Comparative study of [001] surface relaxations of perovskite titanates
1998
Surface relaxations of the cubic perovskite SrTiO and BaTiO crystals have been studied in the framework of the shell model. The 33 positions of atoms in several surface layers embedded into the electrostatic field of the remainder of the crystal were calculated. Ti 4q , Sr 2q ,B a 2q and O 2y ions in six near-surface layers are displaced differently from their crystalline sites. Such effects create the so-called surface rumpling, a dipole moment and the electric field in the near-surface region. Calculated atomic displacements were compared with the LEED experimental data and showed good agreement. Our simulations have demonstrated that the cubic perovskite SrTiO crystals 3 reveal surface p…
Segregation of copper oxide on calcium copper titanate surface induced by Graphene Oxide for Water splitting applications
2020
Abstract Photoelectrochemical cells (PEC) are promising devices for hydrogen production via sunlight energy. One of the important challenges in this area is to design photoactive electrodes able to absorb visible light. A good photoelectrochemical behavior depends on the presence of surface active sites to photogenerate current at the lower possible potential for water splitting. Recent investigations in this field are focusing on perovskite materials such as CaCu3Ti4O12 (CCTO) as visible light active electrode due its outstanding structure in which CCTO encloses in its structure a visible light absorbance component (CuO). The presence CuO on the material surface is mainly responsible for t…
Grain-size-induced relaxor properties in nanocrystalline perovskite films
2004
Thin films of ${\mathrm{Pb}}_{0.76}{\mathrm{Ca}}_{0.24}{\mathrm{TiO}}_{3}$ (PTC), which is a classical ferroelectric as a bulk material and of the relaxor material $\mathrm{Pb}({\mathrm{Sc}}_{0.5}{\mathrm{Nb}}_{0.5}){\mathrm{O}}_{3}$, have been produced to find out whether nanocrystalline ferroelectric films show a grain-size-induced relaxor behavior. Amorphous films were deposited onto a $\mathrm{Ti}∕\mathrm{Pt}$ coated silicon (100) wafer by reactive $\text{rf}$ sputtering. Different grain sizes were prepared by a controlled annealing process and they were determined by profile analysis of x-ray diffraction spectra. Temperature dependent Raman spectroscopy was used to look for phase trans…
Fine grain barium titanate: ferroelectric domains and X-ray diffraction diagram
2002
Through three different studies using various kinds of BaTiO/sub 3/ samples: as a powder while heating over the Curie temperature; as a green ceramic as a function of the forming pressure; as a ceramic while applying a D.C. field. It is shown how X-ray diffraction is able to give information about the evolution of the 90/spl deg/ ferroelectric domain microstructure.
Preparation and Electric Properties of Barium Zirconium Titanate Ceramic
2015
The relaxor behavior of barium zirconium titanate ceramics BaZr0.35Ti0.65O3 prepared by a conventional sintering process was investigated. The synthesized material was determined by an X-ray diffraction and scanning electron microscopy. Based on performed studies, the BaZr0.35Ti0.65O3 ceramic material has been identified as canonical relaxor, related to the Ti-rich polar regions. The freezing temperature Tf and activation energy Ea are calculated from the Vogel-Fulcher relationship.
X-ray Studies of Debye Temperature of Some ABO 3 Perovskites
2002
Debye temperatures T D of some perovskite compounds are determined by X-ray diffraction. Correlation between T D determined at T=180 °C, mean square displacements of atoms, quasi-elastic coupling, and melting temperature of the perovskite compounds is analysed.
On the existence of a pyrochlore-type phase in the system Bi2O3–TiO2
1995
The existence of a bismuth titanate in the range between Bi 2 Ti 4 O 11 (Bi 2 O 3 . 4 TiO 2 ) and Bi 4 Ti 3 O 12 (2 Bi 2 O 3 . 3 TiO 2 ) has been investigated by X-ray diffraction of samples prepared by solid state reactions. For reaction temperatures above 1100 °C and a starting composition Bi 2 O 3 . 2 TiO 2 there appeared additional lines which could be attributed to a cubic face-centred cell with a = 10.354 A. A multiphase Rietveld analysis based on X-ray powder diffraction data confirmed the structural model of a pyrochlore for this compound. There is evidence that this phase belongs to the group of defect pyrochlores with a Bi 3+ -deficiency resulting in a composition of Bi 1.833 Ti 2…
A multi-step mechanism and integrity of titanate nanoribbons.
2014
A one-step hydrothermal treatment of TiO2 powders under strongly basic conditions has been used to synthesize titanate nanoribbons. The nanoparticles were thoroughly characterized using several methods including transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy and X-ray photoelectron spectrometry (XPS) to determine their morphological, structural and chemical characteristics. The influence of the nature and size of the TiO2 precursor and of the reaction duration on the formation of the nanoribbons was investigated. The conditions required to obtain only titanate nanoribbons with a width ranging from 100 to 200 nm and several tens of micrometers in length w…
Elastic Properties of Barium Zirconate Titanate Ceramics
2011
In the paper the influence of zirconium admixture on the structure and material constants of polycrystalline ferroelectric materials BaZrxTi1-xO3 (BZT) was examined. The barium zirconate titanate samples were prepared by a conventional solid state reaction method. A single phase with perovskite structure of the samples, was identified by an X-Ray diffraction technique at room temperature. The performed EDS study revealed that the samples were perfectly sintered and the material was chemically homogeneous. The dependence of shear modulus G on sample composition is similar to the respective dependence of Young's modulus E, whereas the Poisson's ratio ν decreases with the increase in zirconium…
Structural, microstructural and impedance spectroscopy study of functional ferroelectric ceramic materials based on barium titanate
2013
The differences between the physical properties of barium titanate BaTiO3 and newly obtained BaHfxTi1-xO3 were identified. These ceramics were prepared by solid-phase reaction from simple oxides and carbonates using the conventional method. The structure and morphology of investigated samples were characterised by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The application of impedance spectroscopy made possible to characterize of these materials in the terms of electrical properties.