Sol–Gel Synthesis of Tunable Cerium Titanate Materials

2008

Cerium titanate structures present a high technological interest because of their optical and catalytic properties. This work reports the synthesis of these materials by a sol–gel methodology that allows mixed oxides with TiIV/CeIII, TiIV/CeIV or TiIV/CeIII–CeIV species to be obtained. Crystallization of CeO2–TiO2 mixed oxides and Ce2Ti2O7 pyrochlore phase was corroborated by XRD and Raman spectroscopy. Magnetic and EPR measurements were performed in order to clarify the oxidation state of the cerium ions in the system as a result of the easy oxidation of CeIII. The firing atmosphere is crucial for the CeIII/CeIV ratio, which is responsible for the different structure, but it also affects t…

A Study of the Method of Synthesis and Chromatic Properties of the Cr-SnO2 Pigment

2002

The stoichiometry of blue vanadium doped zircon obtained by sol-gel methods

1992

Abstract In this study, Sol-Gel processes in aqueous solution were used to investigate the stoichiometry of the V/1bZrSiO 4 solid solutions achieved by this method. Compositions with a formal stoichiometric defect in: (a) ZrO 2 ([ZrO 2 ] 1−2x [SiO 2 ] [V 2 O 5 ] x ), and (b) in SiO 2 ([ZrO 2 ] [SiO 2 ] 1−2x [V 2 O 5 ] x ), x=0.02, 0.04, 0.05 and 0.10 have been prepared. X Ray Diffraction analyses in fired samples (1200°/3 days) showed that cristobalite and monoclinic zirconia appear as residual crystalline phase in (a) and (b) compositions respectively, except in sample (a) with x=0.02 in which no residual phase was detected and therefore is considered stoichiometric. This sample and sample…

Preparation and characterization of gels with garnet structure: A3B2C3O12, using ‘non-classical’ solvents

1992

Abstract Synthesis and characterization of some crystalline garnets by sol-gel techniques is described. The effects of emthanol, dimethyl sulfoxide (DMSO), CH2Cl2 and toluene solvents on gelation of TEOS are considered. Multicomponent gel formation in systems with stoichiometries 3CaO·Cr2O3·3SiO2 and 3CaO·Al2O2 was studied using DMSO, a polar solvent, and toluene, an apolar solvent. The dried gel was thermally treated and the powder was characterized by X-ray diffraction, differential thermal analysis/thermogravimetric analysis and scanning electron microscopy.