EPR in glass ceramics
2019
Abstract The development of novel materials requires a profound understanding of the relationship between a material's performance and its structural properties. Electron paramagnetic resonance (EPR) is a well-established technique for a direct detection and identification of paramagnetic defects in solids. This chapter provides an overview of the applicability of continuous wave EPR spectroscopy in the studies of glass ceramics focusing on transition metal (Mn2 +, Cu2 +, Cr3 +) and rare earth (Gd3 +, Eu2 +, Er3 +, Yb3 +) ion local structure analysis. EPR spectra features of the above-mentioned paramagnetic probes in glasses and glass ceramics are compared and discussed in detail. The chapt…
High sensitivity characterization of the nonlinear electric susceptibility of a glass ceramic in the microwave range
2019
The nonlinear electric susceptibility of a glass ceramic is characterized in the microwave range by measuring intermodulation of two high-power signals. To achieve the necessary sensitivity for dielectric nonlinearities, the setup ensures that the measured intermodulation can be ascribed to the material under test while all other intermodulation sources are suppressed. This is achieved by coupling three dielectric resonators in a cut-off waveguide. The third order nonlinearity of the glass ceramic is found to be χ3/er = (1.6 ± 0.8) × 10−15 m2/V2 at 950 MHz. The magnitude is comparable to the previously measured high-end sintered ceramics. The power of the intermodulation signal as a functio…
Mechanism of crystallization of fast fired mullite-based glass–ceramic glazes for floor-tiles
2006
Abstract The mechanism of crystallization from a B 2 O 3 -containing glass, with composition based in the CaO–MgO–Al 2 O 3 –SiO 2 system, to a glass–ceramic glaze was studied by different techniques. Glass powder pellets were fast heated, simulating current industrial tile processing methods, at several temperatures from 700 to 1200 °C with a 5 min hold. Microstructural study by field emission scanning electron microscopy revealed that a phase separation phenomenon occurred in the glass, which promoted the onset of mullite crystallization at 900 °C. The amount of mullite in the glass heated between 1100 and 1200 °C was around 20 wt%, as determined by Rietveld refinement. The microstructure …
Effect of boron oxide on the microstructure of mullite-based glass-ceramic glazes for floor-tiles in the CaO–MgO–Al2O3–SiO2 system
2006
Abstract The effect of increasing replacement of Al2O3 by B2O3 in a parent glass on the sintering and further crystallization of mullite was investigated. The composition of the parent glass was chosen in the mullite primary phase field of the CaO–MgO–Al2O3–SiO2 quaternary system. Glass powder pellets were heated under standard (10 °C/min and 2 h of hold time) and fast heatings (25 °C/min and 5 min of hold time) at different temperatures from 700 to 1190 °C. Sintering of B2O3-containing glasses took place in the range between 850 and 1050 °C. X-ray diffraction results showed that mullite formed as unique crystalline phase for glasses containing amounts of B2O3 larger than 6 wt%. For lower a…
Ni-containing spinel aluminates glass-ceramic materials obtained from cordieritic bulk glasses
2003
Monolithic glasses with compositions 2MO � 2Al2O3 � 5SiO2, being M ¼ Ni and equimolar mixtures of Ni and Mg, were prepared at 1650 C by melting mixtures of raw materials. The crystallization of monoliths was produced by heattreatment at several temperatures up to 1200 C. The crystallization sequence was followed by differential thermal analysis (DTA), X-ray powder diffraction (XRD), field emission scanning electron microscopy (FESEM) and energy dispersive X-ray (EDX) and diffuse reflectance spectroscopies. Surprisingly, the only crystalline phase formed after heating up to 1100 C was a nickel-containing aluminate spinel for both compositions. The microstructural characterization indicated t…
Effect of some additives on the development of spinel-based glass-ceramic glazes for floor-tiles
2005
Abstract The feasibility of developing spinel-based glass-ceramic glazes from a glass with composition in the system ZnO–MgO–B 2 O 3 –Al 2 O 3 –SiO 2 was examined. To do it additional fluxes and/or nucleants were added to a parent glass before melting. Pressed pellets of powdered glasses were submitted to standard thermal treatments up to 1200 °C. The crystallization path and the microstructural development at several temperatures were followed by several experimental techniques. The results showed that additions of TiO 2 as nucleant or additional B 2 O 3 as flux to the chosen glass favored the crystallization of cordierite or mullite as main crystalline phase. Glasses which also contained …
Phase transformation in a glass-ceramic observed by laser spectroscopy
1988
The influence of thermal treatment on a (Li2O∶Al2O3∶ SiO2) glass ceramic is studied by laser spectroscopy. At temperatures above 800 °C a fluorescence of Cr3+ ions around 693 nm appears which indicates the growth of crystallites where the Cr3+ ions occupy sites similar to those in Al2O3.
Evolution of the structural and optical properties from cobalt cordierite glass to glass-ceramic based on spinel crystalline phase materials
2007
Co 2+ -containing cordierite stoichiometric glasses have been prepared by melting colloidal gel precursors. After controlled thermal processing in the range of temperatures between 900 and 1300 C different polycrystalline, almost single phase materials displaying l-, a-, and b-cordierite crystalline forms were synthesized. In addition, spinel glass-ceramic materials were also prepared from the base glasses. All these materials were characterized by X-ray powder diffraction and infrared spectroscopy. Room temperature (RT) absorption and emission spectra of Co 2+ – cordierites and – spinel-glass material have allowed determining the local environment of the Co 2+ in the crystalline structure …
Mechanism of crystallization of pyroxene-based glass-ceramic glazes
2004
Abstract The mechanism of crystallization of a powdered glass with composition in the pyroxene crystallization primary field within the CaO–MgO–Al 2 O 3 –SiO 2 quaternary system and containing some additives was studied. The crystallization sequence was compared with that from the same base glass without additives. After a short thermal anneal both powdered glasses showed phase separation. Further thermal treatment gave rise to the crystallization of pyroxene. Anorthite as secondary crystalline phase was also detected in the quaternary glass (without additives). The starting crystallization in the glass with additives took place in the outer surface of glass particles probably in the immisc…
Degree of conversion and microhardness of resin cements photoactivated through glass ceramic
2021
Background To assess whether glass-ceramic shade, thickness and translucency affect degree of conversion (DC) and Knoop microhardness (KHN) of resin cements photoactivated using light-emitting diode (LED) or quartz-tungsten-halogen (QTH) units. Material and Methods Glass-ceramic blocks were cut (2, 3 and 4mm) and sintered. For DC FT Raman spectroscopy (n=3), film specimens of cements (RelyX ARC, U200, Veneer, C&B) were obtained. For KHN test (n=3), cements were inserted in cylindrical matrix and covered by polyester strip. Specimens were photoactivated (30s) using LED or QTH according to each group: direct photoactivation (DP), interposing ceramic specimens or no photoactivation (NP). Data …