Sb Effect on Structural, Dielectric, and Ferroelectric Properties of Na0.5K0.5NbO3Ceramics
2015
Lead-free Na0.5K0.5(Nb1-xSbx)O3 (0<x<0.05) ceramics were fabricated by the solid-state reaction method and materials with more than 95% densification were obtained. A microstructure study confirms that the ceramics are well sintered. All compositions show complete perovskite solid solutions. Structural, dielectric and ferroelectric investigations for these specimens were performed. X-ray measurements showed that all compositions have a single perovskite structure with orthorhombic symmetry. Dielectric study revealed that the ceramics obtained are normal ferroelectrics. However some signs of diffuse phase transition were observed. The transition temperatures and the maximum electric permitti…
Uniaxial stress dependence of the dielectric and ferroelectric properties of the Na0.5K0.5NbO3and Na0.5K0.5NbO3 + 0.5 mol%MnO2ceramics
2013
Na0.5K0.5NbO3 and Na0.5K0.5NbO3 + 0.5 mol%MnO2 lead-free ceramics have been produced by solid phase hot pressing sintering process at 1120–1145°C. The results of the X-ray diffraction measurements showed that the obtained samples possessed a perovskite structure. The micrograph of the fractured surface showed a dense ceramic structure, in compliance with 93% relative density determined by the Archimedes method. The dependence of dielectric and ferroelectric properties on the uniaxial compressive stress (0–3000 bar) of the Na0.5K0.5NbO3 and Na0.5K0.5NbO3 + 0.5 mol%MnO2 ceramics was investigated. Significant influence of the external stress on these properties was revealed. It includes a shif…
Bias Field Effect on Dielectric Response in the Region of Phase Transitions in (Pb,La)(Zr,Sn,Ti)O3Ceramics
2007
The dielectric response of (Pb 0.97 La 0.02 ) (Zr 0.53 Ti 0.12 Sn 0.35 )O 3 (PLZTS-2/53/12/35) ceramics was measured as a function of DC bias field E =. As the bias field intensity increases the values of ϵ′ max and ϵ” max are found to shift towards a lower temperature. A possible coexistence of the ferroelectric and antiferroelectric phases over a wide range of temperatures in the PLZTS-2/53/12/35 samples is assumed to explain the observed features of ϵ′ (T), ϵ” (T), and ϵ′ (E=) curves.
Influence of Compressive Stress on Dielectric and Ferroelectric Properties of the Na0. 5K0.5NbO3, Na0.5K0.5(Nb0.94Sb0.06)O3and Na0.5K0.5(Nb0.94Sb0.06…
2013
Good quality lead-free ceramics of Na0.5K0.5NbO3, Na0.5K0.5(Nb0.94Sb0.06)O3 and Na0.5K0.5(Nb0.94Sb0.06)O3 +0.5mol%MnO2 have been produced by a solid phase hot pressing sintering process at 1120–1145°C. The dependence of dielectric and ferroelectric properties on the uniaxial pressure (0–3000 bar) of the these samples was investigated, revealing a significant influence of the external stress on their properties. This includes a shift of the phase transition, a diffuseness of the permittivity characteristics, a change of the dielectric dispersion and a decrease of the polarization. We discuss our results based on hardening of the soft-mode and domain switching processes under applying of pres…
The physical mechanisms of relaxation times distribution in inorganic and organic disordered ferroelectrics
2007
Abstract We discuss the physical background for relaxation times distribution in organic and inorganic disordered ferroelectrics. We show that such background is a disorder which is believed to be a reason for relaxor behavior. Due to this disorder the internal electric and elastic fields are of a random nature being characterized by certain distribution function. Having the distribution function f ( E ) of random field E , we can obtain the distribution function of relaxation times F ( τ ) with the help of relation between τ and E . Latter relation can be obtained considering the dynamics of a single electric dipole in a random field created by the ensemble of defects and impurities in a s…
SrTiO3and Pr Effects on Structural, Dielectric and Ferroelectric Properties of Na0.5Bi0.5TiO3Ceramic
2015
[(Na0.5Bi0.5TiO3)0.7Sr0.3]1-xPrxTiO3(NBTS30P) (0 ≤ x ≤ 0.025) ceramics were prepared by solid-state synthesis process. Their crystal structure, microstructure dielectric and ferroelectric properties were studied. XRD data show that all of the ceramics possess a single perovskite phase. SEM results confirm that the ceramics are well sintered and exhibit relative densities higher than 97%. The results also reveal that the microstructure of the different compositions do not show a significant variation. The praseodymium (Pr) substitution to NBTS30 results in a change of crystal structure from cubic to tetragonal at x = 0.025. At the same time, electric permittivity decreases, the maximum is br…
INFLUENCE OF ZIRCONIUM ON STRUCTURAL, MICROSTRUCTURAL AND FERROELECTRIC PROPERTIES OF BaZr0.20Ti0.80O3 CERAMIC
2009
ABSTRACT Barium zirconium titanate BaZrxTi1-xO3 ceramics have been obtained by conventional method. The X-ray diffraction analysis showed that the BaZr0.20Ti0.80O3 crystallizes in the cubic structure. The lattice parameter a increases with temperature, at temperature ∼308 K a small deviation is observed. The performed EDS study revealed that the samples were perfectly sintered and that the material was chemically homogeneous. It contains a little glassy phase and the grains are well shaped. The zirconium content (20 mol%) in the examined solid solution caused downward shift of the temperature T m . The increase of the achieved permittivity values ϵm was observed as well.
Proton glass behavior and hopping conductivity in solid solutions of antiferroelectric betaine phosphate and ferroelectric betaine phosphite.
1991
Measurements of the dielectric permittivity are reported for solid solutions of antiferroelectric betaine phosphate and ferroelectric betaine phosphite at frequencies 10 −2 Hz T c the dielectric response is dominated by ac and dc conduction. The 40% sample exhibits pure relational behavior indicative of a transition into an orientational glass state
Dielectric Properties of PbSc1/2Nb1/2O3-PbTiO3Ceramics
2004
Lead titanate solid solutions exhibits extreme values of some physical parameters. We have investigated a ferroelectric relaxor ceramics of PSN-PT composition near the morphotropic phase boundary. Results are discussed with account for the relaxor properties related to defects and disordering of the PSN-PT system.
Low and Infra-Low Frequency Measurements in Lead Titanate Solid Solutions
2006
The study of PSN-PT ferroelectric relaxor ceramics exhibiting extreme values of some physical parameters near the morphotropic phase boundary is reported. The results are discussed to account for the relaxor properties related to defects and disordering of the PSN-PT system.