Background Subcutaneous specific immunotherapy (SCIT) has proven sustained clinical efficacy against allergy. The recommended regimen for SCIT is a gradual updosing over a period of weeks. Commonly, in commercial products for SCIT, the specific allergen is formulated with an adjuvant, most often in the form of aluminium hydroxide (AlOH). It has been shown that allergen-specific IgG antibodies are induced as a result of successful SIT. Objective To investigate the possibility of optimizing the formulation of AlOH-based grass-pollen allergy vaccines for SCIT in a way that allows for shorter updosing regimens while maintaining the immunogenicity of the vaccine. Methods Mice were immunized with…
Co-precipitation synthesis of Nd:YAG nano-powders: the effect of Nd dopant addition with thermal treatment
2007
Nanopowders of Yttrium Aluminium Garnet doped with neodymium ions were obtained by the co-precipitation method from the reaction of aluminium, yttrium and neodymium nitrate with ammonia. The amount of neodymium was selected in order to produce samples of nominal stoichiometry NdXY (3-X)Al5O12 (where X = 0.006, 0.012, 0.024, 0.048, 0.081, 0.096, 0.17, 0.19, 0.38, 0.54, and 0.72, respectively). After washing and drying, the hydroxide precursors were subjected to Thermo-Gravimetry and Differential Thermal Analysis experiments from room temperature up to 1500 °C, which showed the presence of exothermal events accompanying phase transformation phenomena. X-ray diffraction investigations conducte…
Determination of low-molecular-mass aliphatic carboxylic acids and inorganic anions from kraft black liquors by ion chromatography.
2007
An ion chromatographic (IC) method with suppressed conductivity detection (CD) was developed and validated for the quantitative determination of several low-molecular-mass aliphatic mono- and dicarboxylic acids as their carboxylate anions together with some inorganic anions (chloride, sulfate, and thiosulfate) from kraft black liquors. To confirm the identification of some carboxylate anions which lack commercial model substances, a qualitative IC method with suppressed electrospray ionization mass spectrometry (ESI-MS) was also developed. The separations were performed on an IonPac AS 11-HC anion-exchange column operated at 25 degrees C within 25 min by a gradient elution with aqueous pota…
Hydrogen-bond tuning of ferromagnetic interactions: synthesis, structure and magnetic properties of polynuclear copper(ii) complexes incorporating p-…
2006
The reaction of copper(II) hydroxide with 2,2'-bipyridine (bipy) (1 : 1) in alkaline aqueous solution (pH 14) at room temperature affords the alternating carbonate/hydroxo-bridged copper(II) polymeric chain compound {[Cu3(bipy)3(mu-OH)2(mu-CO3)2].11H2O}n, 1, as determined by single-crystal X-ray diffraction. The structure of 1 is built up from two similar centro-symmetric dinuclear [(bipy)Cu(mu-OH)]2 cores which link together via bridging carbonate groups to mononuclear [(bipy)Cu] fragments to form the chain. Interdigitation of adjacent chains through pi-pi interactions, which involve each bipy ligand, forms sheets that are separated by the water molecules of crystallisation. Variable-tempe…
Characterization of Zirconium Phosphate/Polycation Thin Films Grown by Sequential Adsorption Reactions
1997
Monolayer and multilayer thin films consisting of anionic α-zirconium phosphate (α-ZrP) sheets and polycations (poly(allylamine hydrochloride) (PAH), cytochrome c) were characterized by transmission electron microscopy (TEM), ellipsometry, UV−visible absorbance spectroscopy, reflectance FT-IR, XPS, and X-ray diffraction. Titration and powder X-ray diffraction experiments confirm that exfoliation of α-ZrP begins to occur when enough tetra(n-butylammonium) hydroxide (TBA+OH-) has been added to exceed single-layer packing of TBA+ ions (x ≈ 0.50) in the intercalation compound Zr(HPO4)2-x(TBA+PO4-)x·nH2O. The identical contrast of many sheets in TEM micrographs suggests that the suspension is un…
Original Supercritical Water Device for Continuous Production of Nanopowders
2011
Well-crystallized ZnO, ZrO2, TiO2, CeO2, Y2O3 and La2O3 nanoparticles are synthesized under supercritical water conditions (T > 647 K and P > 22.1 MPa) using a home-made continuous process. At room temperature, metallic salts with or without aqueous hydroxide solution (KOH or NaOH) are pressurized to 25–30 MPa. Then, the reactant(s) is/are rapidly heated to 673–773 K by mixing with the supercritical water in a patented reactor. Residence time is in the range from 2 to 8 s. XRD, TEM and surface area analyses highlight the production of pure and well-crystallized nanoparticles with a uniform size distribution.
Synthesis of phenol–formaldehyde resole resins in the presence of tetraalkylammonium hydroxides as catalysts
2000
Abstract We synthesised phenol–formaldehyde resole resins in the presence of tetraalkylammonium hydroxides as catalysts. The activity of these catalysts was compared with the activity of sodium hydroxide. Gas chromatography, thin layer chromatography, 13 C NMR spectrometry, potentiometric titration and a few simple physicochemical methods were used to estimate the composition of the obtained resins and their properties. It was concluded from these studies that tetraalkylammonium hydroxides are active catalysts and the resins obtained in their presence show some interesting properties.
29Si NMR and Small-Angle X-ray Scattering Studies of the Effect of Alkaline Ions (Li+, Na+, and K+) in Silico-Alkaline Sols
1999
Alkali−silica reactions (ASR) which occur in concrete can be simulated in laboratory by destabilization of silico-alkaline aqueous solutions by addition of calcium ions. The relevant features of the reaction depend on the nature of alkaline ions (Li+, Na+, or K+) and on the silica/alkaline ratios which fix the distribution of the molecular species in the precursor solution. 29Si NMR spectroscopy and small-angle X-ray scattering (SAXS) techniques were used to study the structure and size distribution of molecular and colloidal species in sols with different silica/alkaline molar ratio and several types of alkaline ions. Experimental SAXS curves were simulated using a simple structural model …
Halloysite Nanotubes Loaded with Calcium Hydroxide: Alkaline Fillers for the Deacidification of Waterlogged Archeological Woods
2018
A novel green protocol for the deacidifying consolidation of waterlogged archaeological woods through aqueous dispersions of polyethylene glycol (PEG) 1500 and halloysite nanotubes containing calcium hydroxide has been designed. First, we prepared functionalized halloysite nanotubes filled with Ca(OH)2 in their lumen. The controlled and sustained release of Ca(OH)2 from the halloysite lumen extended its neutralization action over time, allowing the development of a long-term deacidification of the wood samples. A preliminary thermomechanical characterization of clay/polymer nanocomposites allows us to determine the experimental conditions to maximize the consolidation efficiency of the wood…