Search results for "nanoparticle"

Cr- and Sb-containing TiO 2 inorganic orange nano-pigments prepared by a relative long hydrocarbon chain polyol

2016

Abstract We report the preparation of a series of orange Cr- and Sb-containing TiO 2 nano-pigments by the polyol via using triethylenglycol (TEG). Poorly crystallized anatase nanopowders with nominal stoichiometric compositions Cr x Sb x Ti 1−2x O 2 , with 0 ≤ x ≤ 0.2, were obtained by heating at 180 °C a solution of antimony acetate, chromium acetylacetone and titanium butoxide in TEG. The transition temperature of the chromium- and antimonium-containing anatase nanoparticles into the rutile crystalline form occurred over the range of temperature between 500 and 650 °C, depending on the dopant amount. After annealing at 800 °C for short time the series of samples displaying the rutile stru…

Mesocrystalline Cr and Sb-codoped anatase visible-light-driven photocatalyst

2018

Abstract We report on the synthesis, characterization and visible-light-driven photocatalytic activity of mesocrystalline Cr- and Sb-codoped anatase nanoparticles. Discrete and morphologically well-defined assemblies of anatase nanoparticles sized below 100 nm × 50 nm were prepared by hydrothermal aging of aqueous solutions containing titanium alkoxide, chromium acetylacetonate, antimony acetate and triethanolamine (TEOA) as stabilizer. The as-prepared and TEOA-free doped nanoparticles showed similar crystallographic parameters and spectroscopic features. The incorporation of Cr and Sb dopant cations into the anatase nanoparticles was evaluated by Rietveld refinement of X-ray diffraction pa…

Reversible Photodoping of TiO2 Nanoparticles for Photochromic Applications

2018

Financial support from the Estonian Research Council (IUT2-25, IUT2-26, and PUTJD680) is gratefully acknowledged. This work was supported by the Academy of Finland (decision numbers 141481 and 286713) and by the EU through the European Regional Development Fund (Center of Excellence for Zero Energy and Resource Efficient Smart Buildings and Districts-ZEBE, 2014-2020.4.01.15-0016). Work is supported by the Latvian Academy of Sciences in the framework of FLPP (Plasmonic oxide quantum dots for energy saving smart windows, lzp-2018/1-0187).

Nanostructured Pt–TiO2 composite thin films obtained by direct liquid injection metal organic chemical vapor deposition: Control of chemical state by…

2015

Abstract Nanostructured Pt–TiO 2 composite thin films were synthesized by direct liquid injection metal organic chemical vapor deposition process, using trimethyl(methylcyclopentadienyl)platinum and titanium isopropoxide as precursors. Surface and cross-sectional morphologies obtained by scanning electron microscopy and transmission electron microscopy evidenced the uniform distribution of platinum nanoparticles in the TiO 2 matrix. At higher Pt content, the X-ray diffraction analysis showed that the face-centered cubic phase of platinum appeared together with an anatase TiO 2 structure. In addition, as far as the platinum chemical state is concerned, the co-deposition of TiO 2 and Pt allow…

Anatase nanoparticles boundaries resulting from titanium tetrachloride hydrolysis

2017

An important factor that governs solar energy transformation into electrical or chemical energy, when using nanoparticles-based devices, is the spatial location of traps limiting electron transport. Evidences have been presented indicating that the electron diffusion is strongly influenced by nanoparticle boundaries, whose characteristics depend on the particles preparation. In the present work we have studied the role of hydrated excess proton structures in the formation of anatase nanoparticles boundaries in samples prepared by TiCl4 hydrolysis at low temperature and strong acidic conditions. The samples, constituted by anatase nanocrystals but, mainly, by amorphous titania, are studied b…

Influence of Amorphous TiO2-x on Titania Nanoparticle Growth and Anatase-to-Rutile Transformation

2012

Amorphous TiO2-x formed together with precursors and anatase nuclei, during TiCl4 hydrolysis at soft conditions, influences both crystal growth and phase stability. The highly defective nanoparticles of anatase grow by reaction of their basic hydroxyls with acidic ones of TiO2 precursor species. The growth of anatase crystals, however, is affected by their interactions with simultaneously formed amorphous TiO2-x which increasingly covers the particles hindering the anatase-precursor contact. The interactions among anatase and amorphous and precursor components have been studied by H-1-MAS (magic angle spinning) NMR spectroscopy. The interaction between acid and basic hydroxyls favors the fo…

Step-by-Step Growth of HKUST-1 on Functionalized TiO2 Surface: An Efficient Material for CO2 Capture and Solar Photoreduction

2018

The present study reports on a simple preparation strategy of a hybrid catalyst, TiO2/HKUST-1, containing TiO2 anatase nanoparticles (NPs) with tailored morphology and photocatalytic activity coupled with a porous metal-organic framework (MOF), namely HKUST-1, as an advanced material for the CO2 photocatalytic reduction. In detail, TiO2/HKUST-1 catalyst was prepared via an easy slow-diffusion method combined with a step-by-step self-assembly at room temperature. The growth of crystalline HKUST-1 onto titania surface was achieved by functionalizing TiO2 nanocrystals, with phosphoesanoic acid (PHA), namely TiO2-PHA, which provides an intimate contact between MOF and TiO2. The presence of a cr…

Mesocrystalline anatase nanoparticles synthesized using a simple hydrothermal approach with enhanced light harvesting for gas-phase reaction

2018

Mesocrystalline TiO2 nanoparticles were synthesized using a hydrothermal approach. A simple two-step procedure at low temperature (<140 °C) allowed the nucleation of primary particles sized 2–4 nm and their subsequent assembly as almost spherical aggregates sized ≈20 nm. X-ray powder diffraction (XRD), Raman and X-ray photoelectron spectroscopy (XPS) studies, and HRTEM studies confirmed anatase as the unique TiO2 crystalline phase. The mesocrystalline structure of the anatase aggregates was clearly evidenced by HRTEM and SAED results. The mesocrystalline nanopowders exhibit a mesoporous structure with a surface area and pore volume of 63.5 m2 g−1 and 0.22 cm3 g−1, respectively. Ultraviolet …

2018

We report a novel multi-step method for the preparation of ordered mesoporous titania scaffolds and show an illustrative example of their application to solar cells. The method is based on (monolayer) colloidal nanosphere lithography that makes use of polystyrene nanoparticles organised at a water–air interface and subsequently transferred onto a solid substrate. A titania precursor solution (titanium(IV) isopropoxide in ethanol) is then drop-cast onto the monolayer and left to “incubate” overnight. Surprisingly, instead of the expected inverse monolayer-structure, a subsequent calcination step of the precursor yields an ordered monolayer of hollow titania nanospheres with a wall thickness …

Preparation and photoactivity of nanostructured anatase, rutile and brookite TiO2 thin films

2006

Photoactive films consisting of pure anatase, brookite or rutile TiO2 were prepared by dip coating from water dispersions obtained by using TiCl4 as the precursor under similar mild experimental conditions