Coating Toughness Estimation through a Laser Shock Testing in Ni-Cr-B-Si-C Coatings
2018
In the nuclear field, efforts are made to find substitutes to cobalt hardfacing alloys since these alloys have a principal drawback, the transmutation from stable 59Co to 60Co under neutron irradiation. In case of wear, fragments could be deposed on the surface of primary circuit and thus contaminate it, causing a real issue for deconstruction.
Estimation of interfacial fracture toughness based on progressive edge delamination of a thin transparent coating on a polymer substrate
2010
Evaluation of interfacial toughness of sub-micron-thickness layers deposited on a ductile substrate is a challenging task which has motivated different experimental approaches Fragmentation testing was used in the present study as a means of interface characterization of a silicon-nitride-coated polyimide substrate. During the test, after an initial rapid segmentation-cracking phase, the coating fragments developed edge delaminations which propagated in a stable manner with further increase in the applied strain The debonding process was modelled by the finite element method Incorporating a cohesive zone at the front of the interfacial crack The edge cracks were found to be dominated by mod…
Transformation of the Software Testing Glossary into a Browsable Concept Map
2014
Authors propose a transformation method of the glossary “Standard glossary of terms used in Software Testing” created by ISTQB document into a basic concept map. By applying natural language processing techniques and analyzing the discovered relations between concepts the most essential aspects of the software testing domain are elicited and integrated. As the result a browsable concept map is created. Browsable concept map can be used as a learning support tool.
Multilayer capsules: a promising microencapsulation system for transplantation of pancreatic islets
2001
In 1980, Lim and Sun introduced a microcapsule coated with an alginate/polylysine complex for encapsulation of pancreatic islets. Characteristic to this type of capsule is, that it consists of a plain membrane which is formed during a single procedural step. With such a simple process it is difficult to obtain instantly a membrane optimized with respect to all the properties requested for islet transplantation. To overcome these difficulties, it is recommended to build up the membrane in several consecutive steps, each optimized for a certain property. In this study, we have analysed such a multilayer microcapsule for the encapsulation of pancreatic islets. Therefore, empty and islet contai…
Predictors of early dropout in treatment for gambling disorder: The role of personality disorders and clinical syndromes
2017
Several treatment options for gambling disorder (GD) have been tested in recent years; however dropout levels still remain high. This study aims to evaluate whether the presence of psychiatric comorbidities predicts treatment outcome according to Millon's evolutionary theory, following a six-month therapy for GD. The role of severity, duration of the disorder, typology of gambling (mainly online or offline) and pharmacological treatment were also analysed. The recruitment included 194 pathological gamblers (PGs) to be compared with 78 healthy controls (HCs). Psychological assessment included the South Oaks Gambling Screen and the Millon Clinical Multiaxial Inventory-III. The "treatment fail…
Research Regarding Physical Testing in the Military Pentathlon at the 50 M Race with Obstacles
2019
Abstract The research started from the necessity of finding new ways to physical test the military students that are part of the military pentathlon 50 m race with obstacles team. The research methods used was the experiment method, using two groups: the first group was the control group and the second the experiment group. The experiment consisted in testing the students at: 50 m speed running, 800 m resistance running, push-ups, and specific testing like: 50 m swimming with obstacles, 8 km run in varied terrain. The results of our investigation showed that calculation of the statistical significance of the differences between the averages of the two samples showed significant values at p&…
Flexural behavior of hybrid glass beams with rectangular cross-sections
2018
Abstract An experimental investigation regarding the flexural and the shear behavior of glass beams with length 900, 1300, 1700 mm and rectangular cross-section is presented and discussed. Rectangular cross-sections were obtained by assembling three float glass panels of depth 200 mm and thickness 6 mm through an acrylic adhesive with an effective depth of 19.52 mm (6 + 0.76 + 6 + 0.76 + 6 mm). Some specimens were also reinforced internally with steel plates of thickness 6 mm and depth 25 mm and thickness 6 mm and plates of thickness 6 mm and depth 50 mm placed at the bottom portion of the beams for the entire length of the beams themselves. Three specimens for each investigated series were…
Structural behaviour of hybrid glass beams with T cross-sections
2018
Abstract An experimental investigation regarding the flexural and the shear behaviour of glass beams with length 900, 1300, 1700 mm and T cross-section is presented and discussed. T cross-sections were obtained by assembling glass web and glass flange. Some specimens were also reinforced internally in the web with steel plates of thickness 6 mm and depth 25 and 50 mm placed at the bottom portion of the beams for the entire length of the beams themselves. Three specimens for each investigated series were tested in flexure focusing on the flexural and shear response through the determination of the load-deflection curves and the crack patterns at rupture identifying the effects of steel plate…
Model-assisted ultrasonic calibration using intentionally embedded defects for in-process weld inspection
2021
Abstract Automated in-process Non-Destructive Testing (NDT) systems are rapidly gaining traction within the manufacturing industry as they reduce manufacturing time and costs. When considering calibration and verification of such systems, creating defects of known geometry and nature during the deposition of a weld can: (I) help examine the capability of the automated system to detect and characterise defects, (II) be used to form a database of signals associated with different defect types to train intelligent defect classification algorithms, and (III) act as a basis for in-process gain calibration during weld inspection at high temperatures, where the ultrasound beam can be skewed as a r…
Adhesive debonding detection of FRP reinforcement by the ultrasonic non-destructive technique
2015
Fiber reinforced polymer (FRP) composite systems are extensively used for repairing and reinforc- ing structurally inefficient concrete structures. The performance of an FRP rehabilitation system is highly influenced by its integrity. In particular, the presence of defects, e.g. voids, inclusions, debonds, improper cure and delaminations, caused by an inaccurately manufacture and installation, may affect the capability of the rehabilitated structure. For this reason, non-destructive (ND) meth- ods could be used to assess the quality of the reinforcement [1,2]. In this work an ultrasonic ND technique for detecting delamination defects in FRP reinforcement is presented. The technique couples …