenomenon in pure tantalum
2014
International audience; The monotonic and cyclic behavior of commercially pure tantalum has been investigated at room temperature, in order to capture and understand the occurrence of the anomalous yield point phenomenon. Interrupted tests have been performed, with strain reversals (tensile or compressive loading) after an aging period. The stress drop is attributed to the interactions between dislocations and solute atoms (oxygen) and its macroscopic occurrence is not systematically observed. InfraRed Thermography (IRT) measurements supported by Scanning Electron Microscopy (SEM) pictures of the polished gauge length of a specimen during an interrupted tensile test reveal the nucleation an…
Theoretical and Experimental Researches Regarding Multilayer Materials Used for Incremental Forming
2014
Although this represents a relatively recent development in the industry, the composite multilayer sheets are currently encountered in almost all industrial domains, due to the density, mechanical strength and energy absorption properties that are higher than those of the blanks realised from a single material. These materials are useful especially in domains such a the automotive industry, where the vehicles must fulfil simultaneously conditions of increased passenger safety, increased comfort, increase of the loading capacity in conditions of a reduced energy consumption. First of all the paper shows the types of multilayer sheets and their areas and areas of use, then the paper analyzes …