Photocatalytic H2 production over inverse opal TiO2 catalysts
2019
Abstract The influence of BiVO4 and CuO on the chemico-physical properties of TiO2-based systems is reported. The performances of these systems were investigated in the photocatalytic H2 production both under UV and solar light irradiation. The characterization data pointed out that the obtained TiO2 samples have highly porous inverse opal structures with interconnected macropores. Inverse opal TiO2 exhibited higher activity in the H2 production than the commercial TiO2 due to the peculiar porosity that allows photons to enter inside the photocatalyst. A further improvement in terms of photoactivity was verified by addition of increasing amounts of BiVO4. On the contrary a small CuO content…
Study of titanium alloy Ti6242S oxidation behaviour in air at 560°C: Effect of oxygen dissolution on lattice parameters
2020
Abstract High temperature oxidation of titanium alloy Ti6242S was studied in air at 560 °C up to 10000 h. Oxidation kinetics obeys a parabolic law (kp = 8.7 × 10−15 g². cm−4.s-1). Oxygen dissolution in the metal was found to represent between 80 and 90% of the total mass gain. Thin oxide scales are mainly composed of TiO2, in top of which some alumina is present. Titanium nitride was detected as a very thin layer at the outer part of the metallic substrate. Underneath, the oxygen dissolution area was found to reach the maximum brittleness after 1000 h of oxidation.
Mechanical behavior of provisional implant prosthetic abutments
2014
Introduction: Implant-supported prostheses have to overcome a major difficulty presented by the morphology and esthetics of peri-implant tissues in the anterior sector. Diverse therapeutic techniques are used for managing the mucosa adjacent to the implant and the most noteworthy is immediate/deferred fixed provisionalization. Objectives: In vitro testing of strength and deformation of implant prosthetic abutments made from different materials (Titanium/PEEK/methacrylate). Material and Methods: Forty Sweden&Martina® implant prosthetic abutments (n=40) were divided into five groups: Group MP: methacrylate provisional abutments with machined titanium base; Group PP: Poly ether ether ketone (P…
Influence of laser–target interaction regime on composition and properties of surface layers grown by laser treatment of Ti plates
2009
Surface laser treatment of commercially pure titanium plates was performed in air using two different Nd : YAG sources delivering pulses of 5 and 35 ns. The laser fluence conditions were set to obtain with each source either yellow or blue surface layers. Nuclear reaction analysis (NRA) was used to quantify the amount of light elements in the formed layers. Titanium oxinitrides, containing different amounts of oxygen and nitrogen, were mainly found, except in the case of long pulses and high laser fluence, which led to the growth of titanium dioxide. The structure of the layers was studied by x-ray diffraction and Raman spectroscopy. In addition, reflectance spectra showed the transition fr…
Comparison of spring characteristics of titanium-molybdenum alloy and stainless steel
2017
Background Titanium-molybdenum alloy (TMA) and stainless steel (SS) wires are commonly used in orthodontics as arch-wires for tooth movement. However, plastic deformation phenomenon in these arch-wires seems to be a major concern among orthodontists. This study aimed to compare the mechanical properties of TMA and SS wires with different dimensions. Material and Methods Seventy-two wire samples (36 TMA and 36 SS) of three different sizes (19×25, 17×25 and 16×22) were analyzed in vitro, with 12 samples in each group. Various mechanical properties of the wires, including spring-back, bending moment and stiffness were determined using a universal testing machine. Student’s t-test showed statis…
The multi-effects of K2TiF6 additive on the properties of PEO coatings on AZ31 Mg alloy
2020
Abstract Plasma electrolytic oxidation of AZ31 Mg alloy was performed in an alkaline silicate-based solution containing various concentrations of K2TiF6 using unipolar waveform at a constant voltage. The surface morphology of all coatings was rough and contained a micro-pore network, micro-cracks, and granules of oxide compounds in different diameters and micro-pore levels. The coating is composed of MgO, MgF2, Mg2SiO4, SiO2 (amorphous), and TiO2 (crystalline and amorphous) phases. The average thickness of the coatings was increased by adding the K2TiF6, where EDS results showed that a skinny fluoride-rich passive layer forms. With increasing time and reaching the final potential, the TiO2 …
Effect of alloy type and casting technique on the fracture strength of implant-cemented structures.
2010
Objectives: To evaluate the influence of alloy type and casting procedure on the fracture strength (FS) of metallic frameworks for implant-supported fixed prostheses. Study design: Thirty three-unit structures for lower posterior bridges were waxed-up and randomly assigned to two groups (n=15) according to alloy type and casting technique: Group 1 (C): cobalt-chromium cast in a centrifugal machine (TS1, Degussa-Hüls); Group 2 (T): titanium cast in a pressure-differential device (Cyclarc II, Morita). Each structure was cemented onto two prefabricated abutments under a constant seating pressure. After 6 months of water aging, samples were loaded in a static universal testing machine (EFH/5/FR…
Osseointegration of one-piece zirconia implants compared with a titanium implant of identical design: a histomorphometric study in the dog
2010
Objective: The aim of this study was to evaluate osseointegration of one-piece zirconia vs. titanium implants depending on their insertion depth by histomorphometry. Material and methods: Four one-piece implants of identical geometry were inserted on each side of six mongrel dogs: (1) an uncoated zirconia implant, (2) a zirconia implant coated with a calcium-liberating titanium oxide coating, (3) a titanium implant and (4) an experimental implant made of a synthetic material (polyetheretherketone). In a split-mouth manner they were inserted in submerged and non-submerged gingival healing modes. After 4 months, dissected blocks were stained with toluidine blue in order to histologically asse…
Luminescence of X-ray induced radiation defects in modified lithium orthosilicate pebbles with additions of titanium dioxide
2017
The authors greatly acknowledge the technical and experimental support of O. Leys, M. H. H. Kolb, and R. Knitter (Karlsruhe Institute of Technology, Germany). The work is performed in the frames of the University of Latvia financed project No. Y9-B044-ZF-N-300, “Nano, Quantum Technologies, and Innovative Materials for Economics”.
Growth of titanium oxynitride layers by short pulsed Nd:YAG laser treatment of Ti plates: Influence of the cumulated laser fluence.
2009
International audience; Titanium oxynitride layerswere formed by surface laser treatment of Ti plates in air using a Nd:YAG laser source of short pulse duration about 5 ns. The cumulated laser fluence was varied in the 100–1200 J cm2 range and its influence on the composition and the structure of the formed layers was studied by different characterization techniques providing physico-chemical and structural information. It was shown that the laser treatment induces the insertion of light elements as O, N and C in the formed layer with the amount increasing with the laser fluence. The in-depth composition of the layers and the co-existence of different phases were also studied. The way in wh…