Two-Step Solution-Processed Two-Component Bilayer Phthalocyaninato Copper-Based Heterojunctions with Interesting Ambipolar Organic Transiting and Eth…

2016

International audience; The two-component phthalocyaninato copper-based heterojunctions fabricated from n-type CuPc(COOC8H17)(8) and p-type CuPc(OC8H17)(8) by a facile two-step solution-processing quasi-Langmuir-Shafer method with both n/p- and p/n-bilayer structures are revealed to exhibit typical ambipolar air-stable organic thin-film transistor (OTFT) performance. The p/n-bilayer devices constructed by depositing CuPc(COOC8H17)(8) film on CuPc(OC8H17)(8) sub-layer show superior OTFT performance with hole and electron mobility of 0.11 and 0.02 cm(2) V-1 s(-1), respectively, over the ones with n/p-bilayer heterojunction structure with the hole and electron mobility of 0.03 and 0.016 cm(2) …

Structure–Property Relationships in Bionanocomposites for Pipe Extrusion Applications

2021

In this work, bionanocomposites based on different biodegradable polymers and two types of nanofillers, namely a nanosized calcium carbonate and an organomodified nanoclay, were produced through melt extrusion, with the aim to evaluate the possible applications of these materials as a potential alternative to traditional fossil fuel-derived polyolefins, for the production of irrigation pipes. The rheological behavior of the formulated systems was thoroughly evaluated by exploiting different flow regimes, and the obtained results indicated a remarkable effect of the introduced nanofillers on the low-frequency rheological response, especially in nanoclay-based bionanocomposites. Conversely, t…

Processability and biodegradation of wood/biopolymer composites

2008

Processability and Properties of Re-Graded, Photo-Oxidized Post-Consumer Greenhouse Films

2005

The recycling of post‐consumer plastics leads, in general, to secondary materials having properties worse than those of the reclaimed material and certainly worse than those of the same virgin polymer. This is because of the degradation undergone by the objects during their use and because of the thermo‐mechanical degradation undergone during the reprocessing operations. The change of the molecular architecture is responsible for this worsening of properties. The use of stabilizing systems can slow the degradation during the melt processing but cannot give any improvement of the final properties of the material. In order to enhance the properties of the recycled plastics, some rebuilding of…