Moisture Absorption Effects on the Resistance to Interlaminar Fracture of Woven Glass/Epoxy Composite Laminates
2012
The influence of moisture absorption on the interlaminar fracture behaviour of 8/8 harness satin weave glass/epoxy composite was investigated. Two series of specimens with 0°/0° and 90°/90° predominant interfaces immersed in water for different duration were tested under double cantilever beam (DCB mode I), single leg bending (SLB mode I + II) and end notched flexural (ENF mode II) loadings. In general, the apparent flexural modulus: E, and the fracture toughness: G C, decrease with increasing moisture content. This effect is more remarkable if mode II participation is bigger. The value of G C measured on 90°/90° specimens reveals higher than that on 0°/0° ones, but the variation in G C is …
Bearing strength and failure behavior of pinned hybrid glass-flax composite laminates
2018
Abstract The aim of the present work is to evaluate the influence of external layers of glass woven fabric on the pin-hole strength of flax/epoxy laminates. Single lap bearing tests were carried out to evaluate the fastened joint performances depending on laminate stacking sequence. In order to better identify the mechanical behavior of the hybrid laminate, full glass and flax laminates were also compared. In particular, bearing stress and failure mechanisms were investigated at varying joint geometry. Furthermore, an experimental failure map, clustering main failure modes of pinned hybrid composite laminate, was used to better clarify the relationship between mechanical failure and geometr…
Mechanical characterization of rose bengal and green light crosslinked collagen scaffolds for regenerative medicine
2021
Abstract Collagen is one of the most important biomaterials for tissue engineering approaches. Despite its excellent biocompatibility, it shows the non-negligible disadvantage of poor mechanical stability. Photochemical crosslinking with rose bengal and green light (RGX) is an appropriate method to improve this property. The development of collagen laminates is helpful for further adjustment of the mechanical properties as well as the controlled release of incorporated substances. In this study, we investigate the impact of crosslinking and layering of two different collagen scaffolds on the swelling behavior and mechanical behavior in micro tensile tests to obtain information on its wearin…
Evolution of the bearing failure map of pinned flax composite laminates aged in marine environment
2020
Abstract Aim of the present paper is to evaluate how the bearing behavior of pinned flax composites can be influenced by their exposition to critical environment such as marine one. To this scope, flax fibers/epoxy pinned laminate was exposed up to 60 days to salt-fog environment, according to ASTM B 117 standard. In particular, samples having different hole diameter (D), laminate width (W), and hole center to laminate free edge distance (E) have been tested under single lap bearing tests at varying the aging exposition time. Following this procedure, an experimental 2D failure map clustering main failure modes was created by placing the experimental results in the plane E/D versus W/D rati…
Prediction of crack onset strain in composite laminates at mixed mode cracking
2009
Failure process of continuous fiber reinforced composite laminates in tension usually starts with appearance of intralaminar cracks. In composite laminates with complex lay-ups and/or under combined loading, intralaminar cracks may develop in plies with different reinforcement directions. A necessary part of mixed mode cracking models is the criterion of failure. For propagation-controlled fracture it is usually formulated in terms of energy release rates and their critical values of the particular composite material. Intralaminar fracture toughness of unidirectionally reinforced glass/epoxy composite was experimentally determined at several mode I and mode II ratios. It is found that the c…
A simplified predictive approach to assess the mechanical behavior of pinned hybrid composites aged in salt-fog environment
2020
Abstract Aim of this paper is to assess the predictive capabilities of a simplified theoretical approach on the failure load of aged pinned hybrid composites. In particular, the mechanical performances of glass-flax hybrid epoxy laminates exposed to salt spray fog environment, were used as input data in order to address the analytical model. Preliminarily, the relationship among mechanical performances, failure mechanisms, joint geometry and ageing time, was evaluated by double-lap joint tests on pinned samples at varying joint geometry and ageing time. The bearing and shear out limit stress of samples aged for 60 days under the salt-fog environment underwent a reduction of about 20% compar…
Boundary Element Method for Composite Laminates
2017
The boundary element method (BEM) is a numerical technique to solve engineering/physical problems formulated in terms of boundary integral equations. Composite laminates are assemblages of stacked different materials layers, generally consisting of variously oriented fibrous composite materials
Une methode générale de prévision du comportement viscoélastique des composites stratifiésGeneral methodology to predict viscoelastic behaviour of co…
2001
Resume On presente dans ce papier un outil ayant pour base la theorie classique des plaques et capable de prevoir le comportement viscoelastique d'un composite stratifie. Alors que la theorie initiale n'est valide que dans le cas ou le comportement des plis est elastique lineaire, on montre que lorsque le comportement des plis est viscoelastique il est encore possible de conserver l'avantage de la souplesse d'emploi et de mise en œuvre de cet outil largement utilisee par les industriels. Des comparaisons entre des resultats obtenus a l'aide de ce nouvel outil et des resultats experimentaux mais egalement avec des calculs par elements finis montrent la pertinence de la methode.
On nonlinear behavior in brittle heterogeneous materials
2006
Abstract Many modern fiber-reinforced composite materials are ‘brittle’, in the sense that their strain to failure under quasi-static loading is typically of the order of 1% when loaded in directions generally controlled by fiber fracture, and the energy-to-failure under the quasi-static loading curve is typically small. For this reason, analysis of these materials is typically done under assumptions of linear elasticity, usually for homogeneous materials or material layers in a laminate. This is in contrast to ‘ductile’ metal behavior in which elastic–plastic behavior is widely discussed. What is most remarkable is the fact that for long-term behavior, the situation is nearly reversed in m…
Experimental characterization of composite laminates under low-velocity multi-impact loading
2019
The use of composite materials undergoes a significant growth in many industries including aeronautic, railway, and automotive. Laminated composites are often subjected to severe loading conditions...