Optimizing the H3PO4 leaching conditions of post-precipitated sewage sludge using response surface methodology
2018
The leaching procedure of post-precipitated aluminium phosphate sludge with dilute phosphoric acid was developed. The leaching offers a route to recover both critical phosphorous from sewage sludge and the metal used in precipitation. Using phosphoric acid as leaching solution makes it possible to continue the recovery process without the need to remove chloride or sulfate anions. The optimization of the leaching was based on experimental three-level-four-variable central composite face-centered design. The four variables included were acid concentration, volume of acid, temperature and time of leaching. The leaching was conducted for dewatered and water-containing sludge (total solid conte…
Use of Calcined Dolomite as Chemical Precipitant in the Simultaneous Removal of Ammonium and Phosphate from Synthetic Wastewater and from Agricultura…
2019
Phosphorus as phosphate and nitrogen as ammonium or nitrate are the main nutrients in wastewaters and agricultural sludges. They runoff easily to waterways and cause eutrophication in water bodies. However, ammonium and phosphate could be precipitated simultaneously and used as recycled nutrients. In this research, dolomite calcined at 650 °
Purification of recovered phosphoric acid by extracting aluminium with di-2-ethylhexyl phosphoric acid
2021
AbstractThe extraction of aluminium from dilute phosphoric acid with di-2-ethylhexyl phosphoric acid (DEHPA) was optimized using response surface methodology. The optimization was based on the experimental three-level central composite face-centred design (CCF) and was conducted on real-life samples. The three variables included were pH, extractant concentration and aqueous to organic phase ratio (AO). Under the optimized conditions (pH 2.5, 0.6 M DEHPA and AO ratio 1:2), extraction efficiency of 99% for aluminium in four extraction stages is achieved. The purified phosphoric acid solution can then be utilized by the fertilizing industry. Stripping tests for organic phase loaded with alumin…
α-Aminophosphonates, Phosphinates, and Phosphine Oxides as Extraction and Precipitation Agents for Rare Earth Metals, Thorium, and Uranium : A Review
2022
α-Aminophosphonates, -phosphinates, and -phosphine oxides are a group of organophosphorus compounds that were investigated as extraction agents for rare earth (RE) metals and actinoids for the first time in the 1960s. However, more systematic investigations of their extraction properties towards REs and actinoids were not started until the 2010s. Indeed, recent studies have shown that these α-amino-functionalized compounds can outperform the commercial organophosphorus extraction agents in RE separations. They have also proven to be very efficient extraction and precipitation agents for recovering Th and U from RE concentrates. These actinoids coexist with REs in some of the commercially im…
RAVITA Technology : new innovation for combined phosphorus and nitrogen recovery
2018
Abstract Present phosphorus (P) recovery technologies mainly contain P recovery from sludge liquor or ash. These types of technologies are suitable for large wastewater treatment plants (WWTPs) with enhanced biological phosphorus removal (EBPR), digestion and/or incineration. In Finland and other Nordic countries, strict P discharge limits require chemical precipitation, thus EBPR alone is not sufficient. Ammonium recovery from wastewater, on the other hand, is not so often discussed. However, recovery from WWTP reject waters would decrease the energy demand of ammonium synthesis by Haber-Bosh technology and the energy demand of the WWTP's biological process. Helsinki Region Environmental S…
Water leaching of roasted vanadium slag : Desiliconization and precipitation of ammonium vanadate from vanadium solution
2023
This research investigated water leaching of roasted vanadium slag and studied the effects of leaching parameters, such as agitation speed, temperature, liquid-to-solid ratio, and leaching time. Further, solution purification via desiliconization and precipitation of ammonium vanadate were studied using the vanadium solution obtained from the water leaching of roasted vanadium slag. Vanadium solution contains residual silicon (1.67 g/L), which should be removed before ammonium vanadate precipitation. Based on the results, vanadium can be effectively recovered from vanadium slag and a recovery efficiency of 96.9% was obtained under optimal water leaching conditions. During solution purificat…
Precipitation of potassium as hazenite from washing water of spent alkaline batteries
2022
Hazenite (KNaMg2(PO4)2 × 14 H2O), a new type of struvite mineral, was precipitated from the potassium-rich washing water of spent alkaline battery black mass. Hazenite can be used as a fertilizer, which would be an additional benefit derived from the sustainable recovery of battery materials. Precipitation experiments were performed using different pH values (9.5–12), Mg:K:PO4 ratios ((1.0–1.5):1:(1.0–1.5)) and temperatures (10–40 °C). Based on the results, hazenite precipitated in a wide pH range under alkaline conditions. The precipitation kinetics were fast, and the purity of the hazenite was high. Overall, hazenite can be precipitated at room temperature without the addition of excess c…
Lignin recovery from spent alkaline pulping liquors using acidification, membrane separation, and related processing steps: A Review
2019
The separation of lignin from the black liquor generated during alkaline pulping is reviewed in this article with an emphasis on chemistry. Based on published accounts, the precipitation of lignin from spent pulping liquor by addition of acids can be understood based on dissociation equilibria of weak acid groups, which affects the solubility behavior of lignin-related chemical species. Solubility issues also govern lignin separation technologies based on ultrafiltration membranes; reduction in membrane permeability is often affected by conditions leading to decreased solubility of lignin decomposition products and the presence of colloidal matter. Advances in understanding of such phenomen…
Anaerobic on-site wastewater treatment at low temperatures
2005
Sari Luostarinen tutki väitöstyössään hajautettua anaerobista jätevesien käsittelyä alhaisissa lämpötiloissa (10-20 °C). Anaerobinen käsittely mahdollistaa sekä jätemateriaalin stabiloinnin, uusiutuvan energian tuotannon metaanina ja/tai vetynä että arvokkaiden yhdisteiden, kuten ravinteiden, uudelleenkäytön. Luostarisen mukaan käsittely voidaan toteuttaa hajautettuna kiinteistö- tai kyläkohtaisissa prosesseissa. Mikäli ravinteiden uudelleenkäyttö ei ole mahdollista, esimerkiksi hygieniamääräyksien vuoksi, ja ravinteiden poistoa vaaditaan, se voidaan toteuttaa aerobisessa jälkikäsittelyprosessissa. Luostarisen tutkimuksessa kaksivaiheinen anaerobinen ylösvirtaussaostuskaivo (UASB-saostuskai…
The use of calcined paper mill sludge as a chemical precipitant in the simultaneous removal of ammonium and phosphate : paper mill waste recycling an…
2020
Currently, recycling and re-use of materials is extremely important due to the diminishing of natural resources. The objective of the European Union’s circular economy strategy is to increase recycling and the use of industrial waste materials and side streams as secondary raw materials. In this study, a chemical precipitation method to simultaneously remove ammonium nitrogen and phosphate from the liquid phase of anaerobic digestate using calcined paper mill sludge was studied. Papermill sludge is a waste material that forms in the paper-making process. In addition, commercial calcium oxide (CaO) was used as a reference precipitant. The suitability of the formed precipitate’s composition f…