Electrodeposition of supported gadolinium-doped ceria solid solution nanowires
2012
Gadolinium-ceria solid solution nanowires with tunable composition have been prepared through template cathodic electrodeposition from solutions containing Ce 3+Gd 3+ in a variable ratio. The employed template is Porous Anodic Alumina because it can function as thermal resistant separator supporting the nanowires if used as ionic conductor in Solid Oxide Fuel Cell (SOFC). Scanning Electron Microscopy of the deposited nanostructures revealed that the use of ethanol as solvent and metal chloride as electrolyte allowed to prepare continuous, compact and well defined nanowires with morphological features stable even after thermal treatment. EDX compositional analysis confirms the presence of bo…
Room temperature electrodeposition of photoactive Cd(OH)2 nanowires
2009
Cd(OH)2 nanowires (NWs) were successfully prepared by room temperature electrogeneration of base using Cd(NO3)2 aqueous electrolyte and Anodic Alumina Membrane (AAM) as template. Cd(OH)2 films have been also deposited on tin-doped indium oxide (ITO) for comparison. SEM analysis shows high quality deposits made of closely packed nanowires (NWs) into AAM and uniform flake-like surface on ITO. XRD analysis reveals that Cd(OH)2 films on ITO are polycrystalline, while the nanowires grow along the preferential directions [100] and [110]. Photoelectrochemical measurements show that Cd(OH)2 NWs are photoactive materials with indirect and direct band gap of 2.15 and 2.75 eV, respectively. Keywords: …
Nucleant layer effect on nanocolumnar ZnO films grown by electrodeposition
2013
Different ZnO nanostructured films were electrochemically grown, using an aqueous solution based on ZnCl2, on three types of transparent conductive oxides grow on commercial ITO (In2O3:Sn)-covered glass substrates: (1) ZnO prepared by spin coating, (2) ZnO prepared by direct current magnetron sputtering, and (3) commercial ITO-covered glass substrates. Although thin, these primary oxide layers play an important role on the properties of the nanostructured films grown on top of them. Additionally, these primary oxide layers prevent direct hole combination when used in optoelectronic devices. Structural and optical characterizations were carried out by scanning electron microscopy, atomic for…
Anodic Electro Deposition of CeO2 and Co-Doped CeO2 Thin Films
2013
CeO2 and Co containing CeO2 thin films were deposited on indium tin oxide and stainless steel by anodic electrodeposition. Scanning electron microscopy showed that the films are flat and show globular morphology and cracks resulting from volume shrinking. According to XRD and Raman Spectroscopy pure ceria layers are crystalline, while the presence of Co induces the formation of amorphous films. The good adhesion and the compactness allowed the photoelectrochemical characterization of the films. A band gap value of 2.9 eV was estimated for CeO2, while slightly higher values (̃3.0 eV) were estimated for Co containing films. A mechanism for ceria anodic electrodeposition is proposed and discus…
Nanostructured Material Fabrication for Energy Conversion
2011
The electrochemical deposition is a suitable via to fabricate nanostructured materials for energy conversion, and for other purposes. This paper deals with the electrochemical synthesis of nanostructured alloys and ruthenium oxide, which can be used in Li-ion batteries and polymer electrolyte membrane electrolyzers.
Template electrosyntesis of CeO2 nanotubes
2007
Nanotube arrays of CeO2 were produced in a single step by potentiostatic electrochemical deposition from a non-aqueous electrolyte, using anodic alumina membrane templates. The CeO2 nanotubes showed a polycrystalline structure, and they were assembled in the membrane nanochannels. The nanotubes had somewhat uniform diameters, with an average external value of about 210 nm, and a maximum length of about 60 µm; the latter parameter was controlled by the electrodeposition time. Each single nanotube was found to consist of crystalline grains having a size of about 3 nm. Raman analysis shows that these CeO2 nanotubes are suitable for catalytic applications.