Effect of high temperature annealing (T > 1650 °C) on the morphological and electrical properties of p-type implanted 4H-SiC layers
2019
This work reports on the effect of high temperature annealing on the electrical properties of p-type implanted 4H-SiC. Ion implantations of Aluminum (Al) at different energies (30-200 keV) were carried out to achieve 300 nm thick acceptor box profiles with a concentration of about 10(20) at/cm(3). The implanted samples were annealed at high temperatures (1675-1825 degrees C). Morphological analyses of the annealed samples revealed only a slight increase of the surface roughness RMS up to 1775 degrees C, while this increase becomes more significant at 1825 degrees C (RMS = 1.2 nm). Room temperature Hall measurements resulted in a hole concentration in the range 0.65-1.34 x 10(18)/cm(3) and m…
Surface hysteresis curves of Fe(110) and Fe(100) crystals in ultrahigh vacuum — evidence of adsorbate influences
1992
Abstract We have investigated hysteresis curves of silicon-stabilized Fe(100) and Fe(110) crystals using Polarized Secondary Electron Emission (PSEE) for surface magnetization processes and Magneto-Optical Kerr Effect (MOKE) for bulk hysteresis curves. In particular, the influence of adsorbates (oxygen and sulphur) and surface roughness on the magnetization reversal has been studied. For surface hysteresis curves we found adsorbate-induced reductions of coercive force of up to 50%; the bulk hysteresis curves showed significantly smaller deviations. Similar changes were caused by surface disorder on an atomic scale induced by ion bombardment. The results agree qualitatively with a previous e…
How and why does willow biochar increase a clay soil water retention capacity?
2018
Addition of biochar into a soil changes its water retention properties by modifying soil textural and structural properties. In addition, internal micrometer-scale porosity that is able to directly store readily plant available water affects soil water retention properties. This study shows how precise knowledge of the internal micrometer-scale pore size distribution of biochar can deepen the understanding of the biochar-water interactions in soils. The micrometer-scale porosity of willow biochar was quantitatively and qualitatively characterized using X-ray tomography, 3D image analysis and Helium ion microscopy. The effect of biochar application on clay soil water retention was studied by…
Measuring intrinsic thickness of rough membranes: application to nanofibrillated cellulose films
2015
Adequate measurement of thickness of sheet-like materials or membranes is most important for quantifying their properties such as density, barrier properties and mechanical strength. Depending on the surface roughness of the membrane, the thickness measured by standard micrometre devices (apparent thickness) may considerably overestimate the actual geometrical mean thickness (intrinsic thickness) required for such purposes. In this work, we present a method for correcting the measured apparent thickness value of thin membranes for their surface roughness, thereby obtaining an improved estimate of the intrinsic thickness. The surface roughness data required for the correction can be obtained…
A Comparative Analysis of the Machined Surfaces Quality of an Aluminum Alloy According to the Cutting Speed and Cutting Depth Variations
2019
The milling operations are a topical and especially future-oriented methods. The purpose of this scientific paper is to carry out an experimental research referring to the end-milling process of the 7136 aluminum alloy. This paper is a continuation of the own research activity carried out so far, within a company with the field of activity in the aerospace industry. The main objective is a comparative analysis which was carried out on the surface quality - machined on various cutting regimes. The cutting process parameters used in the end-milling process are: the cutting speed, the feed per tooth and the cutting depth. The obtained results of the surface roughness’s were measured longitudin…
Physical Fundamentals of Biomaterials Surface Electrical Functionalization
2020
This article is focusing on electrical functionalization of biomaterial&rsquo
Effect of 15% carbamide peroxide bleaching gel on color stability of giomer and microfilled composite resin: an in vitro comparison
2011
Objectives: The effect of 15% carbamide peroxide bleaching gel on color stability and surface topography of a giomer and a microfilled composite resin was evaluated in the present in vitro study. Study design: Forty discs measuring 10 mm in diameter and 1 mm in thickness were prepared from a giomer and a microfilled composite resin. Each material yielded 20 discs with completely smooth surfaces. Then a spectrophotometer was used to measure L* (lightness), a* (redness, greenness) and b* (blueness, yellowness) color coordinates of all the discs. Subsequently, the specimens were subjected to 15% carbamide peroxide bleaching gel. After measuring the color coordinates once again, color changes (…
Method of Discrimination of Surface Fractality
1993
Abstract A simple method for the discrimination of surface fractality is proposed. This method is based on the comparison of the nitrogen adsorption isotherm on a given sample with the "standard" isotherm on a smooth surface. The proposed comparative method makes it possible to determine the lower limit of the scale range of surface fractality. A thermodynamic method is recommended as a complement to fractal analysis in the scale range of about 10-1000 A. The results of the investigation of surface roughness are presented with examples of typical samples of silica gels, porous glasses, apatite, and coal.
Influence of Bleaching Agents on Surface Roughness of Sound or Eroded Dental Enamel Specimens
2010
Purpose: The aim of the present in vitro study was to assess the effect of bleaching agents on eroded and sound enamel specimens. Materials and Methods: Enamel specimens prepared from human permanent anterior teeth were incubated with different bleaching agents containing active ingredients as 7.5 or 13.5% hydrogen peroxide or 35% carbamide peroxide, ranging in pH from 4.9 to 10.8. The effect of the tooth whitening agents on surface roughness was tested for sound enamel surfaces as well as for eroded enamel specimens. To provoke erosive damage, the enamel specimens were incubated for 10 hours with apple juice (pH = 3.4). Afterwards, pretreated and untreated dental slices were incubated wi…
Influence of titanium-substrate roughness on Ca–P–O thin films grown by atomic layer deposition
2013
Abstract Amorphous Ca–P–O films were deposited on titanium substrates using atomic layer deposition, while maintaining a uniform Ca/P pulsing ratio of 6/1 with varying number of atomic layer deposition cycles starting from 10 up to 208. Prior to film deposition the titanium substrates were mechanically abraded using SiC abrasive paper of 600, 1200, 2000 grit size and polished with 3 μm diamond paste to obtain surface roughness R rms values of 0.31 μm, 0.26 μm, 0.16 μm, and 0.10 μm, respectively. The composition and film thickness of as-deposited amorphous films were studied using Time-Of-Flight Elastic Recoil Detection Analysis. The results showed that uniform films could be deposited on ro…