Engineering the crack path in lattice cellular materials through bio-inspired micro-structural alterations
2019
Abstract A computational study on the fracture behaviour of bio-inspired finite-size lattice configurations is performed in this work. The study draws inspiration from recent investigations aimed at increasing the fracture energy of some materials through small modifications of their microstructure. The main question here is whether it is possible, to some extent, to engineer the crack path in metallic cellular materials through such small micro-structural modifications and how to quantify the effect of alternative strategies. Nature provides several examples of strategies used to delay or arrest damage and crack propagation. One striking example is given by the micro-architecture of severa…
Prediction of crack onset strain in composite laminates at mixed mode cracking
2009
Failure process of continuous fiber reinforced composite laminates in tension usually starts with appearance of intralaminar cracks. In composite laminates with complex lay-ups and/or under combined loading, intralaminar cracks may develop in plies with different reinforcement directions. A necessary part of mixed mode cracking models is the criterion of failure. For propagation-controlled fracture it is usually formulated in terms of energy release rates and their critical values of the particular composite material. Intralaminar fracture toughness of unidirectionally reinforced glass/epoxy composite was experimentally determined at several mode I and mode II ratios. It is found that the c…
Crack growth models for multiaxial fatigue in a ship’s propeller shaft
2021
Abstract A premature fatigue failure of a large intermediate propeller shaft in a shuttle tanker is discussed and analyzed. The short fatigue life consists mainly of a crack growth phase. Life predictions are carried out by crack growth modelling based on engineering fracture mechanics. The purpose of the present investigation is to identify the most likely loading modes based on the evolution of the crack propagation. A Linear Elastic Fracture Mechanics Model (LEFM) is applied with the stress intensity factor range entering the Paris law as a key parameter. Existing formulas for the geometry functions are supplemented by more detailed stress intensity factor calculations pertaining to smal…
Molecular-dynamics study of mechanical properties of copper
1998
Mechanical properties of copper have been studied using effective-medium theory and Molecular-Dynamics simulations. At room temperature we calculate the tensile moduli of systems that are elongated along different crystal orientations. These moduli are in very good agreement with the experimental values, the difference being less than 6%. The elastic constants obtained from simulations were also in good agreement with experiments. In addition, the point of maximum stress is found to be of the same order of magnitude as the experimental value. Also crack propagation in systems with periodic boundaries has been studied and micro-voids are seen to generate near the crack tip. Crack propagation…
Evaluation of the fracture performance of different rubberised bitumens based on the essential work of fracture
2017
The fracture performance of rubberised bitumen in addition to one pre-treated with a Warm Mix Additive (Sasobit®) was investigated using different test methods measuring different damage mechanisms. Two Recycled Tyre Rubber (RTR) modifiers together with two base binders were blended in the laboratory to produce various combinations of Recycled Tyre Rubber Modified Bitumens (RTR-MBs). The first RTR is a standard recycled polymer derived from discarded truck and passenger car tyres by ambient grinding. The second RTR consists of 100% recycled truck tyres derived by cryogenic grinding and pre-treated with special oil and WMA to allow further decrease of asphalt mixture production temperatures.…
Fatigue crack growth in 2024-T351 Friction Stir Welded Joints: longitudinal residual stresses and microstructural effects
2009
Abstract The role of longitudinal residual stress on propagation of fatigue cracks was examined in friction stir welds produced in 2024-T351 aluminum alloy. Fatigue crack growth rate was obtained through constant Δ K Iapp tests for notches at different distances from the weld centerline. Subsequently, crack growth was correlated to weld residual stress measured by the cut-compliance method. It was found that residual stresses correspond to low crack growth rates outside the weld zone during fatigue loading. Once in the weld zone, the crack growth was affected by microstructural and hardness changes. Furthermore, weld residual stresses were mechanically relieved and effects on crack propagat…
Damage in composites : from physical mechanisms to modelling
2006
International audience; The most critical types of damage in composite materials are transverse cracking, delamination and fiber breaking. The simulation of the behaviour and the rupture of these materials shows that it is important to consider failure mechanism in the design of structures. Each mechanism induces local deteriorations which can be accelerated when they are coupled with other mechanisms. Global criteria are unable to predict neither these processes nor their interactions. This paper is an attempt to propose realistic criteria which are the witness of local degradations and can be used for the design of composite structures.
Numerical analysis of a piezoelectric structural health monitoring system for composite flange-skin delamination detection
2013
Abstract In this paper, a piezoelectric based Structural Health Monitoring (SHM) system is proposed to detect skin/stiffener debonding and delamination cracks proper of laminated composite structures. The SHM system is analyzed by means of a boundary element code implemented in the framework of piezoelectricity. The multidomain technique, coupled with an interface spring model, is used to model laminated composite structures as well as the bonding between the host delaminated structure and the piezoelectric sensor. Static sensitivity analyses are firstly performed on a drop-ply delaminated structure in order to identify a suitable configuration for the sensor. Then, the dynamic electromecha…
Progressive cracking mastercurves of the transverse ply in a laminate
2009
In this study, progressive cracking of a transverse layer in a cross-ply composite laminate subjected to tensile loading is considered. Using the results of a probabilistic cracking model, approximate relations for crack density as a function of stress are derived for initiation-controlled and propagation-controlled cracking. It is shown that the crack density evolution in the transverse ply can be represented by a mastercurve in suitably normalized coordinates. The mastercurve approach is applied to progressive cracking in glass/epoxy laminates. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers
Model of delamination propagation in brittle-matrix composites under cyclic loading
2001
A model of interlaminar fatigue crack growth based on damage accumulation ahead of the crack is proposed. Linear cumulative assumption is used for damage estimation, and a quadratic failure criterion is applied for complex interlaminar loading. Model parameters are determined from mode I and mode II fatigue tests, and used to predict mixed-mode delamination propagation rate. Comparison of theoretical prediction with mixed-mode test results for different brittle graphite FRP at several mode- and load ratios show reasonable agreement.