Evaluation of bond strength of orthodontic brackets without enamel etching
2015
Background: to compare the shear bond strength of brackets with and without enamel etching. Material and Methods: In this study, 60 sound premolars were randomly divided into four different groups: 1- TXE group: Enamel etching + Transbond XT adhesive + Transbond XT composite. 2- TXS group: Transbond plus self-etch adhesive + Transbond XT composite. 3- PQ1E group: Enamel etching + PQ1 adhesive + Transbond XT composite. 4- PQ1 group: PQ1 adhesive + Transbond XT composite. The shear bond strengths of brackets were evaluated using universal testing machine at cross head speed of 0.5 mm/ min. The Adhesive Remnant Index (ARI) was also measured. One-way ANOVA, Tukey’s post hoc, Kruskal-wallis and …
Evaluation of micro shear bonding strength of two universal dentin bondings to superficial dentin by self etch and etch-and-rinse strategies
2018
Background Universal bondings can be used either with the etch-and-rinse or self-etch technique. Thus, the present study was done to evaluate the micro-shear bonding strength of two types of Universal Bondings to superficial dentin i.e self-etch and etch and rinse. Material and Methods The samples included 70 tooth blocks taken from 35 extracted sound premolar teeth. The superficial dentin was exposed to grinding by 800 grit silicon carbide Disk. The samples were randomly divided into 5 equal groups (14 samples in each group). Scotch bond universal (3M/USA) and All bond universal (BISCO/USA) were applied by self-etch and etch and rinse technique in group 1-4 and Adper Single bond 2 (3M/USA)…
Shear bond strength of metal brackets to ceramic surfaces using a universal bonding resin.
2017
BACKGROUND: Assure Plus is a recently introduced universal adhesive with the ability to bond to various restorations. This study compared the shear bond strength of brackets bonded to two types of ceramics using conventional bonding agent and Assure Plus. Surface damage caused by debonding was also evaluated. MATERIAL AND METHODS: In this in vitro study, 40 feldspathic and lithium disilicate ceramic discs were sandblasted, etched with 9.6% hydrofluoric acid and divided into two groups. In group 1, silane was applied and air-dried followed by application of Transbond XT primer, which was light-cured. In group 2, Assure Plus was applied and air-dried. In both groups, maxillary central incisor…
Effect of thermocycling and surface treatment on repair bond strength of composite.
2017
BACKGROUND Repair of composite restorations is a conservative method that can increase the longevity and durability of restorations while preserving the tooth structure. Achieving a suitable bond between the old and new composite is difficult. To overcome this problem, some methods have been recommended to increase the repair bond strength of composite.This study aimed to assess the effect of aging by thermocycling (5,000 and 10,000 cycles) and mechanical surface treatments (Er,Cr:YSGG laser and bur) on repair shear bond strength of composite resin. MATERIAL AND METHODS Totally, 120 composite blocks measuring 6x4x4 mm were fabricated of Filtek Z250 composite and were randomly divided into t…
Mechanical and dentin bond strength properties of the nanosilver enriched glass ionomer cement
2019
Background The aim of this study was to investigate the mechanical properties and dentin microshear bond strength of a conventional glass ionomer cement (GIC) compared to GIC supplemented with silver nanoparticles (SNPs) at 0.1% and 0.2% (w/w). Material and Methods SNPs were incorporated into a conventional GIC at 0.1% and 0.2% (w/w). The unmodified GIC was used as the control group. Compressive strength, flexural strength, and micro-shear bond strength (µSBS) to dentin were evaluated using a universal testing machine. Surface microhardness was determined using a Vickers microhardness tester. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey’s test. Results GICs co…
Shear bond strength of one-step self-etch adhesives to dentin: Evaluation of NaOCl pretreatment
2018
Background The aim of this study was to evaluate the influence of dentin pretreatment with NaOCl on shear bond strength of four one-step self-etch adhesives with different pH values. Material and methods Bovine permanent incisors were used. Four one-step self-etch adhesives were tested: Adper™ Easy Bond, Futurabond NR, G-aenial Bond, Clearfil S3 Bond. One two-step self-etch adhesive (Clearfil SE Bond) was used as control. Group 1- no pretreatment; group 2- pretratment with 5,25 % NaOCl; group 3- pretreatment with 37 % H3PO4 etching and 5,25 % NaOCl. A hybrid composite resin was inserted into the dentin surface. The specimens were tested in a universal testing machine. The examiners evaluate…
A comparative evaluation of shear bond strength between feldspathic porcelain and lithium di silicate ceramic layered to a zirconia core? An in vitro…
2020
Background The bond strength between the zirconia core and ceramic veneer is the weakest component in the layered structure. Delamination of veneering ceramic is reported as one of the most frequent problems associated with Veneered Zirconia restorations. The aim of this study is to compare the shear bond strength of lithium di silicate porcelain to that of feldspathic porcelain on a zirconia Substrate. Material and Methods Two groups (group A and B) of zirconia blocks with each group having 20 samples were fabricated according to Schmitz Schulmeyer method. Group A (n =20 ) samples were veneered with feldspathic veneering porcelain and Group B (n=20) samples were veneered with heat pressed …
Deformation of Polypropylene Foam Neopolen® P in Compression
2004
Neopolen® P is a two-phase cellular composite foam material produced by BASF AG, Germany. In most of the practical applications, Neopolen® P works under a range of small and compressive deformations. Therefore it is necessary to determine the moduli in compression and compressive strength in the most effective way for a wide range of foam densities: 22≤ρ84≤kg/m3. Several experimental methods of different precision for deformation properties of Neopolen® P were compared. The direct measurements performed by a universal testing machine were used for the main part of the experiments. They were compared with results obtained by a more precise and time-consuming method, using an inductive exten…
Microleakage and shear bond strength of orthodontc brackets bonded to hypomineralized enamel following different surface preparations
2014
Objectives: This study investigated the effects of several conditioning methods on shear bond strength (SBS) and microleakage of orthodontic brackets bonded to demineralized enamel. Study Design: One hundred premolars were selected and immersed in a cariogenic solution for 12 weeks. The teeth were randomly assigned into 5 groups. In groups 1 and 2, the teeth underwent acid etching for 30 and 120 seconds, respectively. In group 3, a combination of laser and acid etching was employed. A self-etch primer (SEP) was applied in group 4 and in group 5, the teeth were exposed to acidulated phosphate fluoride (APF) for 4 minutes before etching. After bracket bonding, the teeth were immersed in methy…
Influence of preheating on mechanical and surface properties of nanofilled resin composites
2019
Background Resin composite preheating is an innovative method that could be clinically beneficial by improving the handling properties, marginal adaptation, and surface properties of uncured nanofilled resin composite materials. There is conflict and unclear information regarding the effect of preheating on the microhardness, fracture toughness and surface roughness of nanofilled resin composites. Thus, it is important to assess whether dental clinicians can adopt preheating procedures without compromising composite mechanical strength. Objective: The purpose of this study was to evaluate the effect of preheating on microhardness, fracture toughness and surface roughness of nanofilled resin…