Mechanical behavior of single-layer ceramized zirconia abutments for dental implant prosthetic rehabilitation
2013
Objectives: This study was undertaken to characterize the mechanical response of bare (as-received) and single-layer ceramized zirconia abutments with both internal and external connections that have been developed to enhanced aesthetic restorations. Material and Methods: Sixteen zirconia implant abutments (ZiReal Post®, Biomet 3i, USA) with internal and external connections have been analyzed. Half of the specimens were coated with a 0.5mm-thick layer of a low-fusing fluroapatite ceramic. Mechanical tests were carried out under static (constant cross-head speed of 1mm/min until fracture) and dynamic (between 100 and 400N at a frequency of 1Hz) loading conditions. The failure location was i…
Effect of water contamination on the shear bond strength of five orthodontic adhesives
2010
Objectives: To evaluate the shear bond strength and site of failure of brackets bonded to dry and wet enamel. Study design: 50 teeth were divided into ten groups of 5 teeth each (10 surfaces). In half the groups enamel was kept dry before bonding, and in the other half distilled water was applied to wet the surface after etching. The following groups were established: 1)Acid/Transbond-XT (dry/wet) XT; 2) Transbond Plus Self Etching Primer (TSEP)/Transbond-XT paste (dry/wet); 3) Concise (dry), Transbond MIP/Concise (wet), 4) FujiOrtho-LC (dry/ wet); 5) SmartBond (dry/wet). Brackets were bonded to both buccal and lingual surfaces. Specimens were stored in distilled water (24 hours at 37ºC) an…
Casein phosphopeptide-amorphous calcium phosphate effects on brackets shear bond strength and enamel damage
2017
Background The aim of study was to evaluate the application of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) and fluoride regarding their effect on the shear bond strength (SBS), bond failure pattern of brackets using the adhesive remnant index (ARI) and assessing the quality of enamel surface using the enamel damage index (EDI). Material and methods Sixty extracted premolar teeth were randomly divided into four groups regarding pretreatment application of CPP-ACP and fluoride. Brackets were bonded using the conventional method. Specimens were thermocycled for 1000 cycles and were subsequently tested for the SBS in a universal testing machine. After debonding, the teeth were e…
Effect of framework type on survival probability of implant-supported temporary crowns : an in vitro study
2020
Made available in DSpace on 2020-12-12T01:29:18Z (GMT). No. of bitstreams: 0 Previous issue date: 2020-01-01 Background: This in vitro study evaluated the effect of framework type on the survival probability of temporary implant-supported crowns and on the implant platform structure after dynamic fatigue. Material and Methods: Thirty (30) external hexagon implants (3.75 x 10 mm) were embedded in acrylic resin following the ISO-14801. Standardized temporary crowns (n=10, N=30) were manufactured in acrylic resin and divided according to the framework type: Total plastic, Plastic with CoCr base and Titanium. The crowns were installed onto the implants (20N. cm) and fatigued (100N, 2 Hz) to det…
Preparation of Sm-loaded brookite TiO2 photocatalysts
2011
Abstract Pure and Sm-loaded brookite nanoparticles and thin films were prepared using TiCl4 as precursor of TiO2. The samples were characterized by X-ray diffraction (XRD), specific surface area (SSA) determination, diffuse reflectance spectroscopy (DRS) and photoluminescence (PL) measurements. The photocatalytic activity of the powders was investigated by employing the photodegradation of 4-nitrophenol in a liquid–solid system whilst the photoreactivity of the films was tested by evaluating the rate of degradation of 2-propanol in a gas–solid system. Loading with Sm resulted in a significant improvement of the photoreactivity of brookite and the beneficial effect was attributed to an incre…
Absolute crystallinity and photocatalytic activity of brookite TiO2 samples
2017
Abstract This study reports a method to determine the absolute crystallinity of partly crystalline brookite TiO2 photocatalysts. A natural, a commercial and various home-prepared brookite powders were characterized by X-ray diffraction analysis, Raman spectroscopy, scanning electron microscopy, UV–vis diffuse reflectance spectroscopy and nitrogen adsorption measurements. The absolute crystallinity was calculated from the ratio between the full width at half maximum intensity of the (121) X-ray diffraction peaks of the brookite samples and the (111) peak of CaF2 as internal standard. The photocatalytic activity of the powders was tested employing the photodegradation of 4-nitrophenol as well…
Binding Behavior of Carbonmonoxide to Gold Atoms on Ag(001)
2020
AbstractThe adsorption behavior of single CO molecules at 4 K bound to Au adatoms on a Ag(001) metal surface is studied with scanning tunneling microscopy (STM) and inelastic electron tunneling spectroscopy (IETS). In contrast to earlier observations two different binding configurations are observed—one on top of a Au adatom and the other one adsorbed laterally to Au on Ag(001). Moreover, IETS reveals different low-energy vibrational energies for the two binding sites as compared to the one for a single CO molecule bound to Ag(001). Density functional theory (DFT) calculations of the adsorption energies, the diffusion barriers, and the vibrational frequencies of the CO molecule on the diffe…
Curing of an epoxy resin modified with nanoclay monitored by dielectric spectroscopy and rheological measurements
2006
Dielectric and rheological measurements have been performed in “real-time” to follow curing reaction on blends of a diglycidyl ether of bisphenol-A epoxy resin with 4,4-methylene bis(2,6-diethylaniline) hardener and different amounts of organically modified nanoclay (Nanofil 919) as modifier. The effect of the modifier and its amount on the curing reaction, as well as that of the curing temperature has been studied. Changes in molecular mobility in the reaction mixture have been investigated by dielectric relaxation spectroscopy. Evolutions of ionic conductivity and main relaxation have been analyzed and vitrification times have been obtained and compared with those obtained by rheological …
Decay pathways of stored metal-cluster anions after collisional activation
1999
Size-selected gold clusters, Open image in new window (n ≤ 21), and tungsten clusters, Open image in new window , and Open image in new window (n = 4 – 8 and 12), stored in a Penning trap have been collisionally activated. Neutral monomer and dimer evaporation are observed in the case of gold. While no fragment products have been observed for tungsten clusters, there is evidence of electron emission from the anions.
The effect of Zn vacancies and Ga dopants on the electronic structure of ZnO:Ab initiosimulations
2012
Zinc oxide modied by metal dopants can be used as a low-cost material for production of transparent conducting lms. Its optical and electronic properties vary with the type and the concentration of dopants. In this study we have performed rst-principle calculations on ZnO with Zn vacancies and that with Ga dopants in wurtzite type hexagonal morphology using density functional theory approach. Dependence of the electronic properties on the concentration of dopants has been studied using supercells of dierent sizes.