Urea Glass Route as a Way to Optimize YAGG:Ce3+,Cr3+,Pr3+ Nanocrystals for Persistent Luminescence Applications

2022

A new approach for the synthesis of Y3Al2Ga3O12 (YAGG) nanophosphors allowing the preparation of crystallites with sizes starting from 45 nm is presented. The controllability of the energy and trap density of the resulting material samples by annealing temperature was confirmed by thermoluminescence (TL) measurements. It has been shown that the annealing of samples at temperatures up to 1300 degrees C does not cause any substantial growth of crystallites, still remaining below 100 nm, but leads to changes in the activation energy of the persistent luminescence (PersL) process. On the other hand, annealing above 1400 degrees C results in grain growth on the submicron scale, which was confirm…