Influence of design mistakes and material degradation on the collapse of a long-span RC roof in South Italy
2020
Abstract In 2004, during ordinary maintenance work, consisting in the waterproofing of a building located in the South of Italy, the long-span (14.50 m) in situ cast reinforced concrete (RC) roof partially collapsed. The building, constructed in 1950, was in service as a cinema up to 1967 and utilized as a school up to 1985. Finally, it was a hotel up to 2000. In 2004, when the building was not in service and underwent maintenance work, it partially collapsed under the dead load. After the collapse, which involved a large portion of the roof, several beams and two columns, the Court nominated a first Official Technical Consultant in order to investigate on the causes of failure and related …
Analysis of a Collapsed Long-Span Reinforced Concrete Roof in South Italy: Design Mistakes and Material Degradation
2020
In 2004, during ordinary maintenance work, consisting of waterproofing a building located in the south of Italy, the long-span (14.5 m) in situ RC roof partially collapsed. The building, constructed in 1950, was in service as a cinema until 1967 and then utilized as a school until 1985. Lastly, it was a hotel until 2000. In 2004, when the building was not in service and was undergoing maintenance work, it partially collapsed under dead load. After the collapse, which involved a large portion of the roof, several beams, and two columns, the Italian court nominated an official technical consultant to investigate the direct and related causes of the failure. After the main causes were identifi…
Assessment of protection treatments for carbonatic stone using nanocomposite coatings
2020
In this paper the effect of the application of four kinds of polymer dispersions containing nanoparticles, used as protectives, on two type of carbonatic lithotypes, White Noto and Comiso stone, is reported. The study was conducted by analysing the contribution of each component of the system. After the structural characterization of the coating itself, the performance of those colloidal systems has been studied upon application on the calcarenites, preferring non-invasive techniques and microdestructive techniques. Effect of the nanoparticles presence on hydrorepellency and roughness of the stone surface and on chromatic changes has also been considered. The tests conducted have proven tha…